Molding composition for crosslinked foam material from polyolefins and ethylene-propylene elastomer, and process for the production of the foam material

Claim 2

An expandable molding composition for the production of a crosslinked foam material that has a predominantly closed cell structure with an average pore size of not more than 500 μm and that is a mixture consisting essentially of polyethylene and a partially crystalline ethylene-propylene terpolymer, and a blowing agent, in the presence of a crosslinking agent, the amount of the terpolymer in said composition, per 100 parts by weight of polyethylene, being 25-150 parts by weight, and said terpolymer having a tensile strength at break of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, with a melting heat (according to DSC) ΔH s of at least 10 J/g, and a content of 60-80% by weight of ethylene, 10-38% by weight of propylene and 2-10% of a non-conjugated diene tercomponent of ethylidene norbornene or 1,4-hexadiene.

Claim 3

A molding composition according to claim 1, wherein the ethylene-propylene terpolymer has a content of 65-80% by weight of ethylene, 10-31% by weight of propylene, and 4-10% by weight of the tercomponent.

Claim 4

A molding composition according to claim 1, wherein the amount of the ethylene-propylene terpolymer in said composition, per 100 parts by weight of polyethylene, is 25-60 parts by weight.

Claim 5

A molding composition according to claim 1, wherein the polyethylene has a melt index (MFI 190/2) of 1-8 and a density of 0.91-0.96 g/cm 3 .

Claim 6

An expandable molding composition for the production of a chemically crosslinked foam material that has a predominantly closed cell structure with an average pore size of not more than 500 μm and that is a mixture consisting essentially of polyethylene and a partially crystalline ethylene-propylene terpolymer, a blowing agent and a crosslinking agent; the amount of said terpolymer, per 100 parts by weight of polyethylene being 25-150 parts by weight, the terpolymer having a tensile strength at break of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, a melting heat (DSC) ΔH s larger than 10 J/g, and a content of 60-80% by weight of ethylene, 10-38% by weight of propylene, and 2-10% by weight of a tercomponent of ethylidene norbornene or 1,4-hexadiene, and the amount of the crosslinking agent being 0.6-1.6 parts by weight per 100 parts by weight of polyethylene.

Claim 7

An expandable molding composition for the production of a chemically crosslinked foam material that has a predominantly closed cell structure with an average pore size of not more than 500 μm and that is a mixture consisting essentially of polyethylene and a partially crystalline ethylene-propylene terpolymer, a blowing agent and a crosslinking agent; the amount of said terpolymer, per 100 parts by weight of polyethylene being 25-150 parts by weight, the terpolymer having a tensile strength at break of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, a melting heat (DSC) ΔH s larger than 10 J/g, and a content of 60-80% by weight of ethylene, 10-38% by weight of propylene, and 2-10% by weight of a tercomponent of ethylidene norbornene or 1,4-hexadiene, and the amount of the crosslinking agent being 0.6-1.6 parts by weight per 100 parts by weight of polyethylene.

Claim 8

A molding composition according to claim 5, wherein the peroxide crosslinking agent comprises dicumyl peroxide.

Claim 9

A molding composition according to claim 6, wherein the blowing agent has a decomposition temperature higher than that of the crosslinking agent and includes azodicarbonamide, dinitrosopentamethylenetetramine, p,p'-oxybis(benzenesulfonylhydrazide), or toluenesulfonylhydrazide.

Claim 10

A crosslinked foam material component formed on a mixture consisting essentially of polyethylene and a partially crystalline ethylene-propylene terpolymer, a blowing agent, and optionally a crosslinking agent, the amount of said terpolymer, per 100 parts by weight of polyethylene, being 25-150 parts by weight and the partially crystalline ethylene-propylene terpolymer having a tensile strength at break of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, a melting heat ΔH s (DSC) larger than 10 J/g, and being prepared from a monomeric mixture of 60-80% by weight of ethylene, 10-38% by weight of propylene, and 2-10% by weight of a tercomponent of ethylidene norbornene or 1,4-hexadiene, and said foam material being of a closed-cell very fine cellular structure with an average pore size of not more than 500 μm.

