Process for making crumb silicone material
Assignee: Dow Silicones Corp
•
Filing: 1986-03-03
•
Granted: 1987-06-02
•
Expires: 2006-03-03
Abstract
Abstract Mixing under low shear vinyl-containing polyorganosiloxane, a silicon-bonded hydrogen polysiloxane and a platinum catalyst, and continue mixing produces a crumb which has an extrusion rate of at least 50 grams per minute through an orifice of 0.5 inch diameter under a pressure of 345 kilopascals and compression points of less than 1035 kilopascals. The crumb is useful in hydraulic applications.
Inventors
- 👤 Earl W. Beck
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:52
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08G77/22; C08G77/24; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
212 words
A method of making a silicone crumb comprising mixing under low shear the following ingredients which cure to a material with a low internal shear strength and a low durometer, (A) a vinyl-containing polyorganosiloxane consisting essentially of units selected from the group consisting of diorganosiloxane units, monoorganosilsesquioxane units, and triorganosiloxy units in which the organic radicals are monovalent hydrocarbon radicals or monovalent halogenated hydrocarbon radicals, in the polyorganosiloxane the organic radicals being such that at least 0.1 weight percent of them are vinyl radicals, (B) a silicon-bonded hydrogen containing polysiloxane in which there is at least 0.5 weight percent silicon-bonded hydrogen atoms, the valences of the silicon atoms not being satisfied by divalent oxygen atoms or silicon-bonded hydrogen atoms are satisfied by monovalent hydrocarbon radicals or monovalent halogenated hydrocarbon radicals, (C) a platinum catalyst for the hydrosilation reaction of (A) and (B), the mixing being continued until a crumb which is in a fine particulate form which exhibits an extrusion rate of at least 50 grams per minute through an orifice of 0.5 inch diameter under a pressure of 345 kilopascals and compression points of less than 1035 kilopascals for the first two compressions, said mixing being sufficient to thoroughly mix the ingredients before significant cure takes place and crumb is formed.
Claim 2
Independent Claim
212 words
A method of making a silicone crumb comprising mixing under low shear the following ingredients which cure to a material with a low internal shear strength and a low durometer, (A) a vinyl-containing polyorganosiloxane consisting essentially of units selected from the group consisting of diorganosiloxane units, monoorganosilsesquioxane units, and triorganosiloxy units in which the organic radicals are monovalent hydrocarbon radicals or monovalent halogenated hydrocarbon radicals, in the polyorganosiloxane the organic radicals being such that at least 0.1 weight percent of them are vinyl radicals, (B) a silicon-bonded hydrogen containing polysiloxane in which there is at least 0.5 weight percent silicon-bonded hydrogen atoms, the valences of the silicon atoms not being satisfied by divalent oxygen atoms or silicon-bonded hydrogen atoms are satisfied by monovalent hydrocarbon radicals or monovalent halogenated hydrocarbon radicals, (C) a platinum catalyst for the hydrosilation reaction of (A) and (B), the mixing being continued until a crumb which is in a fine particulate form which exhibits an extrusion rate of at least 50 grams per minute through an orifice of 0.5 inch diameter under a pressure of 345 kilopascals and compression points of less than 1035 kilopascals for the first two compressions, said mixing being sufficient to thoroughly mix the ingredients before significant cure takes place and crumb is formed.
Claim 3
Dependent Claim
21 words
The method in accordance with claim 1 further comprising extruding the crumb through a particle sizer to make uniform particle distribution.
Claim 4
Dependent Claim
27 words
The method in accordance with claim 1 in which the ingredients cure to a material with a durometer on the Shore OO scale of less than 65.
Claim 5
Dependent Claim
27 words
The method in accordance with claim 2 in which the ingredients cure to a material with a durometer on the Shore OO scale of less than 65.
Claim 6
Dependent Claim
22 words
The method in accordance with claim 1 in which the ingredients are mixed and heated to shorten the cure and crumb time.
Claim 7
Dependent Claim
22 words
The method in accordance with claim 2 in which the ingredients are mixed and heated to shorten the cure and crumb time.
Claim 8
Dependent Claim
22 words
The method in accordance with claim 3 in which the ingredients are mixed and heated to shorten the cure and crumb time.
Claim 9
Dependent Claim
22 words
The method in accordance with claim 4 in which the ingredients are mixed and heated to shorten the cure and crumb time.
