Electrically conductive resinous bond and method of manufacture
Assignee: United States Department of Energy
•
Filing: 1985-03-29
•
Granted: 1987-05-19
•
Expires: 2005-03-29
Abstract
Abstract A method of bonding elements together with a bond of high strength and good electrical conductivity which comprises: applying an unfilled polyimide resin between surfaces of the elements to be bonded, heat treating said unfilled polyimide resin in stages between a temperature range of about 40 DEG to 365 DEG C. to form a strong adhesive bond between said elements, applying a metal-filled polyimide resin overcoat between said elements so as to provide electrical connection therebetween, and heat treating said metal-filled polyimide resin with substantially the same temperature profile as the unfilled polyimide resin. The present invention is also concerned with an adhesive, resilient, substantially void free bonding combination for providing a high strength, electrically conductive adhesive attachment between electrically conductive elements which comprises a major amount of an unfilled polyimide resin and a minor amount of a metal-filled polyimide resin.
Inventors
- 👤 Thomas M. Snowden, Jr.
- 👤 Barbara J. Wells
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 11:03
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; H01B1/22; C; C09; C09J; C09J5/00; C09J5/06; H01R; H01R4/00; H01R4/04; H03; H03H; H03H3/00; H03H3/007; H03H3/02; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/321; Y; Y10; Y10T; Y10T29/00; Y10T29/42; Y10T428/00; Y10T428/31504; Y10T428/31721
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
130 words
A method of bonding elements together with a bond of high strength and good electrical conductivity, which comprises: applying an unfilled polyimide resin on a surface of each element to be bonded; bringing and holding said surfaces together; heat treating said unfilled polyimide resin in stages over a temperature range of about 40° to 365° C. to form a strong adhesive bond between said element surfaces; applying metal-filled polyimide resin over an exposed edge of said heat treated resin layer and in contact with an unbonded area of each bonded element, said metal-filled resin constituting a separate layer from said unfilled resin layer and forming an electrical connection between said bonded elements; and heat treating said metal-filled polyimide resin at the same temperature range profile as the unfilled polyimide resin.
Claim 2
Independent Claim
130 words
A method of bonding elements together with a bond of high strength and good electrical conductivity, which comprises: applying an unfilled polyimide resin on a surface of each element to be bonded; bringing and holding said surfaces together; heat treating said unfilled polyimide resin in stages over a temperature range of about 40° to 365° C. to form a strong adhesive bond between said element surfaces; applying metal-filled polyimide resin over an exposed edge of said heat treated resin layer and in contact with an unbonded area of each bonded element, said metal-filled resin constituting a separate layer from said unfilled resin layer and forming an electrical connection between said bonded elements; and heat treating said metal-filled polyimide resin at the same temperature range profile as the unfilled polyimide resin.
Claim 3
Dependent Claim
31 words
The method as recited in claim 1, wherein the metal-filled polyimide resin is selected from the group consisting of a silver-filled polyimide resin, a good-filled polyimide resin, or a mixture thereof.
Claim 4
Dependent Claim
33 words
The method as recited in claim 1, wherein the metal-filled resin is applied so as to contact the top surface of one of the elements and the top surface of the other element.
Claim 5
Dependent Claim
32 words
The method as recited in claim 1, wherein the metal-filled polyimide resin is applied so as to contact the bottom surface of one element and the bottom surface of the other element.
Claim 6
Dependent Claim
27 words
The method as recited in claim 1, wherein one of the elements to be bonded is a crystal blank and the other element is a resonator clip.
Claim 7
Dependent Claim
37 words
The method as recited in claim 1, wherein the metal-filled polyimide resin is provided along the peripheral surfaces of the elements to be bonded together and the unfilled polyimide is disposed internal to said metal-filled polyimide resin.
