Polymeric compositions
Assignee: Ciba Specialty Chemicals Water Treatments Ltd
•
Filing: 1985-08-15
•
Granted: 1987-06-30
•
Expires: 2005-08-15
Abstract
Abstract A polymer of an ethylenically unsaturated monomer containing a pendant hydrophobic group and, optionally, other monomers such as (meth) acrylic acid, ethyl acrylate or acrylamide is provided as a stable, substantially anhydrous dispersion containing at least 40% by weight of the polymer in a continuous phase of a non-aqueous liquid. The polymer in the dispersion generally includes acid groups and is neutralized, preferably with ammonia or a volatile amine. The dispersion can be made by reverse phase polymerization of an aqueous blend of monomers, followed by dehydration, or by making the polymer from a water insoluble blend of monomers by oil in water emulsion polymerization, dispersing the resultant oil in water emulsion into the non-aqueous liquid, and then dehydrating. The monomer including the hydrophobic group is preferably an allyl ether.
Inventors
- 👤 Adrian Allen
- 👤 David Farrar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 00:17
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08F; C08F2/00; C08F2/32; C08J3/09; C08J2300/00; C08J2300/10; C08J2300/14
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
122 words
A dispersion in a continuous liquid phase of a polymer that is formed by polymerising (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer by a polymerisation technique selected from reverse phase polymerisation and oil-in-water emulsion polymerisation and in which the dispersion is stable, substantially anhydrous and contains at least 40% by weight of the polymer, and the continuous liquid phase is a non-aqueous liquid.
Claim 2
Dependent Claim
122 words
A dispersion in a continuous liquid phase of a polymer that is formed by polymerising (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer by a polymerisation technique selected from reverse phase polymerisation and oil-in-water emulsion polymerisation and in which the dispersion is stable, substantially anhydrous and contains at least 40% by weight of the polymer, and the continuous liquid phase is a non-aqueous liquid.
Claim 3
Dependent Claim
116 words
In a dispersion of a polymer in a non-aqueous liquid and that is stable, substantially anhydrous and contains at least 40% by weight of the polymer the improvement in which the polymer has been formed by copolymerising (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer by a polymerisation technique selected from reverse phase polymerisation and oil-in-water emulsion polymerisation.
Claim 4
Dependent Claim
116 words
In a dispersion of a polymer in a non-aqueous liquid and that is stable, substantially anhydrous and contains at least 40% by weight of the polymer the improvement in which the polymer has been formed by copolymerising (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer by a polymerisation technique selected from reverse phase polymerisation and oil-in-water emulsion polymerisation.
Claim 5
Dependent Claim
65 words
A dispersion according to claim 1 in which the monomer (b) is present and includes acidic monomer, the polymer is substantially water insoluble and non-swellable when in free acid form but is a water soluble or swellable thickening polymer when in alkali metal, ammonium or amine salt form, and in which the polymer in the dispersion is in alkali metal, ammonium, or amine salt form.
Claim 6
Dependent Claim
27 words
A dispersion according to claim 1 in which monomer (b) is present and is an acidic monomer and the polymer is neutralised with ammonia or volatile amine.
Claim 7
Dependent Claim
20 words
A dispersion according to claim 1 including a suspension stabiliser that is an amphipathic copolymer of hydrophilic and hydrophobic monomers.
Claim 8
Dependent Claim
12 words
A dispersion according to claim 1 including a high HLB oil-in-water emulsifier.
Claim 9
Independent Claim
192 words
A method of making a stable anhydrous dispersion in a non-aqueous liquid of a polymer formed by polymerising (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer, the method comprising forming an aqueous dispersion of the polymer in the non-aqueous liquid by a polymerisation technique selected from (1) reverse phase polymerisation of a water soluble blend of monomers in the non-aqueous liquid to form the aqueous dispersion and (2) oil-in-water emulsion polymerisation of a water insoluble blend of monomers and dispersion of the resultant emulsion into the non-aqueous liquid, and wherein the amount of polymer is at least 40% based on the combined weight of polymer and non-aqueous liquid, and then dehydrating the aqueous dispersion to form a stable substantially anhydrous dispersion containing at least 40% by weight of the polymer in the non-aqueous liquid.
Claim 10
Independent Claim
192 words
A method of making a stable anhydrous dispersion in a non-aqueous liquid of a polymer formed by polymerising (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer, the method comprising forming an aqueous dispersion of the polymer in the non-aqueous liquid by a polymerisation technique selected from (1) reverse phase polymerisation of a water soluble blend of monomers in the non-aqueous liquid to form the aqueous dispersion and (2) oil-in-water emulsion polymerisation of a water insoluble blend of monomers and dispersion of the resultant emulsion into the non-aqueous liquid, and wherein the amount of polymer is at least 40% based on the combined weight of polymer and non-aqueous liquid, and then dehydrating the aqueous dispersion to form a stable substantially anhydrous dispersion containing at least 40% by weight of the polymer in the non-aqueous liquid.
Claim 11
Dependent Claim
30 words
A dispersion according to claim 1 in which monomer a is an amide of ester of an ethylenically unsaturated acid or a meth(allyl)ether and monomer b is an acrylic monomer.
