Water absorbent styrene-acrylic acid copolymers
Assignee: BASF SE
•
Filing: 1986-04-21
•
Granted: 1987-06-30
•
Expires: 2006-04-21
Abstract
Abstract Water absorbing, cross-linked acrylate resin copolymers are prepared by aqueous polymerization of (A) acrylic acid neutralized 70 to 100 mole percent for example with ammonia, and/or caustic alkali and/or an amine; with (B) styrene and/or methyl methacrylate in an amount of 1% to 25% based on the weight of acrylic acid or acrylate, and (C) acrylamide in a mole ratio of 70 to 100 mole percent (A) to 30:0 mole percent (C); and (D) a water miscible or a water soluble polyvinyl monomer in an amount of 0.001 to 0.3 weight percent based on the total weight of (A), (B), (C) and (D).
Inventors
- 👤 William Alexander
- 👤 Barbara R. Regan
- 👤 Mark Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:53
CPC Classifications
C; C08; C08F; C08F220/00; C08F220/02; C08F220/04; C08F220/06; A; A61; A61L; A61L15/00; A61L15/16; A61L15/42; A61L15/60; B; B01; B01J; B01J20/00; B01J20/22; B01J20/26
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
137 words
A process for preparing a solid water absorbing resin comprising mixing a monomer solution of (A) acrylic acid neutralized 70-100 mole percent; (B) styrene in an amount of 1% to 25% based on the weight of acrylic acid and (C) a water-miscible to water-soluble polyvinyl monomer in a combined concentration of (A), (B) and (C) of at least 30 wt. %; with water to form a mixed monomer solution wherein the monomers of the mixed monomer solution consist essentially of (A) and (B) and (C) and initiating polymerization of monomers (A), (B) and (C) such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, cross-linking and to drive off sufficient water to obtain a solid cross-linked resin having a water content of 15 percent by weight or less.
Claim 2
Dependent Claim
137 words
A process for preparing a solid water absorbing resin comprising mixing a monomer solution of (A) acrylic acid neutralized 70-100 mole percent; (B) styrene in an amount of 1% to 25% based on the weight of acrylic acid and (C) a water-miscible to water-soluble polyvinyl monomer in a combined concentration of (A), (B) and (C) of at least 30 wt. %; with water to form a mixed monomer solution wherein the monomers of the mixed monomer solution consist essentially of (A) and (B) and (C) and initiating polymerization of monomers (A), (B) and (C) such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, cross-linking and to drive off sufficient water to obtain a solid cross-linked resin having a water content of 15 percent by weight or less.
Claim 3
Dependent Claim
30 words
A process as defined in claim 1 wherein the combined concentration of the monomers (A), (B) and (C) is at least 30 wt. % and less than 70 wt. %.
Claim 4
Dependent Claim
23 words
A process as defined in claim 1 wherein the mixed monomer solution has a temperature of 20° to 85° C. prior to polymerization.
Claim 5
Dependent Claim
20 words
A process as defined in claim 1 wherein monomer (C) is selected from the group consisting of N,N-methylenebisacrylamide and N,N-methylenebismethacrylamide.
Claim 6
Dependent Claim
32 words
A process as defined in claim 1 wherein the mixed monomer solution contains 1 to 10 wt. % of an organic solvent based on the weight of monomers (A), (B) and (C).
Claim 7
Dependent Claim
26 words
A process as defined in claim 1 wherein the mixed monomer solution further contains an organic solvent having a boiling point of 40° to 150° C.
Claim 8
Dependent Claim
168 words
A process for preparing a solid, water absorbing, cross-linked resin comprising: combining a monomer mixture of (A) potassium acrylate; (B) styrene in an amount of 1% to 25% based on the amount of acrylate computed based on the weight of acrylic acid; and (C) a polyvinyl monomer, with water in an amount of at least 30 combined weight percent of (A) plus (B) plus (C) based on the total weight of (A) plus (B) plus (C) plus water to form a monomer mixture wherein the monomers of the the monomer mixture consist essentially of (A), (B) and (C); adding a polymerization initiator to said monomer mixture capable of initiating, and in an amount sufficient to initiate polymerization of said monomer mixture; copolymerizing said monomer mixture while utilizing the exothermic heat of reaction as substantially the only non-ambient energy source to drive water away from said polyacrylate resin copolymer to form said cross-linked resin copolymer having a water content sufficiently low to be powdered without an intermediate drying step.
Claim 9
Dependent Claim
168 words
A process for preparing a solid, water absorbing, cross-linked resin comprising: combining a monomer mixture of (A) potassium acrylate; (B) styrene in an amount of 1% to 25% based on the amount of acrylate computed based on the weight of acrylic acid; and (C) a polyvinyl monomer, with water in an amount of at least 30 combined weight percent of (A) plus (B) plus (C) based on the total weight of (A) plus (B) plus (C) plus water to form a monomer mixture wherein the monomers of the the monomer mixture consist essentially of (A), (B) and (C); adding a polymerization initiator to said monomer mixture capable of initiating, and in an amount sufficient to initiate polymerization of said monomer mixture; copolymerizing said monomer mixture while utilizing the exothermic heat of reaction as substantially the only non-ambient energy source to drive water away from said polyacrylate resin copolymer to form said cross-linked resin copolymer having a water content sufficiently low to be powdered without an intermediate drying step.
