Amorphous silicon electrophotographic sensitive member
Assignee: Kyocera Corp
•
Filing: 1984-03-28
•
Granted: 1987-05-19
•
Expires: 2004-03-28
Abstract
Abstract The invention relates to improvements in an electrophotographic sensitive member having a photoconductive layer formed with amorphous silicon produced by glow discharge decomposition or sputtering. An electrophotographic sensitive member is formed by laminating an amorphous silicon barrier layer and an amorphous photoconductive layer successively on an electrically conductive substrate, the first mentioned layer containing an impurity of Group IIIa of Periodic Table of Elements, or nitrogen and impurity of Group IIIa of same Table, and also containing oxygen within a range of 0.1 to 20.0 atomic % at the point of the layer and in a progressively decreasing pattern throughout the rest thereof. Constructed as such, the photosensitive member has an increased photosensitivity to near-infrared beams, a large charge-holding capability, and low-rate dark attenuation characteristics. In addition, it is less expensive to manufacture.
Inventors
- 👤 Takao Kawamura
- 👤 Hideaki Iwano
- 👤 Naooki Miyamoto
- 👤 Yasuo Nishiguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:58
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08; G03G5/082; G03G5/08214; G03G5/08235; G03G5/08242
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
256 words
An electrophotographic sensitive member comprising: an electrically conductive substrate; a 0.2 to 5.0 micron thick amorphous silicon barrier layer interfacing the substrate, the barrier layer containing from 50 to 500 ppm of a Group III (a) impurity, the barrier layer including 0.1 to 20.0 atomic percent of oxygen, the atomic pecentage of oxygen decreasing throughout the barrier layer from the interface with the substrate, the barrier layer including from 10 to 40 atomic percent of hydrogen; a 5-100 micron amorphous silicon photoconductive layer interfacing the barrier layer, the photoconductive layer containing 0.0001 to 0.05 atomic percent of oxygen or oxygen and nitrogen, from 10 to 40 atomic percent of hydrogen and from 10 to 20,000 ppm of a Group III (a) impurity; and a 0.05 to 1.0 micron amorphous silicon protective layer interfacing the photoconductive layer, the protective layer having from 1 to 60 atomic percent oxygen or oxygen and nitrogen, from 10 to 40 atomic percent hydrogen, and from 0 to 20,000 ppm of a Group III (a) impurity, wherein the oxygen or oxygen plus nitrogen content of the barrier layer at a point farthest from the substrate is approximately equal to the oxygen or oxygen plus nitrogen content of the photoconductive layer at a point closest to the barrier layer, and wherein the oxygen or oxygen plus nitrogen content of the protective layer at a point closest to the photoconductive layer is approximately equal to the oxygen or oxygen plus nitrogen content of the photoconductive layer at a point closest to the protective layer.
Claim 2
Dependent Claim
256 words
An electrophotographic sensitive member comprising: an electrically conductive substrate; a 0.2 to 5.0 micron thick amorphous silicon barrier layer interfacing the substrate, the barrier layer containing from 50 to 500 ppm of a Group III (a) impurity, the barrier layer including 0.1 to 20.0 atomic percent of oxygen, the atomic pecentage of oxygen decreasing throughout the barrier layer from the interface with the substrate, the barrier layer including from 10 to 40 atomic percent of hydrogen; a 5-100 micron amorphous silicon photoconductive layer interfacing the barrier layer, the photoconductive layer containing 0.0001 to 0.05 atomic percent of oxygen or oxygen and nitrogen, from 10 to 40 atomic percent of hydrogen and from 10 to 20,000 ppm of a Group III (a) impurity; and a 0.05 to 1.0 micron amorphous silicon protective layer interfacing the photoconductive layer, the protective layer having from 1 to 60 atomic percent oxygen or oxygen and nitrogen, from 10 to 40 atomic percent hydrogen, and from 0 to 20,000 ppm of a Group III (a) impurity, wherein the oxygen or oxygen plus nitrogen content of the barrier layer at a point farthest from the substrate is approximately equal to the oxygen or oxygen plus nitrogen content of the photoconductive layer at a point closest to the barrier layer, and wherein the oxygen or oxygen plus nitrogen content of the protective layer at a point closest to the photoconductive layer is approximately equal to the oxygen or oxygen plus nitrogen content of the photoconductive layer at a point closest to the protective layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-18 | 1990-11-17 | 1991-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-18 | 1994-11-17 | 1995-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-18 | 1998-11-17 | 1999-05-19 | $7700.00 | Window Closed / Lapsed |