Claim 10
Dependent Claim
37 words
The method in accordance with claim 3 in which the ingredients cure to a material which has no measurable tensile strength at break and no measurable elongation at break as determined by the test procedure of ASTM-D-412.
Claim 11
Dependent Claim
37 words
The method in accordance with claim 4 in which the ingredients cure to a material which has no measurable tensile strength at break and no measurable elongation at break as determined by the test procedure of ASTM-D-412.
Claim 12
Dependent Claim
37 words
The method in accordance with claim 7 in which the ingredients cure to a material which has no measurable tensile strength at break and no measurable elongation at break as determined by the test procedure of ASTM-D-412.
Claim 13
Dependent Claim
37 words
The method in accordance with claim 8 in which the ingredients cure to a material which has no measurable tensile strength at break and no measurable elongation at break as determined by the test procedure of ASTM-D-412.
Claim 14
Dependent Claim
50 words
The method in accordance with claim 5 further comprising carrying out the curing and crumbing process in a closed chamber and reducing the pressure within the chamber during the curing and crumbing process thereby removing unreacted and unreactable low molecular species and providing a crumb with a low weight loss.
Claim 15
Dependent Claim
50 words
The method in accordance with claim 6 further comprising carrying out the curing and crumbing process in a closed chamber and reducing the pressure within the chamber during the curing and crumbing process thereby removing unreacted and unreactable low molecular species and providing a crumb with a low weight loss.
Claim 16
Dependent Claim
50 words
The method in accordance with claim 7 further comprising carrying out the curing and crumbing process in a closed chamber and reducing the pressure within the chamber during the curing and crumbing process thereby removing unreacted and unreactable low molecular species and providing a crumb with a low weight loss.
Claim 17
Dependent Claim
50 words
The method in accordance with claim 8 further comprising carrying out the curing and crumbing process in a closed chamber and reducing the pressure within the chamber during the curing and crumbing process thereby removing unreacted and unreactable low molecular species and providing a crumb with a low weight loss.
Claim 18
Dependent Claim
50 words
The method in accordance with claim 11 further comprising carrying out the curing and crumbing process in a closed chamber and reducing the pressure within the chamber during the curing and crumbing process thereby removing unreacted and unreactable low molecular species and providing a crumb with a low weight loss.
Claim 19
Dependent Claim
50 words
The method in accordance with claim 12 further comprising carrying out the curing and crumbing process in a closed chamber and reducing the pressure within the chamber during the curing and crumbing process thereby removing unreacted and unreactable low molecular species and providing a crumb with a low weight loss.
Claim 20
Dependent Claim
22 words
The method in accordance with claim 1 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 21
Dependent Claim
22 words
The method in accordance with claim 2 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 22
Dependent Claim
22 words
The method in accordance with claim 4 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 23
Dependent Claim
22 words
The method in accordance with claim 6 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 24
Dependent Claim
22 words
The method in accordance with claim 8 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 25
Dependent Claim
22 words
The method in accordance with claim 12 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 26
Dependent Claim
22 words
The method in accordance with claim 18 in which the crumb exhibits an extrusion rate of at least 800 grams per minute.
Claim 27
Dependent Claim
20 words
The method in accordance with claim 5 further comprising a platinum catalyst inhibitor is present in the ingredients being mixed.
Claim 28
Dependent Claim
20 words
The method in accordance with claim 6 further comprising a platinum catalyst inhibitor is present in the ingredients being mixed.
Claim 29
Dependent Claim
20 words
The method in accordance with claim 7 further comprising a platinum catalyst inhibitor is present in the ingredients being mixed.
Claim 30
Dependent Claim
20 words
The method in accordance with claim 8 further comprising a platinum catalyst inhibitor is present in the ingredients being mixed.
Claim 31
Dependent Claim
20 words
The method in accordance with claim 9 further comprising a platinum catalyst inhibitor is present in the ingredients being mixed.
Claim 32
Dependent Claim
20 words
The method in accordance with claim 25 further comprising a platinum catalyst inhibitor is present in the ingredients being mixed.
References Cited (Backward Citations)
US3843601A
Cited
US4528156A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-01 | 1990-12-01 | 1991-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-01 | 1994-12-01 | 1995-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-01 | 1998-12-01 | 1999-06-02 | $7700.00 | Window Closed / Lapsed |