Ballistic spall liner
Assignee: United States Department of the Army
•
Filing: 1986-04-21
•
Granted: 1987-05-12
•
Expires: 2006-04-21
Abstract
Abstract A lightweight, economical, add-on armor plate, ballistic spall liner, installable on the inner surfaces of unprotected vehicles, structures, or other craft. The spall liner provides additional protection to vehicle occupants and internal equipment from the risk of injury or damage due to flying metallic debris, "spall", caused by ballistic damage to the vehicles or the structure's interior when a munitions-type projectile penetrates a wall. The spall liner is a laminate made from layers of high tensile strength, woven fabric such as polyaramid fabric or ballistic nylon which are bonded together with at least one reinforcing layer of martensite sheet steel interposed between the woven fabric layers. The spall liner controls the spall generated by the penetration of a munitions-type projectile by dissipating the projectile's force, framentizing the projectile, and trapping the fragments in the spall liner's interior.
Inventors
- 👤 Server Tasdemiroglu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:50
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/14; F; F41; F41H; F41H5/00; F41H5/02; F41H5/04; F41H5/0442; F41H5/0457; F41H5/0464; B32B2262/00; B32B2262/02; B32B2262/0261; B32B2307/00; B32B2307/50; B32B2307/54; B32B2571/00; B32B2571/02; Y; Y10; Y10S; Y10S428/00; Y10S428/911
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
314 words
A laminated spall liner for controlling spall generated by the penetration of a projectile comprising: a delaminating base layer comprised of at least three plies of a high tensile strength fabric bonded with a resinous adhesive to form the delaminating base layer, which upon impact by the projectile undergoes local shattering and a delaminating effect within a constrained area as the projectile penetrates through each fabric ply, thereby dissipating the projectile's force; a first continuous facing layer of martensite sheet steel adjacent the base layer, said first layer of martensite sheet steel having a minimum design tensil strength of at least 220,000 psi; a delaminating intermediate layer, comprised of at least three plies of a high tensile strength fabric, bonded with a resinous adhesive to form the delaminating intermediate layer, located adjacent the first layer of martensite sheet steel, the delaminating intermediate layer having fabric plies which recede in the direction of the penetrating projectile's path, and bend, elongating in tension to the point of separation, thereby further dissipating the projectile's force in a lateral direction, normal to the projectile's path; a second continuous facing layer of martensite sheet steel having a minimum design tensil strength of 220,000 psi, located adjacent the delaminating intermediate layer, the second steel layer recedes, bulging under the projectile's impact and framents the projectile, trapping the fragments within the bulge; an elongating outer layer, comprised of at least three plies of high tensile strength fabric, bonded with a resinous adhesive to form the elongating outer layer, located adjacent to the second layer of martensite sheet steel, the elongating outer layer having fabric plies which act in tension to absorb forces not contained by the second martensite sheet steel layer; each of the layers being bonded to adjacent layers with a plastic resinous adhesive, to form a rigid, laminated armor plate liner having a thickness of at least approximately 0.29".
Claim 2
Dependent Claim
314 words
A laminated spall liner for controlling spall generated by the penetration of a projectile comprising: a delaminating base layer comprised of at least three plies of a high tensile strength fabric bonded with a resinous adhesive to form the delaminating base layer, which upon impact by the projectile undergoes local shattering and a delaminating effect within a constrained area as the projectile penetrates through each fabric ply, thereby dissipating the projectile's force; a first continuous facing layer of martensite sheet steel adjacent the base layer, said first layer of martensite sheet steel having a minimum design tensil strength of at least 220,000 psi; a delaminating intermediate layer, comprised of at least three plies of a high tensile strength fabric, bonded with a resinous adhesive to form the delaminating intermediate layer, located adjacent the first layer of martensite sheet steel, the delaminating intermediate layer having fabric plies which recede in the direction of the penetrating projectile's path, and bend, elongating in tension to the point of separation, thereby further dissipating the projectile's force in a lateral direction, normal to the projectile's path; a second continuous facing layer of martensite sheet steel having a minimum design tensil strength of 220,000 psi, located adjacent the delaminating intermediate layer, the second steel layer recedes, bulging under the projectile's impact and framents the projectile, trapping the fragments within the bulge; an elongating outer layer, comprised of at least three plies of high tensile strength fabric, bonded with a resinous adhesive to form the elongating outer layer, located adjacent to the second layer of martensite sheet steel, the elongating outer layer having fabric plies which act in tension to absorb forces not contained by the second martensite sheet steel layer; each of the layers being bonded to adjacent layers with a plastic resinous adhesive, to form a rigid, laminated armor plate liner having a thickness of at least approximately 0.29".