Claim 12
Dependent Claim
67 words
A dispersion according to claim 1 in which the monomer (a) has the formula CH 2 ═CR'CH 2 OB n A m R where R' is H or Me, A is propoxy or butoxy, B is ethoxy, n is a positive integer of from 2 to 100, m is zero or an integer less than n, R is a hydrophobic group of at least 8 carbon atoms.
Claim 13
Dependent Claim
28 words
A dispersion according to claim 1 in which the monomer (b) is (meth)acrylic acid alone or blended with acrylamide or ethyl acrylate, optionally with a cross linking agent.
Claim 14
Dependent Claim
133 words
A process of making a stable anhydrous dispersion comprising forming a stable dispersion in non-aqueous liquid of an aqueous blend of ethylenically unsaturated monomer and polymerising by reverse phase polymerisation to form a stable dispersion of aqueous polymer in the non-aqueous liquid and dehydrating the dispersion to form a stable anhydrous dispersion containing at least 40% by weight of the polymer, characterized in that the monomer comprises (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer.
Claim 15
Dependent Claim
133 words
A process of making a stable anhydrous dispersion comprising forming a stable dispersion in non-aqueous liquid of an aqueous blend of ethylenically unsaturated monomer and polymerising by reverse phase polymerisation to form a stable dispersion of aqueous polymer in the non-aqueous liquid and dehydrating the dispersion to form a stable anhydrous dispersion containing at least 40% by weight of the polymer, characterized in that the monomer comprises (a) 1 to 100% by weight ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of at least 8 carbon atoms and (b) 0 to 99% other copolymerisable ethylenically unsaturated monomer.
Claim 16
Dependent Claim
33 words
A process according to claim 11 in which the monomer (a) is the ester or amide of an ethylenically unsaturated acid, or (meth)allyl ether, with a hydroxy terminated surfactant of HLB above 8.
Claim 17
Dependent Claim
173 words
A process of making a stable dispersion in a continuous liquid phase of a polymer obtained by copolymerising (a) ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of least 8 carbon atoms and (b) other copolymerisable ethylenically unsaturated monomer including acidic monomer characterized in that the polymer is formed from a water insoluble blend of the monomers by oil in water emulsion polymerisation while the acidic monomer is in free acid form and the oil in water emulsion is then dispersed into non-aqueous liquid to form an aqueous dispersion of polymer in the non-aqueous liquid, the aqueous dispersion is then dehydrated to form a stable, substantially anhydrous dispersion containing at least 40% by weight of the polymer, and the acidic groups are converted to alkali metal, ammonium or amine form during or after forming the aqueous dispersion.
Claim 18
Dependent Claim
173 words
A process of making a stable dispersion in a continuous liquid phase of a polymer obtained by copolymerising (a) ethylenically unsaturated monomer containing a group --B n A m R where B is ethoxy, n is a positive integer of at least 2, A is propoxy or butoxy, m is zero or an integer less than n, and R is a hydrophobic group of least 8 carbon atoms and (b) other copolymerisable ethylenically unsaturated monomer including acidic monomer characterized in that the polymer is formed from a water insoluble blend of the monomers by oil in water emulsion polymerisation while the acidic monomer is in free acid form and the oil in water emulsion is then dispersed into non-aqueous liquid to form an aqueous dispersion of polymer in the non-aqueous liquid, the aqueous dispersion is then dehydrated to form a stable, substantially anhydrous dispersion containing at least 40% by weight of the polymer, and the acidic groups are converted to alkali metal, ammonium or amine form during or after forming the aqueous dispersion.
Claim 19
Dependent Claim
30 words
A process according to claim 11 or claim 13 in which the aqueous dispersion of polymer includes a suspension stabiliser that is an amphipathic copolymer of hydrophilic and hydrophobic monomers.
Claim 20
Dependent Claim
69 words
A process according to claim 11 or claim 13 in which monomer a has the formula CH 2 ═CR'CH 2 OB n A m R where R' is H or Me, A is propoxy or butoxy, B is ethoxy, n is a positive integer of from 2 to 100, m is zero or an integer less than n, R is a hydrophobic group of at least 8 carbon atoms.
Claim 21
Dependent Claim
15 words
A dispersion according to claim 1 in which n is an integer greater than 5.
Claim 22
Dependent Claim
15 words
A dispersion according to claim 2 in which n is an integer greater than 5.
Claim 23
Dependent Claim
15 words
A process according to claim 11 in which n is an integer greater than 5.
Claim 24
Dependent Claim
15 words
A process according to claim 13 in which n is an integer greater than 5.
Claim 25
Dependent Claim
38 words
A process according to claim 7 in which the polymer was formed from a water insoluble blend of monomers by oil in water emulsion polymerisation and the aqueous dispersion was formed by dispersing this emulsion into non-aqueous liquid.
Claim 26
Dependent Claim
15 words
A process according to claim 7 in which n is an integer greater than 5.
Claim 27
Dependent Claim
16 words
A dispersion according to claim 1 in which the polymer is made by oil-in-water emulsion polymerisation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-29 | 1990-12-29 | 1991-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-29 | 1994-12-29 | 1995-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-29 | 1998-12-29 | 1999-06-30 | $7700.00 | Window Closed / Lapsed |