Process for purification of polyether
Assignee: Asahi Kasei Corp
•
Filing: 1985-11-08
•
Granted: 1987-06-30
•
Expires: 2005-11-08
Abstract
Abstract A process for purifying a polyalkylene ether, which comprises mixing a polyalkylene ether or a mixture of a polyalkylene ether and an organic solvent containing a heteropoly acid and/or its salt with at least one solvent for purification selected from hydrocarbons having 3 to 15 carbon atoms or halogenated hydrocarbons having 1 to 15 carbon atoms and separating by precipitation the phase composed mainly of the heteropoly acid and/or its salt, and a process wherein the polyalkylene ether or a mixture of a polyalkylene ether and an organic solvent containing a heteropoly acid and/or its salt is brought into contact with a solid adsorbent capable of adsorbing the heteropoly acid and/or its salt in the presence of at least one solvent for purification as described above, either further after the separation according to the process described above, or in the state unseparated. According to the present invention, the heteropoly acid and/or its salt dissolved in the polyalkylene ether or the mixture of the polyalkylene ether with the organic solvent can be removed efficiently in the form which can be reused. Further after the treatment with an adsorbent, the concentration of heteropoly acids in the polyalkylene ether can be reduced to extremely lower.
Inventors
- 👤 Atsushi Aoshima
- 👤 Setsuo Yamamatsu
- 👤 Shoichiro Tonomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 07:46
CPC Classifications
C; C08; C08G; C08G65/00; C08G65/02; C08G65/30; B; B01; B01D; B01D15/00; B01J; B01J20/00; B01J20/02; B01J20/06; B01J20/08; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/582
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
157 words
A process for purifying a polyoxytetramethylene ether which comprises the steps of: (1) mixing (A) a polyoxytetramethylene ether having a molecular weight of 500 to 5000, or a mixture of said polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol, with (B) at least one solvent for purification selected from hydrocarbons having 3 to 15 carbon atoms or halogenated hydrocarbons having 1 to 15 carbon atoms; said polyoxytetramethylene ether or said mixture containing a heteropoly acid and/or its salt, said heteropoly acid being an oxy acid formed by condensation of at least one oxide of Mo, W or V with an oxy acid of P, Si, As, Ge, B, Ti, Ce or Co, the atomic ratio of said oxide to said oxy acid being 2.5 to 12; and a salt of an oxy acid; and (2) separating the phase composed mainly of said heteropoly acid and/or its salt from the mixture formed in step (1).
Claim 2
Dependent Claim
157 words
A process for purifying a polyoxytetramethylene ether which comprises the steps of: (1) mixing (A) a polyoxytetramethylene ether having a molecular weight of 500 to 5000, or a mixture of said polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol, with (B) at least one solvent for purification selected from hydrocarbons having 3 to 15 carbon atoms or halogenated hydrocarbons having 1 to 15 carbon atoms; said polyoxytetramethylene ether or said mixture containing a heteropoly acid and/or its salt, said heteropoly acid being an oxy acid formed by condensation of at least one oxide of Mo, W or V with an oxy acid of P, Si, As, Ge, B, Ti, Ce or Co, the atomic ratio of said oxide to said oxy acid being 2.5 to 12; and a salt of an oxy acid; and (2) separating the phase composed mainly of said heteropoly acid and/or its salt from the mixture formed in step (1).
Claim 3
Dependent Claim
153 words
A process for purifying a polyoxytetramethylene ether wherein (A) a polyoxytetramethylene ether having a molecular weight of 500 to 5000 or a mixture of said polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol, said polyoxytetramethylene ether or said mixture containing a heteropoly acid and/or its salt; said heteropoly acid being (1) an oxy acid formed by condensation of at least one oxide of Mo, W or V with an oxy acid of P, Si, As, Ge, B, Ti, Ce or Co, the atomic ratio of said oxide to said oxy acid being 2.5 to 12 and (2) a salt of an oxy acid, is brought into contact with (B) a solid adsorbent capable of adsorbing the heteropoly acid and/or its salt in the presence of (C) at least one solvent for purification selected from hydrocarbons having 3 to 15 carbon atoms and halogenated hydrocarbons having 1 to 15 carbon atoms.
