Process for producing a shaped electroconductive thermoplastic resin composition article
Assignee: Marubishi Oil Chemical Co Ltd
•
Filing: 1985-12-27
•
Granted: 1987-06-23
•
Expires: 2005-12-27
Abstract
Abstract A shaped electroconductive thermoplastic resin composition article having a preferable surface appearance is produced by a process including (1) mixing a matrix resinous material containing 100 parts by weight of a thermoplastic resin and, optionally, 120 parts by weight or less of a flame x retardant additive and 40 parts by weight or less of a flame retardant synergistic additive, with 1 to 15% based on the weight of the matrix resinous material, of stainless steel fibers having a length of 2.5 to 7.5 mm and adhered to each other with a thermoplastic resinous adhesive to form a number of bundles; (2) kneading the resultant mixture at an elevated temperature at which the matrix resinous material is melted and (3) shaping the kneaded mixture into a desired form, the kneading the shaping procedures being carried out so that the stainless steel fibers are uniformly dispersed in the melted matrix resinous material and the dispersed stainless steel fibers have an average length of 0.5 to 2.0 mm. The ratio of the average length of the dispersed and sheared stainless steel fibers to the length of the stainless steel fiber bundles is preferably in a range of 1/6 to 1/3.
Inventors
- 👤 Kazuto Wakita
- 👤 Kazuo Tsuchiya
- 👤 Kazuaki Kobayashi
- 👤 Ken Higashitsuji
- 👤 Teruhisa Kojima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:46
CPC Classifications
C; C08; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/06; H; H01; H01B; H01B1/00; H01B1/20; H01B1/22
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
164 words
A process for producing a shaped electroconductive thermoplastic resin compostion article comprising the steps of: mixing a matrix resinous material containing a thermoplastic resin with 1 to 15%, based on the weight of the matrix resinous material, of stainless steel fibers having a length of 2.5 to 7.5 mm and in the form of a number of bundles in which the stainless steel fibers are adhered to each other with a thermoplastic resin adhesive; and kneading the resultant mixutre at an elevated temperature at which the matrix resinous material is melted; and shaping the resultant kneaded mixture into a desired form, said kneading and shaping procedures being carried out to an extent that the stainless steel fibers are released from the bundles, are uniformly dispersed in the melted matrix resinuous maerial and are sheared into a decreased average length of from 1/6 to 1/3 of the original length of the stainless steel fiber bundles and having a length of from 0.5 to 2.0 mm.
Claim 2
Dependent Claim
164 words
A process for producing a shaped electroconductive thermoplastic resin compostion article comprising the steps of: mixing a matrix resinous material containing a thermoplastic resin with 1 to 15%, based on the weight of the matrix resinous material, of stainless steel fibers having a length of 2.5 to 7.5 mm and in the form of a number of bundles in which the stainless steel fibers are adhered to each other with a thermoplastic resin adhesive; and kneading the resultant mixutre at an elevated temperature at which the matrix resinous material is melted; and shaping the resultant kneaded mixture into a desired form, said kneading and shaping procedures being carried out to an extent that the stainless steel fibers are released from the bundles, are uniformly dispersed in the melted matrix resinuous maerial and are sheared into a decreased average length of from 1/6 to 1/3 of the original length of the stainless steel fiber bundles and having a length of from 0.5 to 2.0 mm.
Claim 3
Dependent Claim
31 words
The process as claimed in claim 1, wherein the thermoplastic resin adhesive is in an amount of from 1% to 20% based on the weight of the stainless steel fiber bundles.
Claim 4
Dependent Claim
30 words
The process as claimed in claim 1, wherein the thermoplastic resin adhesive comprises at least one polymer selected from the group consisting of vinyl acetate-containing copolyemrs and saturated polyester copolymers.
Claim 5
Dependent Claim
20 words
The process as claimed in claim 1, wherein the stainless steel fibers have a thickness of 2 to 20 microns.
Claim 6
Dependent Claim
20 words
The process as claimed in claim 1, wherein each stainless steel fiber bundle includes 1,000 to 50,000 stainless steel fibers.
Claim 7
Dependent Claim
43 words
The process as claimed in claim 1, wherein the thermoplastic resin comprises at least one molding resin selected from the group consisting of nylon 6, nylon 66, nylon 11, nylon 12, acrylonitrile-butylene-styrene copolymers, polypropylene, polyesters, high impact polystyrene compositions, polycarbonates, and polyphenylene oxide.
Claim 8
Dependent Claim
33 words
The process as claimed in claim 1, wherein the matrix resinous material further contains 120 parts by weight or less of a flame retardant additive per 100parts by weight of the thermoplastic resin.
Claim 9
Dependent Claim
20 words
The process as claimed in claim 6, wherein the flame retardant additive comprises at least one flame retardant decabromodiphenyl compound.
Claim 10
Dependent Claim
23 words
The process as claimed in claim 8, wherein the flame retardant decabromodiphenyl compound is selected from the group consisting of decabromodiphenylether and decabromodiphenyl.
Claim 11
Dependent Claim
36 words
The process as claimed in claim 7, wherein the matrix resinous material still further contains 40 parts by weight or less of a flame retardant synergistic additive per 100 parts by weight of the thermoplastic resin.
Claim 12
Dependent Claim
16 words
The process as claimed in claim 10, wherein the flame retardant synergistic additive comprises antimony trioxide.
Claim 13
Dependent Claim
22 words
The process as claimed in claim 1, wherein in the mixing procedure, the matrix resinous material is in the form of pellets.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-22 | 1990-12-22 | 1991-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-22 | 1994-12-22 | 1995-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-22 | 1998-12-22 | 1999-06-23 | $7700.00 | Window Closed / Lapsed |