Claim 3
Dependent Claim
17 words
The laminated ballistic spall liner of claim 1 wherein the high tensile strength fabric is ballistic nylon.
Claim 4
Dependent Claim
17 words
The laminated ballistic spall liner of claim 1 wherein the high tensile strength fabric is polyaramid fabric.
Claim 5
Dependent Claim
35 words
The laminated ballistic spall liner of claim 1 wherein at least one of the plies of high tensile strength, fabric is polyaramid fabric and the other plies of high tensile strength fabric are ballistic nylon.
Claim 6
Dependent Claim
206 words
A laminated spall liner for controlling spall generated by the penetration of a projectile, comprising: a delaminating top layer, comprised of at least four plies of a high tensile strength fabric bonded with a resinous adhesive to form the delaminating top layer, so that the individual plies of the top layer recede before the penetrating projectile, bend and break, causing a constrained delaminating effect within said delaminating top layer, thereby dissipating the projectile's force; a continuous facing layer of martensite sheet steel having a minimum design tensile strength of 220,000 psi, located adjacent the delaminating top layer, the layer of martensite sheet steel recedes, bulging under the projectile's impact and framents the projectile, trapping the fragments within the bulge; an elongating bottom layer, located adjacent the layer of martensite sheet steel, comprised of at least six plies of high tensil strength fabric, bonded with a resinous adhesive, to form the elongating bottom layer so that the plies of the elongating bottom layer act in tension to absorb forces not contained in the martensite sheet steel layer; each of the layers being bonded to adjacent layers with a plastic resinous adhesive, to form a rigid, laminated armor plate liner having a thickness of at least approximately 0.25".
Claim 7
Dependent Claim
206 words
A laminated spall liner for controlling spall generated by the penetration of a projectile, comprising: a delaminating top layer, comprised of at least four plies of a high tensile strength fabric bonded with a resinous adhesive to form the delaminating top layer, so that the individual plies of the top layer recede before the penetrating projectile, bend and break, causing a constrained delaminating effect within said delaminating top layer, thereby dissipating the projectile's force; a continuous facing layer of martensite sheet steel having a minimum design tensile strength of 220,000 psi, located adjacent the delaminating top layer, the layer of martensite sheet steel recedes, bulging under the projectile's impact and framents the projectile, trapping the fragments within the bulge; an elongating bottom layer, located adjacent the layer of martensite sheet steel, comprised of at least six plies of high tensil strength fabric, bonded with a resinous adhesive, to form the elongating bottom layer so that the plies of the elongating bottom layer act in tension to absorb forces not contained in the martensite sheet steel layer; each of the layers being bonded to adjacent layers with a plastic resinous adhesive, to form a rigid, laminated armor plate liner having a thickness of at least approximately 0.25".
Claim 8
Dependent Claim
17 words
The laminated ballistic spall liner of claim 5 wherein the high tensile strength fabric is ballistic nylon.
Claim 9
Dependent Claim
17 words
The laminated ballistic spall liner of claim 5 wherein the high tensile strength fabric is polyaramid fabric.
Claim 10
Dependent Claim
35 words
The laminated ballistic spall liner of claim 5 wherein at least one of the plies of high tensile strength fabric is polyaramid fabric and the other plies of high tensile strength, fabric are ballistic nylon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-11 | 1990-11-10 | 1991-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-11 | 1994-11-10 | 1995-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-11 | 1998-11-10 | 1999-05-12 | $7700.00 | Window Closed / Lapsed |