Claim 4
Dependent Claim
153 words
A process for purifying a polyoxytetramethylene ether wherein (A) a polyoxytetramethylene ether having a molecular weight of 500 to 5000 or a mixture of said polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol, said polyoxytetramethylene ether or said mixture containing a heteropoly acid and/or its salt; said heteropoly acid being (1) an oxy acid formed by condensation of at least one oxide of Mo, W or V with an oxy acid of P, Si, As, Ge, B, Ti, Ce or Co, the atomic ratio of said oxide to said oxy acid being 2.5 to 12 and (2) a salt of an oxy acid, is brought into contact with (B) a solid adsorbent capable of adsorbing the heteropoly acid and/or its salt in the presence of (C) at least one solvent for purification selected from hydrocarbons having 3 to 15 carbon atoms and halogenated hydrocarbons having 1 to 15 carbon atoms.
Claim 5
Dependent Claim
162 words
a process according to claim 1 or claim 2, wherein the polyoxytetramethylene ether or the mixture of polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol, or neopentyl glycol is a polymerization mixture composed mainly of a polyoxytetramethylene ether having polyoxytetramethylene chains in the molecule and tetrahydrofuran, and the solvent for purification selected from hydrocarbons having 3 to 15 carbon atoms or halogenated hydrocarbons having 1 to 15 carbon atoms is at least one solvent for purification selected from hydrocarbons having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith, tetrahydrofuran is recovered by distillation after separation of the phase composed mainly of the heteropoly acid and/or its salt, and the residual mixture of the said polyalkylene ether and the the said solvent for purification is subjected to phase separation to thereby separate the liquid composed mainly of the said polyalkylene ether from most of the said solvent for purification.
Claim 6
Dependent Claim
34 words
A process according to claim 3, wherein the polyoxytetramethylene ether having polyoxytetramethylene chains in the molecule is obtained by a polymerization with the use of the heteropoly acid and/or its salt as a catalyst.
Claim 7
Dependent Claim
20 words
A process according to claim 3, wherein the solvent for purification existing in the said polyoxytetramethylene ether is further evaporated.
Claim 8
Dependent Claim
19 words
A process according to claim 3, wherein the polyoxytetramethylene ether having polyoxytetramethylene chains in the molecule is polyoxytetramethylene glycol.
Claim 9
Dependent Claim
117 words
A process according to claim 3, wherein the polyoxytetramethylene ether or the mixture of polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol to be purified is brought into contact with a solid adsorbent capable of adsorbing the heteropoly acid and/or its salt at either one of the stage after the phase composed mainly of the heteropoly acid and/or its salt is separated by precipitation by adding at least one solvent for purification selected from hydrocarbons having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith and the stage after further tetrahydrofuran is recovered by distillation or at the both stages thereof.
Claim 10
Dependent Claim
117 words
A process according to claim 6, wherein the polyoxytetramethylene ether or the mixture of polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol to be purified is brought into contact with a solid adsorbent capable of adsorbing the heteropoly acid and/or its salt at either one of the stage after the phase composed mainly of the heteropoly acid and/or its salt is separated by precipitation by adding at least one solvent for purification selected from hydrocarbons having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith and the stage after further tetrahydrofuran is recovered by distillation or at the both stages thereof.
Claim 11
Dependent Claim
45 words
A process according to claim 2, wherein the solid adsorbent is one or a mixture of two or more adsorbents selected from: (A) activated charcoal; (B) aluminum oxides; (C) oxides, hydroxides and carbonates of magnesium, calcium and rare earth metals; and (D) basic ion-exchange resins.
Claim 12
Dependent Claim
45 words
A process according to claim 7, wherein the solid adsorbent is one or a mixture of two or more adsorbents selected from: (A) activated charcoal; (B) aluminum oxides; (C) oxides, hydroxides and carbonates of magnesium, calcium and rare earth metals; and (D) basic ion-exchange resins.
