Method of strengthening glass article formed of float glass by ion exchange
Assignee: Central Glass Co Ltd
•
Filing: 1986-03-07
•
Granted: 1987-06-09
•
Expires: 2006-03-07
Abstract
Abstract The invention relates to a method of strengthening a glass article formed of sheet glass produced by the float process. The strengthening method includes a known ion exchange treatment to replace alkali metal ions in the surface layers of the glass with, e.g., alkali metal ions larger in ionic radius such as potassium ions. To prevent warping of the glass article during the ion exchange treatment by the influence of a metal element such as tin used as the molten metal in the float process and diffused into one surface of the sheet glass, the glass article is pretreated by contacting at least said surface with an external source of sodium ions and/or lithium ions and heating the glass article together with the external source of the alkali metal ions at 350°-650° C. for 0.01-100 hr. The pretreatment is neither preceded nor followed by grinding or polishing of said surface of the glass. By incorporating the pretreatment, the ion exchange strengthening can be accomplished to a high degree without degrading flatness and surface smoothness of the glass even when the glass thickness is not more than about 3 mm.
Inventors
- 👤 Shinichi Aratani
- 👤 Masaaki Katano
- 👤 Takeshi Mizoguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:09
CPC Classifications
C; C03; C03C; C03C21/00; C03C21/001; C03C21/002; G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/133337; Y; Y10; Y10T; Y10T428/00; Y10T428/31; Y10T428/315
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
209 words
A method of chemically strengthening a glass article which is formed of a sheet glass produced by the float process and has a first surface which was in contact with the surface of a molten metal bath used in the float process and a second or opposite surface, the method comprising the steps of: (a) contacting at least said first surface of the glass article with an external source of ions of at least one alkali metal selected from the group consisting of Na and Li and which comprises a prncipal alkali metal in the glass composition of the glass sheet, and heating the glass article together with the external source of alkali metal ions at a temperature in the range from 350° to 650° C. for a time in the range from 0.01 to 100 hr; and (b) strengthening the glass article after the treatment at step (a) by exchange of ions of said at least one alkali metal present in surface layers of glass article with ions of another alkali metal, which is different from any of said at least one alkali metal and is larger in ionic radius than the principal alkali metal in the glass composition of the glass sheet, supplied from another external source.
Claim 2
Independent Claim
209 words
A method of chemically strengthening a glass article which is formed of a sheet glass produced by the float process and has a first surface which was in contact with the surface of a molten metal bath used in the float process and a second or opposite surface, the method comprising the steps of: (a) contacting at least said first surface of the glass article with an external source of ions of at least one alkali metal selected from the group consisting of Na and Li and which comprises a prncipal alkali metal in the glass composition of the glass sheet, and heating the glass article together with the external source of alkali metal ions at a temperature in the range from 350° to 650° C. for a time in the range from 0.01 to 100 hr; and (b) strengthening the glass article after the treatment at step (a) by exchange of ions of said at least one alkali metal present in surface layers of glass article with ions of another alkali metal, which is different from any of said at least one alkali metal and is larger in ionic radius than the principal alkali metal in the glass composition of the glass sheet, supplied from another external source.
Claim 3
Dependent Claim
50 words
A method according to claim 1, wherein said external source at step (a) is a molten salt bath, the treatment of step (a) being performed by keeping the glass article immersed in said molten salt bath so as to contact both said first and second surfaces with the molten salt.
Claim 4
Dependent Claim
105 words
A method according to claim 1, wherein step (a) comprises the sub-steps of immersing the glass article in a molten salt bath which comprises said external source in molten state so as to contact both said first and second surfaces with said external source in molten state, soon withdrawing the glass article from said molten salt bath, then cooling the glass article to solidify said external source adherent to the glass article, removing the solidified external source from said second surface of the glass article, heating the glass article at said temperature for said time while said external source is adherent to said first surface.
Claim 5
Dependent Claim
76 words
A method according to claim 1. wherein step (a) comprises the sub-steps of introducing the glass article into a molten salt bath which comprises said external source in molten state so as to contact only said first surface with said external source in molten state, soon taking up the glass article from said molten salt bath, heating the glass article at said temperature for said time while said external source is adherent to said first surface.
Claim 6
Dependent Claim
65 words
A method according to claim 1, wherein step (a) comprises the sub-steps of contacting at least said first surface of the glass article with an aqueous solution in which said external source is dissolved, drying the glass article so as to leave said external source in solid phase on at least said first surface, thereafter heating the glass article at said temperature for said time.
Claim 7
Dependent Claim
20 words
A method according to claim 1, wherein said external source at step (a) is in the form of a vapor.
Claim 8
Dependent Claim
32 words
A method according to claim 1, wherein said external source at step (a) comprises a sodium salt selected from the group consisting of sodium nitrate, sodium nitrite, sodium sulfate and sodium phosphate.
Claim 9
Dependent Claim
32 words
A method according to claim 1, wherein said external source at step (a) comprises a lithium salt selected from the group consisting of lithium nitrate, lithium nitrite, lithium sulfate and lithium phosphate.
Claim 10
Dependent Claim
21 words
A method according to claim 1, wherein said temperature at step (a) is in the range from 400° to 600° C.
Claim 11
Dependent Claim
21 words
A method according to claim 9, wherein said temperature at step (a) is in the range from 0.1 to 50 hr.
Claim 12
Dependent Claim
13 words
A method according to claim 1, wherein said another alkali metal is potassium.
Claim 13
Dependent Claim
14 words
A method according to claim 1, wherein said sheet glass is a soda-lime-silicate glass.
Claim 14
Dependent Claim
19 words
A method according to claim 1, wherein the thickness of said sheet glass is not more than 3 mm.
Claim 15
Dependent Claim
14 words
A method according to claim 1, wherein the glass article is a glass disk.
References Cited (Backward Citations)
US3453095A
Cited
GB1094431A
Cited
US3533888A
Cited
US3990877A
Cited
GB1249365A
Cited
US3630704A
Cited
GB1317023A
Cited
US3798013A
Cited
JPS5417765A
Cited
EP0001957A1
Cited
JPS58115043A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-08 | 1990-12-08 | 1991-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-08 | 1994-12-08 | 1995-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-08 | 1998-12-08 | 1999-06-09 | $7700.00 | Window Closed / Lapsed |