Preparation of ferromagnetic chromium dioxide
Assignee: Emtec Magnetics GmbH
•
Filing: 1985-08-07
•
Granted: 1987-06-02
•
Expires: 2005-08-07
Abstract
Abstract Ferromagnetic chromium dioxide is prepared by converting oxides of trivalent and hexavalent chromium under superatmospheric pressure and at elevated temperatures in the presence of water and with the addition of an antimony compound as a modifier and, if required, further additives in an amount of not more than 15% by weight, by a method in which the antimony compound is present in the form of a water-soluble salt whose anion contains one or more organic molecular moieties which are oxidized in concentrated chromic acid.
Inventors
- 👤 Manfred Ohlinger
- 👤 Norbert Mueller
- 👤 Peter Rudolf
- 👤 Eugen Wettstein
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:55
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; C; C01; C01G; C01G37/00; C01G37/02; C01G37/027; G11B5/70626; G11B5/70636; C01P; C01P2004/00; C01P2004/10; C01P2004/80; C01P2004/82; C01P2006/00; C01P2006/11; C01P2006/12; C01P2006/42
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
177 words
A process for the preparation of a ferromagnetic chromium dioxide by converting oxides of trivalent and hexavalent chromium under a pressure of from 100 to 700 bar and at a temperature of from 200° to 600° C. in the presence of water, an antimony modifier and acicular iron oxide particles or acicular iron particles in an amount of not more than 15% by weight comprising adding an antimony compound as a modifier in the form of a water-soluble salt in an amount of at least 0.1% by weight but less than 4% by weight, based on the resulting chromium dioxide and said iron oxide or iron particles to a mixture of hexavalent chromium oxide and water, adding trivalent chromium oxide thereto and subjecting the resultant mixture to said pressure and temperature, with a proviso that the water-soluble antimony compound contains at least one organic molecular moiety anion which is oxidized by the oxide of hexavalent chromium with the evolution of gas when said antimony compound is added to a mixture of said hexavalent chromium oxide and water.
Claim 2
Dependent Claim
177 words
A process for the preparation of a ferromagnetic chromium dioxide by converting oxides of trivalent and hexavalent chromium under a pressure of from 100 to 700 bar and at a temperature of from 200° to 600° C. in the presence of water, an antimony modifier and acicular iron oxide particles or acicular iron particles in an amount of not more than 15% by weight comprising adding an antimony compound as a modifier in the form of a water-soluble salt in an amount of at least 0.1% by weight but less than 4% by weight, based on the resulting chromium dioxide and said iron oxide or iron particles to a mixture of hexavalent chromium oxide and water, adding trivalent chromium oxide thereto and subjecting the resultant mixture to said pressure and temperature, with a proviso that the water-soluble antimony compound contains at least one organic molecular moiety anion which is oxidized by the oxide of hexavalent chromium with the evolution of gas when said antimony compound is added to a mixture of said hexavalent chromium oxide and water.
Claim 3
Dependent Claim
16 words
The process of claim 1, wherein the antimony compound used as a modifier is antimony tartrate.
Claim 4
Dependent Claim
35 words
The process of claim 1, wherein the antimony compound used as a modifier is potassium antimonyl tartrate, and is added in an amount of less than 2% by weight, based on the resulting chromium dioxide.
Claim 5
Dependent Claim
32 words
The process of claim 3, wherein the potassium antimonyl tartrate used as a modifier is employed in an amount of from 0.1 to 1% by weight, based on the resulting chromium dioxide.
Claim 6
Dependent Claim
46 words
The process of claim 3, wherein acicular iron oxide particles in the form of α- or γ-FeOOH, Fe 3 O 4 or γ- or α-Fe 2 O 3 , in an amount of from 0.5 to 15% by weight, based on the chromium dioxide, are used.
Claim 7
Dependent Claim
41 words
The process of claim 3, wherein acicular iron particles having a BET specific surface area of from 5 to 40 m 2 /g are used, in an amount of from 0.4 to 10% by weight, based on the resulting chromium dioxide.
Claim 8
Dependent Claim
46 words
The process of claim l, wherein acicular iron oxide particles in the form of α- or γ-FeOOH, Fe 3 O 4 or γ- or α-Fe 2 O 3 , in an amount of from 0.5 to 15% by weight, based on the chromium dioxide, are used.
Claim 9
Dependent Claim
41 words
The process of claim 1, wherein acicular iron particles having a BET specific surface area of from 5 to 40 m 2 /g are used in an amount of from 0.4 to 10% by weight, based on the resulting chromium dioxide.
References Cited (Backward Citations)
US3034988A
Cited
US3278263A
Cited
US3449073A
Cited
US3687851A
Cited
US3778373A
Cited
US4340494A
Cited
US4524008A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-06-01 | 1990-12-01 | 1991-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-06-01 | 1994-12-01 | 1995-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-06-01 | 1998-12-01 | 1999-06-02 | $7700.00 | Window Closed / Lapsed |