Method of manufacturing perpendicular magnetic recording floppy disk
Assignee: Toshiba Corp
•
Filing: 1985-12-02
•
Granted: 1987-07-14
•
Expires: 2005-12-02
Abstract
Abstract A method of manufacturing a perpendicular magnetic recording floppy disk is disclosed. A first magnetic recording layer is formed by sputtering a perpendicularly magnetizable material on one side of a plastic film substrate. A second magnetic recording layer is formed by sputtering the perpendicularly magnetizable material on the other side of the plastic film substrate after forming the first magnetic recording layer. The second magnetic recording layer has a thickness greater than that of the first magnetic recording layer, when a curl of the first magnetic recording layer on the plastic film substrate, resulting from forming the first magnetic recording layer on the plastic film substrate, is to the outside. On the other hand, the second magnetic recording layer has a thickness lower than that of the first magnetic recording layer, when a curl of the first magnetic recording layer on the plastic film substrate is to the inside.
Inventors
- 👤 Masayuki Sagoi
- 👤 Reiji Nishikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:09
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/64; G11B5/65; G11B5/656; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31786
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
119 words
A method of manufacturing a perpendicular magnetic recording floppy disk comprising the steps of: forming a first magnetic recording layer by sputtering a perpendicularly magnetizable material on one side of a plastic film substrate; and forming a second magnetic recording layer by sputtering said perpendicularly magnetizable material on the other side of said plastic film substrate, after forming said first magnetic recording layer, said second magnetic recording layer having a thickness greater than that of said first magnetic recording layer when a curl of the first magnetic recording layer on the plastic film substrate, resulting from forming the first magnetic recording layer on the plastic film substrate, is to the outside with respect to said first magnetic recording layer.
Claim 2
Independent Claim
119 words
A method of manufacturing a perpendicular magnetic recording floppy disk comprising the steps of: forming a first magnetic recording layer by sputtering a perpendicularly magnetizable material on one side of a plastic film substrate; and forming a second magnetic recording layer by sputtering said perpendicularly magnetizable material on the other side of said plastic film substrate, after forming said first magnetic recording layer, said second magnetic recording layer having a thickness greater than that of said first magnetic recording layer when a curl of the first magnetic recording layer on the plastic film substrate, resulting from forming the first magnetic recording layer on the plastic film substrate, is to the outside with respect to said first magnetic recording layer.
Claim 3
Dependent Claim
38 words
The method according to claim 1, in which said perpendicularly magnetizable material is a Co--Cr-based magnetic material and said second magnetic recording layer has a thickness 2% to 10% greater than that of said first magnetic recording layer.
Claim 4
Dependent Claim
71 words
The method according to claim 1, further comprising the steps of: forming, before the formation of said first magnetic recording layer, a first soft magnetic layer by sputtering a soft magnetic material; and forming, before the formation of said second magnetic recording layer, a second soft magnetic layer by sputtering said soft magnetic material, said second soft magnetic layer having a thickness greater than that of said first soft magnetic layer.
Claim 5
Dependent Claim
54 words
The method according to claim 3, wherein during the formation of said first and second soft magnetic layers, a plastic film substrate temperature is kept as high as possible, but within a range is which said plastic film substrate is subject to no heat damage resulting from the sputtering of said soft magnetic material.
Claim 6
Dependent Claim
54 words
The method according to claim 1, wherein during the formation of said first and second magnetic recording layers, a plastic film substrate temperature is kept as high as possible, but within a range in which said plastic film substrate is subject to no heat damage resulting from the sputtering of said perpendicularly magnetizable material.
Claim 7
Independent Claim
119 words
A method of manufacturing a perpendicular magnetic recording floppy disk comprising the steps of: forming a first magnetic recording layer by sputtering a perpendicularly magnetizable material on one side of a plastic film substrate; and forming a second magnetic recording layer by sputtering said perpendicularly magnetizable material on the other side of said plastic film substrate after forming said first magnetic recording layer, said second magnetic recording layer having a thickness lower than that of said first magnetic recording layer when a curl of the first magnetic recording layer on the plastic film substrate, resulting from forming the first magnetic recording layer on the plastic film substrate, is to the inside with respect to said first magnetic recording layer.
Claim 8
Independent Claim
119 words
A method of manufacturing a perpendicular magnetic recording floppy disk comprising the steps of: forming a first magnetic recording layer by sputtering a perpendicularly magnetizable material on one side of a plastic film substrate; and forming a second magnetic recording layer by sputtering said perpendicularly magnetizable material on the other side of said plastic film substrate after forming said first magnetic recording layer, said second magnetic recording layer having a thickness lower than that of said first magnetic recording layer when a curl of the first magnetic recording layer on the plastic film substrate, resulting from forming the first magnetic recording layer on the plastic film substrate, is to the inside with respect to said first magnetic recording layer.
Claim 9
Dependent Claim
37 words
The method according to claim 6, wherein said perpendicularly magnetizable material is a Co--Cr-based magnetic material and said second magnetic recording layer has a thickness 10 to 35% lower than that of said first magnetic recording layer.
Claim 10
Dependent Claim
54 words
The method according to claim 6, wherein during the formation of said first and second magnetic recording layers, a plastic film substrate temperature is kept as high as possible, but within a range in which said plastic film substrate is subject to no heat damage resulting from the sputtering of said perpendicularly magnetizable material.
References Cited (Backward Citations)
US4423454A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-07-13 | 1991-01-12 | 1991-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-07-13 | 1995-01-12 | 1995-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-07-13 | 1999-01-12 | 1999-07-14 | $7700.00 | Window Closed / Lapsed |