Method for increasing the molecular weight of polyamides and polyesteramides

Claim 2

A process for increasing the molecular weight of a preformed thermoplastic polymer characterized by recurring amide linkages and having been prepared by the reaction of an organic diisocyanate and a dicarboxylic acid which process comprises fluxing and homogenizing said thermoplastic polymer with an effective amount of an organic diisocyanate reagent at a temperature of at least about 150° C.

Claim 3

A process according to claim 1 wherein the amount of said diisocyanate reagent is from about 0.1 to about 10 percent by weight.

Claim 4

A process according to claim 1 wherein said fluxing and homogenizing is carried out at a temperature of from about 150° C. to about 350° C.

Claim 5

A process acccrding to claim 1 wherein said diisocyanate reagent is an aromatic diisocyanate.

Claim 6

A process according to claim 1 wherein said diisocyanate reagent is employed as a solution in a liquid carrier.

Claim 7

A process according to claim 1 wherein said fluxing and homogenizing is carried out in a melt-extruder apparatus.

Claim 8

A process according to claim 1 wherein said fluxing and homogenizing is carried out in a vented twin-screw extruder.

Claim 9

A process according to claim 1 wherein said thermoplastic polymer comprises the product of the reaction of at least one aromatic diisocyanate and a dicarboxylic acid selected from the group consisting of aromatic dicarboxylic acids, aliphatic dicarboxylic acids, dicarboxylic acid terminated polyesters, dicarboxylic acid terminated polyethers, and mixtures of any two or more such acids.

Claim 10

A process according to claim 1 wherein said thermoplastic polymer has been prepared from said diisocyanate and said dicarboxylic acid in substantially stoichiometric proportions.

Claim 11

A process according to claim 1 wherein said thermoplastic polymer contains from 0 to about 20 percent by weight of solvent and has been prepared from said diisocyanate and said dicarboxylic acid in the proportions of from about 0.90 to about 0.99 equivalent per one equivalent respectively.

Claim 12

A process according to claim 1 wherein said thermoplastic polymer has been prepared from 4,4'-methylenebis(phenyl isocyanate) and a dicarboxylic acid mixture comprising adipic and azelaic acids and said added diisocyanate is selected from 4,4'-methylenebis(phenyl isocyanate) or liquefied form thereof.

Claim 13

A process according to claim 1 wherein said thermoplastic polymer has been prepared from 4,4'-methylenebis(phenyl isocyanate) and a dicarboxylic acid mixture comprising azelaic acid and azelaic acid terminated poly(hexamethylene adipate) and said added diisocyanate is selected from 4,4'-methylenebis(phenyl isocyanate) or liquefied form thereof.

Claim 14

A process according to claim 1 wherein said thermoplastic polymer has been prepared from 4,4'-methylenebis(phenyl isocyanate) and a dicarboxylic acid mixture comprising azelaic, adipic, and isophthalic acids and said added diisocyanate is selected from 4,4'-methylenebis(phenyl isocyanate) or liquefied form thereof.

Claim 15

A process for increasing the molecular weight of, and, optionally removing solvent from, a preformed thermoplastic polymer containing from 0 to about 20 percent by weight of solvent said polymer characterized by recurring amide linkages and having been prepared by the reaction of from about 0.90 to about 0.99 equivalent of at least one aromatic diisocyanate with about one equivalent of at least one dicarboxylic acid which process comprises: (i) fluxing said thermoplastic polymer at a temperature of from about 150° C. to about 350° C. in a first mixing and heating zone of a vented twin-screw extruder; (ii) adding into said fluxed thermoplastic polymer via an inlet port of said extruder from about 0.1 to about 10 percent by weight of an aromatic diisocyanate; (iii) fluxing and homogenizing the resulting mixture at a temperature of from about 150° C. to about 350° C.; (iv) venting the carbon dioxide and solvent, when present, in a vented zone during said fluxing and homogenizing; and (v) removing the resulting polymer from said extruder via a shaping zone.

Claim 16

A process for increasing the molecular weight of, and, optionally removing solvent from, a preformed thermoplastic polymer containing from 0 to about 20 percent by weight of solvent said polymer characterized by recurring amide linkages and having been prepared by the reaction of from about 0.90 to about 0.99 equivalent of at least one aromatic diisocyanate with about one equivalent of at least one dicarboxylic acid which process comprises: (i) fluxing said thermoplastic polymer at a temperature of from about 150° C. to about 350° C. in a first mixing and heating zone of a vented twin-screw extruder; (ii) adding into said fluxed thermoplastic polymer via an inlet port of said extruder from about 0.1 to about 10 percent by weight of an aromatic diisocyanate; (iii) fluxing and homogenizing the resulting mixture at a temperature of from about 150° C. to about 350° C.; (iv) venting the carbon dioxide and solvent, when present, in a vented zone during said fluxing and homogenizing; and (v) removing the resulting polymer from said extruder via a shaping zone.

Claim 17

A process according to claim 14 wherein the recited steps are carried out continuously.

Claim 18

A process according to claim 15 wherein said thermoplastic polymer containing from about 1 to about 10 percent by weight of tetramethylene sulfone is prepared from 4,4'-methylenebis(phenyl isocyanate) and a mixture of adipic and azelaic acids, and said added diisocyanate is a liquefied form of 4,4'-methylenebis(phenyl isocyanate) dissolved in trixylyl phosphate as carrier.

Claim 19

A process according to claim 15 wherein said thermoplastic polymer containing from about 1 to about 10 percent by weight of tetramethylene sulfone is prepared from a mixture of 4,4'-methylenebis(phenyl isocyanate) with 2,4-toluenediisocyanate and a mixture of isophthalic and azelaic acids, and said added diisocyanate is 4,4'-methylenebis(phenyl isocyanate).