Deicing chemicals and their preparation from polysaccharide sources
Assignee: STATE OF SOUTH DAKOTA AS REPRESENTED BY DEPARTMENT OF TRANSPORTATION A CORP OF SD
•
Filing: 1984-09-28
•
Granted: 1987-05-12
•
Expires: 2004-09-28
Abstract
Abstract Deicing chemicals intended primarily for decing pavement such as roads, bridges, and runways are prepared from polysaccharide sources (e.g., waste products such as sawdust) by reaction at a pressure of less than 600 psi and a temperature less than 200° C. with a treating agent comprising alkali metal carbonates or bicarbonates or a mixture thereof and excess oxygen in the presence of water followed by the removal of oxalate and the treating agent. The reaction produces a liquid or a liquid/solid reaction product wherein the liquid contains the deicing chemical and the solid comprises a valuable pulp by-product. Calcium oxide or calcium hydroxide may be added to reduce the pressure resulting from the formation of large amounts of carbon dioxide during the reaction process and to aid in the removal of any oxalic acid formed during the reaction process. The deicing chemicals are impure mixtures of alkali metal salts of lower carboxylic acids substantially free of the alkali metal salt of oxalic acid, carbonic acid and of other organic compounds. The deicing chemicals are intended to be a substitute for the inorganic chloride salts (e.g, sodium chloride) commonly used for deicing highways.
Inventors
- 👤 Robert L. Sandvig
- 👤 William A. Klemm
- 👤 Jack R. Gaines
- 👤 Robert W. Looyenga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:13
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/18; C09K3/185
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
216 words
A deicer product of a process of producing a cellulosic pulp and a deicing composition, containing in part a mixture of alkali metal salts of lower carboxylic acids, which consists essentially of: (a) reacting a lignocellulosic biomass raw material with a treating agent comprising an alkali metal carbonate, bicarbonate or mixtures thereof at a ratio of 0.3 to 3 equivalents of the treating agent per 100 grams of raw materials under enriched oxygen conditions, 0.5 to 4.0 gram-moles of oxygen per each 100 grams of biomass, at a temperature of less than about 200° C., at a pressure less than about 600 p.s.i.g., and with suitable agitation producing a crude liquid/solid reaction product; (b) separating the reaction product into a liquid phase and a cellulosic phase; (c) separating from the liquid phase a substantial proportion of both the carbonate or bicarbonate treating agent and the oxylate; and (d) thereby obtaining from the liquid phase a deicer product which consists essentially of a mixture, substantially free of an alkali metal salt of oxalic acid and carbonic acid, of alkali metal salts of lower carboxylic acids including salts of glycolic acid, formic acid, acetic acid, maleic acid and at least a trace of alkali metal salts of lactic acid, fumeric acid, malic acid, malonic acid and tartaric acid.
Claim 2
Dependent Claim
216 words
A deicer product of a process of producing a cellulosic pulp and a deicing composition, containing in part a mixture of alkali metal salts of lower carboxylic acids, which consists essentially of: (a) reacting a lignocellulosic biomass raw material with a treating agent comprising an alkali metal carbonate, bicarbonate or mixtures thereof at a ratio of 0.3 to 3 equivalents of the treating agent per 100 grams of raw materials under enriched oxygen conditions, 0.5 to 4.0 gram-moles of oxygen per each 100 grams of biomass, at a temperature of less than about 200° C., at a pressure less than about 600 p.s.i.g., and with suitable agitation producing a crude liquid/solid reaction product; (b) separating the reaction product into a liquid phase and a cellulosic phase; (c) separating from the liquid phase a substantial proportion of both the carbonate or bicarbonate treating agent and the oxylate; and (d) thereby obtaining from the liquid phase a deicer product which consists essentially of a mixture, substantially free of an alkali metal salt of oxalic acid and carbonic acid, of alkali metal salts of lower carboxylic acids including salts of glycolic acid, formic acid, acetic acid, maleic acid and at least a trace of alkali metal salts of lactic acid, fumeric acid, malic acid, malonic acid and tartaric acid.
Claim 3
Dependent Claim
34 words
A deicing composition which comprises a mixture of rock salt and about 0.01 to 100 parts by weight of the deicing composition product of claim 1 per each part by weight of rock salt.
Claim 4
Dependent Claim
41 words
A deicer composition which comprises a mixture of a particulate and about 0.01 to 100 parts by weight of the deicing composition product of claim 1 per each part by weight of the particular comprising sand, gravel, cinders or mixtures thereof.
Claim 5
Dependent Claim
23 words
The deicer of claim 3 wherein the deicer additionally comprises about 0.01 to 100 parts of rock salt per part of the particulate.
Claim 6
Dependent Claim
23 words
The deicer of claim 3 wherein the deicer additionally comprises about 0.01 to 100 parts of calcium chloride per part of the particulate.