Claim 11

A crosslinked foam material component formed on a mixture consisting essentially of polyethylene and a partially crystalline ethylene-propylene terpolymer, a blowing agent, and optionally a crosslinking agent, the amount of said terpolymer, per 100 parts by weight of polyethylene, being 25-150 parts by weight and the partially crystalline ethylene-propylene terpolymer having a tensile strength at break of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, a melting heat ΔH s (DSC) larger than 10 J/g, and being prepared from a monomeric mixture of 60-80% by weight of ethylene, 10-38% by weight of propylene, and 2-10% by weight of a tercomponent of ethylidene norbornene or 1,4-hexadiene, and said foam material being of a closed-cell very fine cellular structure with an average pore size of not more than 500 μm.

Claim 12

A process for the production of crosslinked foam materials with a very fine, uniform predominantly closed cell structure with an average pore size of not more than 500 μm and based on a mixture of polyethylene and a partially crystalline ethylene-propylene terpolymer, a blowing agent, and optionally a crosslinking agent, comprising first preparing a homogeneous mixture consisting essentially of the polyethylene and 25-150% by weight, based on the weight of the polyethylene, of a partially crystalline ethylene-propylene terpolymer having a tensile strength of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, and a melting heat ΔH s (according to DSC) larger than 10 J/g, and containing 60-80% by weight of ethylene, 10-38% by weight of propylene, and 2-10% by weight of a tercomponent of ethylidene norbornene or 1,4-hexadiene, as well as a suitable blowing agent and optionally a suitable crosslinking agent, at below the decomposition temperatures of the crosslinking agent and blowing agent, the blowing agent having a decomposition temperature lying above the decomposition temperature of the crosslinking agent; and subsequently molding the mixture, treating same optionally with high energy radiation with a dose of 1-20 Mrad and/or heating same for crosslinking and expansion to provide said cell structure with hot air, radiation and/or a liquid bath to temperatures of between 200° and 240° C.

Claim 13

A process for the production of crosslinked foam materials with a very fine, uniform predominantly closed cell structure with an average pore size of not more than 500 μm and based on a mixture of polyethylene and a partially crystalline ethylene-propylene terpolymer, a blowing agent, and optionally a crosslinking agent, comprising first preparing a homogeneous mixture consisting essentially of the polyethylene and 25-150% by weight, based on the weight of the polyethylene, of a partially crystalline ethylene-propylene terpolymer having a tensile strength of at least 8.0N/mm 2 , a Mooney viscosity (ML 1+4/100) larger than 50, and a melting heat ΔH s (according to DSC) larger than 10 J/g, and containing 60-80% by weight of ethylene, 10-38% by weight of propylene, and 2-10% by weight of a tercomponent of ethylidene norbornene or 1,4-hexadiene, as well as a suitable blowing agent and optionally a suitable crosslinking agent, at below the decomposition temperatures of the crosslinking agent and blowing agent, the blowing agent having a decomposition temperature lying above the decomposition temperature of the crosslinking agent; and subsequently molding the mixture, treating same optionally with high energy radiation with a dose of 1-20 Mrad and/or heating same for crosslinking and expansion to provide said cell structure with hot air, radiation and/or a liquid bath to temperatures of between 200° and 240° C.

Claim 14

A process according to claim 9, wherein said ethylene-propylene terpolymer contains 65-80% by weight of ethylene, 10-31% by weight of propylene, and 4-10% by weight of the tercomponent.

Claim 15

A process according to claim 9, wherein the polyethylene has a melt index (MFI 190/2) of 1-8 and a density of 0.91-0.96 g/cm 3 .

Claim 16

A process according to claim 9, wherein, for the chemical crosslinking step, dicumyl peroxide, in an amount of 0.6-1.6 parts by weight, based on 100 parts by weight of polyethylene, and 25-150 parts by weight of ethylene-propylene terpolymer are utilized.

Claim 17

A process according to claim 12, wherein the molded mixture is temperature treated (tempered) prior to crosslinking and expansion, at a temperature below the decomposition temperature of the crosslinking agent, especially at a temperature of between about 90° and 110° C. for a period of 2-90 minutes.

Claim 18

A process according to claim 12, wherein the molded mixture is temperature treated prior to crosslinking and expansion at room temperature, about 15°-20° C., for a period of at least one day.

Claim 19

A molding composition according to claim 1, wherein the polymeric components within said mixture consists of polyethylene and said terpolymer.

Claim 20

A molding composition according to claim 5, wherein the polymeric components within said mixture consists of polyethylene and said terpolymer.

Claim 21

A foam material according to claim 15, wherein the polymeric components within said mixture consists of polyethylene and said terpolymer.

Claim 22

A process according to claim 9, wherein the polymeric components within said mixture consists of polyethylene and said terpolymer.