Claim 13
Dependent Claim
56 words
A process according to claim 3, wherein, after tetrahydrofuran is recovered by distillation, the solvent for purification which is recovered by the phase separation, either as such or after the purification operation such as distillation, is utilized again as the solvent for purification for separating the phase composed mainly of the heteropoly acid and/or its salt.
Claim 14
Dependent Claim
56 words
A process according to claim 7, wherein, after tetrahydrofuran is recovered by distillation, the solvent for purification which is recovered by the phase separation, either as such or after the purification operation such as distillation, is utilized again as the solvent for purification for separating the phase composed mainly of the heteropoly acid and/or its salt.
Claim 15
Dependent Claim
28 words
A process according to claim 1 or claim 2, wherein the separated phase composed mainly of the heteropoly acid and/or its salt is reused as the polymerization catalyst.
Claim 16
Dependent Claim
25 words
A process according to claim 3, wherein the separated phase composed mainly of the heteropoly acid and/or its salt is reused as the polymerization catalyst.
Claim 17
Dependent Claim
25 words
A process according to claim 7, wherein the separated phase composed mainly of the heteropoly acid and/or its salt is reused as the polymerization catalyst.
Claim 18
Dependent Claim
29 words
A process according to claim 2, wherein the purified polymer after contact with the solid adsorbent is treated under reduced pressure at a temperature of 100° to 180° C.
Claim 19
Dependent Claim
29 words
A process according to claim 7, wherein the purified polymer after contact with the solid adsorbent is treated under reduced pressure at a temperature of 100° to 180° C.
Claim 20
Dependent Claim
125 words
A process according to claim 1 or claim 2, wherein the polyoxytetramethylene ether or the mixture of the polyoxytetramethylene ether and tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol containing the heteropoly acid and/or its salt is (1) the reaction mixture obtained by the polymerization of tetrahydrofuran alone, or the copolymerization of tetrahydrofuran and propylene oxide, ethylene glycol or neopentyl glycol, with the use of the heteropoly acid and/or its salt as a catalyst, and the subsequent removal of the phase containing said catalyst from the reaction mixture (1) when the reaction mixture (1) consists of two phases, one of said phases containing said catalyst or (2) the concentrated reaction mixture obtained by recovering at least a part of unreacted monomer from reaction mixture (1).
Claim 21
Dependent Claim
54 words
A process according to claim 1 or claim 2, wherein the hydrocarbon having 3 to 15 carbon atoms or the halogenated hydrocarbon having 3 to 15 carbon atoms is one or a mixture of two or more selected from pentane, hexane, heptane, octane, nonane, decane, undecane, dodecane, cyclopentane, cyclohexane, cycloheptane, cyclooctane, cyclononane and cyclodecane.
Claim 22
Dependent Claim
47 words
A process according to claim 3, wherein the hydrocarbon having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith is one or a mixture of two or more selected from n-heptane, octane and nonane.
Claim 23
Dependent Claim
47 words
A process according to claim 7, wherein the hydrocarbon having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith is one or a mixture of two or more selected from n-heptane, octane and nonane.
Claim 24
Dependent Claim
41 words
A process according to claim 3, wherein the hydrocarbon having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith is one or a mixture of octane and nonane.
Claim 25
Dependent Claim
41 words
A process according to claim 7, wherein the hydrocarbon having not more than 15 carbon atoms which has a boiling point higher than tetrahydrofuran and does not form an azeotropic mixture therewith is one or a mixture of octane and nonane.
Claim 26
Dependent Claim
23 words
The process of claim 1 or 2 wherein said tetrahydrofuran, propylene oxide, ethylene glycol or neopentyl glycol contains a small amount of water.
References Cited (Backward Citations)
US2751419A
Cited
US4137396A
Cited
JPS55165918A
Cited
JPS5616524A
Cited
US4460796A
Cited
US4480124A
Cited
US4500705A
Cited
US4528364A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-29 | 1990-12-29 | 1991-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-29 | 1994-12-29 | 1995-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-29 | 1998-12-29 | 1999-06-30 | $7700.00 | Window Closed / Lapsed |