Claim 7
Independent Claim
79 words
A method of deicing surfaces which comprises contacting a surface bearing snow or ice with a deicing chemical consisting essentially of a mixture of alkali metal salts of lower carboxylic acids including formic acid, acetic acid, glycolic acid, maleic acid and at least a trace of alkali metal salts of fumaric acid, malic acid, malonic acid, tartaric acid, and lactic acid wherein the deicing chemical is substantially free of an alkali metal salt of oxalic acid and carbonic acid.
Claim 8
Independent Claim
79 words
A method of deicing surfaces which comprises contacting a surface bearing snow or ice with a deicing chemical consisting essentially of a mixture of alkali metal salts of lower carboxylic acids including formic acid, acetic acid, glycolic acid, maleic acid and at least a trace of alkali metal salts of fumaric acid, malic acid, malonic acid, tartaric acid, and lactic acid wherein the deicing chemical is substantially free of an alkali metal salt of oxalic acid and carbonic acid.
Claim 9
Dependent Claim
27 words
The method of claim 6 wherein the deicing chemical is in the form of a concentrated aqueous solution of the alkali metal salts of lower carboxylic acids.
Claim 10
Dependent Claim
48 words
The method of claim 6 wherein the deicing chemical is in the form of a liquid containing rock salt and on a dry basis, about 0.01 to 100 parts by weight of the alkali metal salts of lower carboxylic acids per each part by weight of rock salt.
Claim 11
Dependent Claim
258 words
A product of a process of producing a mixture of alkali metal salts of lower carboxylic acid useful as a deicing composition which consists essentially of the product of the steps: (a) presoaking a lignocellulosic raw material in an acidic, basic, or neutral pretreatment forming a pretreated lignocellulosic material; (b) mixing the pretreated lignocellulosic material with an oxalic acid precipitating compound and a treating agent comprising an alkali metal carbonate, alkali metal bicarbonate or mixtures thereof; (c) reacting the pretreated cellulosic material and the treating agent at a ratio of 0.3 to 3 parts of treating agent per 100 grams of raw material in oxygen enriched conditions, 0.5 to 4 gram-moles of oxygen per each 100 grams of lignocellulosic biomass at a pressure of less than 400 p.s.i.g. at a temperature of less than 200° C. in a closed system with suitable agitation to form a mixed liquid solid reaction product; (d) reducing the temperature of the reaction product after reaction is complete; (e) removing volatile gaseous by-products from the reaction mixture; (f) separating the reaction mixture into a liquid phase and a solid cellulosic phase; (g) removing the treating agent; and (h) thereby obtaining from the liquid phase a deicer product which consists essentially of a mixture of alkali metal salts of lower carboxylic acids including glycolic acid, formic acid, acetic acid, maleic acid and at least a trace of alkali metal salts of lactic acid, malic acid, malonic acid, and tartaric acid, and substantially free of an alkali metal salts of oxalic acid and carbonic acid.
Claim 12
Dependent Claim
258 words
A product of a process of producing a mixture of alkali metal salts of lower carboxylic acid useful as a deicing composition which consists essentially of the product of the steps: (a) presoaking a lignocellulosic raw material in an acidic, basic, or neutral pretreatment forming a pretreated lignocellulosic material; (b) mixing the pretreated lignocellulosic material with an oxalic acid precipitating compound and a treating agent comprising an alkali metal carbonate, alkali metal bicarbonate or mixtures thereof; (c) reacting the pretreated cellulosic material and the treating agent at a ratio of 0.3 to 3 parts of treating agent per 100 grams of raw material in oxygen enriched conditions, 0.5 to 4 gram-moles of oxygen per each 100 grams of lignocellulosic biomass at a pressure of less than 400 p.s.i.g. at a temperature of less than 200° C. in a closed system with suitable agitation to form a mixed liquid solid reaction product; (d) reducing the temperature of the reaction product after reaction is complete; (e) removing volatile gaseous by-products from the reaction mixture; (f) separating the reaction mixture into a liquid phase and a solid cellulosic phase; (g) removing the treating agent; and (h) thereby obtaining from the liquid phase a deicer product which consists essentially of a mixture of alkali metal salts of lower carboxylic acids including glycolic acid, formic acid, acetic acid, maleic acid and at least a trace of alkali metal salts of lactic acid, malic acid, malonic acid, and tartaric acid, and substantially free of an alkali metal salts of oxalic acid and carbonic acid.
References Cited (Backward Citations)
US2233185A
Cited
US2673148A
Cited
US2686120A
Cited
US2750414A
Cited
US3640768A
Cited
US3769152A
Cited
US3764464A
Cited
US3756956A
Cited
US4108669A
Cited
US4374743A
Cited
US4351669A
Cited
US4448702A
Cited
US4377488A
Cited
US4430240A
Cited
US4400285A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-11 | 1990-11-10 | 1991-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-11 | 1994-11-10 | 1995-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-11 | 1998-11-10 | 1999-05-12 | $7700.00 | Window Closed / Lapsed |