Process for the preparation of elastic polyurethane flexible foams usable in cold-mold techniques to produce molded articles
Assignee: BASF SE
•
Filing: 1986-05-30
•
Granted: 1987-05-26
•
Expires: 2006-05-30
Abstract
Abstract The invention is a process for the preparation of elastic polyurethane flexible foams having densities from approximately 25 to 60 kg/m 3 , and producing molded articles in closed molds at temperatures from 25° to 80° C., comprising reacting (A) an organic polyisocyanate prepolymer having an isocyanate content from 6 to 20 percent by weight prepared by reacting a toluene diisocyanate and/or a diphenylmethane diisocyanate with a di- to tetrafunctional polyether polyol having a hydroxyl number from 20 to 50 and oxyethylene terminal group content of at least 10 to 30 percent by weight (B) a mixture of compounds containing reactive hydrogen atoms, comprising a mixture of (a) from 55 to 89.5 parts by weight of at least one di- to tetrafunctional polyether polyol having a hydroxyl number of from 20 to 80 and less than 10 percent by weight terminal oxyethylene groups, (b) from 0.5 to 20 parts by weight of at least one alkanolamine, and (c) from 10 to 25 parts by weight water, in the presence of (C) a blowing agent, (D) a catalyst, and optionally (E) auxiliaries and/or additives.
Inventors
- 👤 Gerhard Mueller
- 👤 Matthias Marx
- 👤 Wolfgang Jarre
- 👤 Edwin Baumann
- 👤 Ingolf Buethe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:02
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; Y; Y10; Y10S; Y10S521/00; Y10S521/914
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
94 words
A process for the preparation of elastic polyurethane flexible foams comprising reacting (A) an organic polyisocyanate prepolymer (B) a compound having reactive hydrogen atoms comprising a mixture of (a) at least one di- to tetrafunctional polyether polyol having less than 10 percent by weight terminal oxyethylene groups based on the total content of said groups and having a hydroxyl number of from 20 to 80, (b) an alkanolamine, and (c) from 10 to 25 percent by weight water, based on the total weight of the mixture, (C) a blowing agent, and (D) a catalyst.
Claim 2
Dependent Claim
94 words
A process for the preparation of elastic polyurethane flexible foams comprising reacting (A) an organic polyisocyanate prepolymer (B) a compound having reactive hydrogen atoms comprising a mixture of (a) at least one di- to tetrafunctional polyether polyol having less than 10 percent by weight terminal oxyethylene groups based on the total content of said groups and having a hydroxyl number of from 20 to 80, (b) an alkanolamine, and (c) from 10 to 25 percent by weight water, based on the total weight of the mixture, (C) a blowing agent, and (D) a catalyst.
Claim 3
Dependent Claim
23 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein auxiliaries and additives are added to the reaction components.
Claim 4
Dependent Claim
91 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein said compound having reactive hydrogen atoms (B) comprises a mixture comprising (a) from 55 to 89.5 parts by weight of at least one di- to tetrafunctional polyether polyol having less than 10 percent by weight terminal oxyethylene groups and a hydroxyl number from 20 to 80, (b) from 0.5 to 20 parts by weight of at least one alkanolamine, and (c) from 10 to 25 parts by weight water, based on the total weight of the mixture.
Claim 5
Dependent Claim
82 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein the organic polyisocyanate prepolymer (A) has an isocyanate content of from 6 to 20 percent by weight and is prepared by reacting toluene diisocyanates and/or diphenylmethane diisocyanates with at least one di- to tetrafunctional polyether polyol having a hydroxyl number of from 20 to 50 and a terminal oxyethylene group content of at least 10 to 30 percent by weight and at least 50 percent primary hydroxyl groups.
Claim 6
Dependent Claim
33 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein di- and/or trialkanolamines having 2 to 3 carbon atoms in the alkylene radical are used as the alkanolamines (B,b).
Claim 7
Dependent Claim
22 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein the isocyanate index is from 70 to 120.
Claim 8
Dependent Claim
28 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein the reaction is performed in the absence of halogenated hydrocarbons as a blowing agent.
Claim 9
Dependent Claim
31 words
The process for the preparation of elastic polyurethane flexible foams of claim 1 wherein the reaction is performed in a closed mold at a temperature range of 25° to 80° C.
Claim 10
Dependent Claim
22 words
The process of claim 1 wherein the elastic polyurethane flexible foam has a density of from 25 to 60 kg/m 3 .
Claim 11
Dependent Claim
25 words
An elastic polyurethane flexible foam with a density of from 25 to 60 kg/m 3 , obtained by the processes of claims 1 through 6.
Claim 12
Dependent Claim
31 words
An elastic molded article comprising a polyurethane flexible foam with a density from 25 to 60 kg/m 3 , obtained in closed molds by the processes of claims 1 through 7.
References Cited (Backward Citations)
US4559366A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-25 | 1990-11-24 | 1991-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-25 | 1994-11-24 | 1995-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-25 | 1998-11-24 | 1999-05-26 | $7700.00 | Window Closed / Lapsed |