Sintered shrink-on cam and process of manufacturing such cam
Assignee: Miba Sintermetall GmbH
•
Filing: 1986-04-10
•
Granted: 1987-05-12
•
Expires: 2006-04-10
Abstract
Abstract Cams which meet all strength requirements and can be shrunk on a shaft can be made in a simple manner by sintering from a nickel- and copper-free mixture which comprises iron powder and contains 0.3 to 1.0 weight percent carbon and molybdenum and/or tungsten in such amounts that the sum of the molybdenums content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 0.5 and 3 weight percent.
Inventors
- 👤 Manfred Drozda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:26
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0264; F; F16; F16H; F16H53/00; F16H53/02; F16H53/025; B; B22; B22F; B22F3/00; B22F3/24; B22F2003/248; B22F2998/00; B22F2998/10; Y; Y10; Y10T; Y10T74/00; Y10T74/21; Y10T74/2101
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
86 words
In a sintered shrink-on cam, the improvement residing in that the cam consists of a sintered powder compact which is free of nickel and copper and contains iron, 0.3 to 1.0 weight percent carbon, and at least one alloying element selected from the group consisting of molybdenum and tungsten in such amounts that the sum of the molybdenum content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 0.5 and 3 weight percent.
Claim 2
Dependent Claim
86 words
In a sintered shrink-on cam, the improvement residing in that the cam consists of a sintered powder compact which is free of nickel and copper and contains iron, 0.3 to 1.0 weight percent carbon, and at least one alloying element selected from the group consisting of molybdenum and tungsten in such amounts that the sum of the molybdenum content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 0.5 and 3 weight percent.
Claim 3
Dependent Claim
62 words
The improvement set forth in claim 1, wherein said compact contains at least one alloying element selected from the group consisting of molybdenum and tungsten in such amounts that the sum of the molybdenum content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 1 to 1.5 weight percent.
Claim 4
Dependent Claim
218 words
In a process of manufacturing a sintered shrink-on cam by compacting a powder mixture which comprises iron and at least 0.3 weight percent carbon to form powder compacts and sintering said powder compacts, the improvement residing in that a powder mixture is provided which is free of nickel and copper and comprises iron and contains 0.3 to 1.0 weight percent carbon and at least one alloying element selected from the group consisting of molybdenum and tungsten in such amounts that the sum of the molybdenum content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 0.5 and 3 weight percent, said powder mixture is compacted to form powder compacts having an apparent specific gravity of at least 7.2 g/cm 3 , said compacts are heated to form temporarily a eutectic mixute including iron and at least one intermediate compound of the group consisting of molybdenum carbide and tungsten carbide and is heated above the eutectic point of said eutectic mixture to a sintering temperature which is below the solidus point of an adjacent system which consists of gamma iron with dissolved carbon and at least one alloying element of the group consisting of molybdenum and tungsten when said system is in the state of euilibrium.
Claim 5
Dependent Claim
218 words
In a process of manufacturing a sintered shrink-on cam by compacting a powder mixture which comprises iron and at least 0.3 weight percent carbon to form powder compacts and sintering said powder compacts, the improvement residing in that a powder mixture is provided which is free of nickel and copper and comprises iron and contains 0.3 to 1.0 weight percent carbon and at least one alloying element selected from the group consisting of molybdenum and tungsten in such amounts that the sum of the molybdenum content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 0.5 and 3 weight percent, said powder mixture is compacted to form powder compacts having an apparent specific gravity of at least 7.2 g/cm 3 , said compacts are heated to form temporarily a eutectic mixute including iron and at least one intermediate compound of the group consisting of molybdenum carbide and tungsten carbide and is heated above the eutectic point of said eutectic mixture to a sintering temperature which is below the solidus point of an adjacent system which consists of gamma iron with dissolved carbon and at least one alloying element of the group consisting of molybdenum and tungsten when said system is in the state of euilibrium.
Claim 6
Dependent Claim
63 words
The improvement set forth in claim 3, wherein said powder mixture contains at least one alloying element selected from the group consisting of molybdenum and tungsten in such amounts that the sum of the molybdenum content and the tungsten content multiplied with the ratio of the atomic weight of molybdenum to the atomic weight of tungsten lies between 1 to 1.5 weight percent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-11 | 1990-11-10 | 1991-05-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-11 | 1994-11-10 | 1995-05-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-11 | 1998-11-10 | 1999-05-12 | $7700.00 | Window Closed / Lapsed |