Sliding surface of composite nickel-plated sliding member
Assignee: Toyota Motor Corp
•
Filing: 1985-02-27
•
Granted: 1987-05-19
•
Expires: 2005-02-27
Abstract
Abstract A composite nickel plated sliding surface is obtained by the formation of a composite nickel plating film on a sliding surface of an automobile part such as an engine cylinder or piston by electroless nickel plating. The plating film contains at least one member of wear resistant particles having an average particle size of 0.1 to 1.0μ selected from SiC, TiC, WC, BC 4 , TiN, Al 2 O 3 or the like, and also at least one member of lubricating particles having an average particle size of 1 to 10μ selected from BN, MoS 2 , and Teflon. The nickel plating bath is adjusted to have a phosphorus concentration of 0.5 to 12%. When the matrix of the nickel plating film has a phosphorus concentration of 0.5 to 5%, the film hardness is improved.
Inventors
- 👤 Hideo Yano
- 👤 Keiichi Kano
- 👤 Hitoshi Ozawa
- 👤 Shinji Kato
- 👤 Yoshio Takagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:52
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/32; C23C18/34; C23C18/36; F; F02; F02B; F02B75/00; F02B75/02; F02B2075/022; F02B2075/027; F05; F05C; F05C2201/00; F05C2201/02; F05C2201/021; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12472; Y10T428/12493; Y10T428/12535; Y10T428/12576; Y10T428/12736; Y10T428/1275; Y10T428/12771; Y10T428/12861; Y10T428/12944
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
80 words
A composite plated sliding surface of a sliding member, on which a nickel alloy film containing water resistant particles and lubricating particles are dispersed is formed by using a nickel plating bath having a phosphorus concentration of 0.5 to 12%, comprising silicon carbide having a cubic crystalline structure particles as the wear resistant particles having an average particle size of 0.1 to 1.0μ and boron nitride particles as the lubricating particles having an average particle size of 1 to 10μ.
Claim 2
Dependent Claim
80 words
A composite plated sliding surface of a sliding member, on which a nickel alloy film containing water resistant particles and lubricating particles are dispersed is formed by using a nickel plating bath having a phosphorus concentration of 0.5 to 12%, comprising silicon carbide having a cubic crystalline structure particles as the wear resistant particles having an average particle size of 0.1 to 1.0μ and boron nitride particles as the lubricating particles having an average particle size of 1 to 10μ.
Claim 3
Dependent Claim
23 words
A sliding surface according to claim 1, wherein a matrix of the nickel alloy film has a phosphorus concentration of 0.5 to 5%.
Claim 4
Independent Claim
107 words
A method of performing composite nickel plating on a sliding surface of a sliding member, comprising the steps of dispersing wear resistant particles and lubricating particles in a nickel plating bath adjusted to have a phosphorus concentration of 0.5 to 12%, in which the wear resistant particles having an average particle size of 0.1 to 1.0μ and being silicon carbide having cubic crystalline structure, and the lubricating particles having an average particle size of 1 to 10μ and being boron nitride; and forming a nickel alloy film containing the wear resistant particles and the lubricating particles on the sliding surface of said sliding member by electroless plating.
Claim 5
Independent Claim
107 words
A method of performing composite nickel plating on a sliding surface of a sliding member, comprising the steps of dispersing wear resistant particles and lubricating particles in a nickel plating bath adjusted to have a phosphorus concentration of 0.5 to 12%, in which the wear resistant particles having an average particle size of 0.1 to 1.0μ and being silicon carbide having cubic crystalline structure, and the lubricating particles having an average particle size of 1 to 10μ and being boron nitride; and forming a nickel alloy film containing the wear resistant particles and the lubricating particles on the sliding surface of said sliding member by electroless plating.
References Cited (Backward Citations)
DE390776C
Cited
US3617363A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-18 | 1990-11-17 | 1991-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-18 | 1994-11-17 | 1995-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-18 | 1998-11-17 | 1999-05-19 | $7700.00 | Window Closed / Lapsed |