Claim 8
Dependent Claim
129 words
The method as recited in claim 1, wherein said heat treating comprises: heating the unfilled polyimide resin in a first stage at a temperature of about 40° to 80° C. for about 3/4 to 11/4 hours to remove absorbed water; heating said resin in a second stage at a temperature of about 140° to 180° C. for about 3/4 to 11/4 hours to remove solvent; heating said resin in a third stage at a temperature of about 250° to 390° C. for about 13/4 to 21/4 hours to complete imidization; heating said resin in a fourth stage at a temperature of about 325° to 365° C. for about 3/4 to 11/4 hours to remove residual organics; and substantially repeating the same heat treatment profile for the metal-filled polyimide resin.
Claim 9
Dependent Claim
65 words
The method as recited in claim 7, wherein the heat treatments of the metal-filled and unfilled polyimide resins are conducted at the following stages: Stage 1 at about 50° C. for about 1 hour; Stage 2 at about 150° C. for about 1 hour; Stage 3 at about 275° C. for about 2 hours; and Stage 4 at about 345° C. for about 1 hour.
Claim 10
Dependent Claim
24 words
The process as recited in claim 7, wherein the heat treatment process is conducted at atmospheric pressure and in an atmosphere of dry nitrogen.
Claim 11
Dependent Claim
75 words
An adhesive, resilient, substantially void-free bonding combination for providing a high strength, electrically conductive adhesive attachment between electrically conductive elements, which comprises a major quantity of unfilled polyimide resin in the form of a layer-between the elements bonded and a minor quantity of a metal-filled polyimide resin further joining said elements, said metal-filled resin being in contact with an edge of said unfilled resin layer and forming a separate layer from said unfilled resin layer.
Claim 12
Dependent Claim
75 words
An adhesive, resilient, substantially void-free bonding combination for providing a high strength, electrically conductive adhesive attachment between electrically conductive elements, which comprises a major quantity of unfilled polyimide resin in the form of a layer-between the elements bonded and a minor quantity of a metal-filled polyimide resin further joining said elements, said metal-filled resin being in contact with an edge of said unfilled resin layer and forming a separate layer from said unfilled resin layer.
Claim 13
Dependent Claim
20 words
The bonding combination as recited in claim 10, wherein the metal-filled polyimide resin is a silver-filled or gold-filled polyimide resin.
Claim 14
Dependent Claim
26 words
The bonding combination as recited in claim 10, wherein the metal-filled polyimide resin is a mixture of a gold-filled polyimide resin and a silver-filled polyimide resin.
Claim 15
Dependent Claim
30 words
The bonding combination of claim 10, comprising about 80 to 90 weight % of the unfilled polyimide resin and about 10 to 20 weight % of the metal-filled polyimide resin.
Claim 16
Dependent Claim
92 words
A quartz crystal bonded to a mounting structure with a bonding assembly comprising a layer of unfilled polyimide resin between said crystal and said structure and, in contact with said unfilled resin layer and with said crystal and mounting structure, a separate layer of metal-filled polyimide resin, said unfilled resin constituting about 80 to 90% and said filled resin about 10 to 20% of the total weight of resin in the assembly, said bonding assembly providing a void-free, resilient, electrically conductive and strong bond between the quartz crystal and the mounting structure.
Claim 17
Dependent Claim
92 words
A quartz crystal bonded to a mounting structure with a bonding assembly comprising a layer of unfilled polyimide resin between said crystal and said structure and, in contact with said unfilled resin layer and with said crystal and mounting structure, a separate layer of metal-filled polyimide resin, said unfilled resin constituting about 80 to 90% and said filled resin about 10 to 20% of the total weight of resin in the assembly, said bonding assembly providing a void-free, resilient, electrically conductive and strong bond between the quartz crystal and the mounting structure.
Claim 18
Dependent Claim
21 words
The quartz crystal bonded to a mounting structure as recited in claim 14, wherein the mounting structure is a resonator clip.
Claim 19
Dependent Claim
30 words
The quartz crystal bonded to a mounting structure as recited in claim 14, wherein the metal-filled polyimide resin is a silver-filled polyimide resin, gold-filled polyimide resin, or a mixture thereof.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-18 | 1990-11-17 | 1991-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-18 | 1994-11-17 | 1995-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-18 | 1998-11-17 | 1999-05-19 | $7700.00 | Window Closed / Lapsed |