Claim 10
Dependent Claim
35 words
The process of claim 7 further including the step of adjusting the temperature of the monomer mixture to a temperature of 25° to 85° C. prior to adding said polymerization initiator to said monomer mixture.
Claim 11
Dependent Claim
27 words
The process of claim 8 wherein said polymerization initiator is added in an amount of at least 0.5% total by weight of monomers (A), (B) and (C).
Claim 12
Dependent Claim
33 words
The process of claim 8 wherein the water content of said cross-linked resin copolymer is not greater than about 10% by weight as recovered from the polymerized mixture, without an additional drying step.
Claim 13
Dependent Claim
30 words
The process of claim 8 further including combining a non-aqueous solvent having a boiling point of 40°-150° C. with said monomers (A), (B) and (C) to form a porous resin.
Claim 14
Dependent Claim
17 words
The process of claim 8 including the step of pulverizing said cross-linked resin to form a powder.
Claim 15
Independent Claim
160 words
A method of manufacturing a resin composition comprising mixing a monomer solution of (A) acrylic acid, neutralized 70 to 100 mole percent, (B) styrene in an amount of 1% to 25% based on the weight of acrylic acid and (C) acrylamide in a mole ratio of (A):(C) in the range of 70:30 to 100:0; (D) a water soluble or water miscible polyvinyl monomer cross-linking agent in an amount of 0.001 to 0.3 percent by weight of (A) plus (B) plus (C); and water to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of (A), (B), (C) and (D); and initiating polymerization of monomers (A), (B) and (C) such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, cross-linking and to drive off sufficient water to form a water absorbing cross-linked polyacrylate resin composition having a water content of 15 percent by weight or less.
Claim 16
Independent Claim
160 words
A method of manufacturing a resin composition comprising mixing a monomer solution of (A) acrylic acid, neutralized 70 to 100 mole percent, (B) styrene in an amount of 1% to 25% based on the weight of acrylic acid and (C) acrylamide in a mole ratio of (A):(C) in the range of 70:30 to 100:0; (D) a water soluble or water miscible polyvinyl monomer cross-linking agent in an amount of 0.001 to 0.3 percent by weight of (A) plus (B) plus (C); and water to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of (A), (B), (C) and (D); and initiating polymerization of monomers (A), (B) and (C) such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, cross-linking and to drive off sufficient water to form a water absorbing cross-linked polyacrylate resin composition having a water content of 15 percent by weight or less.
Claim 17
Dependent Claim
37 words
The method of claim 13 wherein the water content of said cross-linked polyacrylate resin copolymer is not greater than about 10% by weight as recovered from the mixed monomer solution after copolymerization, without an additional drying step.
Claim 18
Dependent Claim
24 words
The method of claim 13 including depositing said monomer mixture including said initiator onto a support surface in sheet form for polymerization and cross-linking.
Claim 19
Independent Claim
189 words
A method of absorbing water comprising mixing a monomer solution of (A) acrylic acid, neutralized 70 to 100 mole percent, (B) styrene in an amount of 1% to 25% based on the weight of acrylic acid and (C) acrylamide in a mole ratio of acrylic acid: acrylamide in the range of 70:30 to 100:0; (D) a water soluble or water miscible polyvinyl monomer cross-linking agent in an amount of 0.001 to 0.3 percent by weight of (A) plus (B) plus (C); and water to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of (A), (B), (C) and (D) and the monomer concentration is below 70 percent by weight of the monomer solution prior to polymerization initiation; and initiating polymerization of monomers (A) and (B) such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, cross-linking and to drive off sufficient water to form a water absorbing cross-linked polyacrylate resin having a water content of 15 percent by weight or less, and thereafter contacting said resin with water to absorb water into said resin.
Claim 20
Independent Claim
189 words
A method of absorbing water comprising mixing a monomer solution of (A) acrylic acid, neutralized 70 to 100 mole percent, (B) styrene in an amount of 1% to 25% based on the weight of acrylic acid and (C) acrylamide in a mole ratio of acrylic acid: acrylamide in the range of 70:30 to 100:0; (D) a water soluble or water miscible polyvinyl monomer cross-linking agent in an amount of 0.001 to 0.3 percent by weight of (A) plus (B) plus (C); and water to form a mixed monomer solution, wherein the monomers of the mixed monomer solution consist essentially of (A), (B), (C) and (D) and the monomer concentration is below 70 percent by weight of the monomer solution prior to polymerization initiation; and initiating polymerization of monomers (A) and (B) such that during polymerization, the exothermic heat of reaction is substantially the only heat energy used to accomplish polymerization, cross-linking and to drive off sufficient water to form a water absorbing cross-linked polyacrylate resin having a water content of 15 percent by weight or less, and thereafter contacting said resin with water to absorb water into said resin.
References Cited (Backward Citations)
US4342858A
Cited
US4552938A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-29 | 1990-12-29 | 1991-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-29 | 1994-12-29 | 1995-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-29 | 1998-12-29 | 1999-06-30 | $7700.00 | Window Closed / Lapsed |