US4673543A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of producing hardened inorganic products
Assignee: Panasonic Electric Works Co Ltd
•
Filing: 1986-02-05
•
Granted: 1987-06-16
•
Expires: 2006-02-05
Abstract
Abstract A method of producing hardened inorganic products is characterized in that a hydraulic material comprising slag as an effective component is mixed with gypsum and water, and mixture is then shaped and aged at an internal temperature of 50° to 100° C. to produce TSH therein and to cause hydration and hardening. The resulting hardened inorganic product features a light weight and improved fire resistance, freezing resistance, dimensional stability and strength.
Inventors
- 👤 Tamotsu Akasaka
- 👤 Shinichi Tomiuchi
- 👤 Kazuo Seto
- 👤 Kenichi Matsui
- 👤 Yasushi Sawada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:57
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B28/06; C04B28/065; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y02W30/91
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
120 words
A method of producing a hardened inorganic product characterized by: admixing a hydraulic material comprising slag as an effective component, gypsum, MSH and water, the proportion of said hydraulic material comprising slag as an active component, said gypsum and said MSH being set such that the amount of TSH to be generated is 5 to 50% by weight in hardened product matrix and such that the weight ratio of said gypsum to said MSH is between 0.7 to 10; shaping said mixture; and aging said shaped product in a humid atmosphere keeping the temperature of the product at about 50° to 100° C. to simultaneously generate TSH from said gypsum and MSH and hydrate the slag to harden the product.
Claim 2
Independent Claim
120 words
A method of producing a hardened inorganic product characterized by: admixing a hydraulic material comprising slag as an effective component, gypsum, MSH and water, the proportion of said hydraulic material comprising slag as an active component, said gypsum and said MSH being set such that the amount of TSH to be generated is 5 to 50% by weight in hardened product matrix and such that the weight ratio of said gypsum to said MSH is between 0.7 to 10; shaping said mixture; and aging said shaped product in a humid atmosphere keeping the temperature of the product at about 50° to 100° C. to simultaneously generate TSH from said gypsum and MSH and hydrate the slag to harden the product.
Claim 3
Dependent Claim
56 words
A method according to claim 1, wherein to 100 weight parts of hardened product matrix are added 0.5 to 2 weight parts of one or mixture selected from the group consisting of alkali-resistant glass fiber and synthetic fiber, 4 to 8 weight parts of pulp, and 2 to 15 weight parts of rockwool as reinforcing components.
Claim 4
Dependent Claim
14 words
A method according to claim 2, wherein shaping is performed by a sheet-forming method.
Claim 5
Dependent Claim
19 words
A method according to claim 3, wherein said sheet-forming method is practiced with an elongated screen type sheet-forming machine.
Claim 6
Dependent Claim
56 words
A method according to claim 1, wherein to 100 weight parts of hardened product matrix are added 0.5 to 2 weight parts of one or mixture selected from the group consisting of alkali-resistant glass fiber and synthetic fiber, 4 to 8 weight parts of pulp and 2 to 15 weight parts of rockwool as reinforcing components.
Claim 7
Dependent Claim
14 words
A method according to claim 5, wherein shaping is performed by a sheet-forming method.
Claim 8
Dependent Claim
19 words
A method according to claim 6, wherein said sheet-forming method is practiced with an elongated screen type sheet-forming machine.
Claim 9
Independent Claim
25 words
A method according to any one of claims 1 and 2 to 7, wherein said humid atmosphere has a relative humidity of 80 to 100%.
Claim 10
Independent Claim
39 words
A method according to any one of claims 1 and 2 to 7, wherein to 100 weight parts of said matrix is added 5 to 30 weight parts of inorganic filler component having a diameter of 500 or less.
Claim 11
Dependent Claim
21 words
A method according to claim 1, wherein the weight ratio of said gypsum to said MSH is between 1.0 to 4.0.
References Cited (Backward Citations)
US3202522A
Cited
US4045533A
Cited
US3872204A
Cited
JPS5157693A
Cited
US4148781A
Cited
JPS53121021A
Cited
JPS53121020A
Cited
US4310358A
Cited
US4389359A
Cited
JPS5796808A
Cited
US4407769A
Cited
JPS5820763A
Cited
US4427610A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-15 | 1990-12-15 | 1991-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-15 | 1994-12-15 | 1995-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-15 | 1998-12-15 | 1999-06-16 | $7700.00 | Window Closed / Lapsed |