Higher molecular weight thermoplastics having multimodal molecular weight distribution
Assignee: Lyondell Chemical Technology LP
•
Filing: 1986-05-12
•
Granted: 1987-05-05
•
Expires: 2006-05-12
Abstract
Abstract Thermoplastic particles are suspended in water or other suspending fluids with a suspending aid(s) to prevent agglomeration of the beads, pellets or particles. To this suspension is added monomer(s) containing a multifunctional initiator(s). The monomer and initiator(s) are pre-emulsified in water or other fluid(s) before the addition in order to improve distribution of the monomer(s) and initiator(s) in or on the particles. After or during the addition(s), the suspension temperature is raised to cause polymerization. The procedures may be repeated to increase the coating or penetrated polymer content. New compositions of matter are made by this technique wherein the new compositions are plastic resins either coated or penetrated, or both, with a thermoplastic(s) of very high molecular weight not obtainable by present, commercial polymerization techniques. The compositions are superior to the feed resins because of the enhancement of physical properties brought about by the high molecular weights phase(s). This enhancement would be extended to foams made from these new resins.
Inventors
- 👤 Bernard H. Meyer
- 👤 Adolph V. DiGiulio
- 👤 Joseph C. Kinslow
- 👤 Dennis M. Hajnik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:46
CPC Classifications
C; C08; C08F; C08F257/00; C08F257/02
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
185 words
A method of improving the mechanical properties of thermoplastic polymers comprising: (a) suspending styrene polymer particles in a suitable suspension medium with the aid of a suitable suspending agent system; (b) forming an emulsion of monoethylenically unsaturated monomer or monomers capable of swelling said styrene polymer particles, a multi-functional peroxide having a 10-hour half-life temperature of 40° C. to 140° C., with or without a mono-functional peroxide having a 10-hour half-life temperature of 95° C. to 110° C.; (c) adding said emulsion to said suspension to allow the monomers and peroxides to be absorbed into the polymer particles; (d) heating said suspension to a temperature of 80°-135° C. and maintaining the suspension at said temperature for 0.10 to 6 hours to polymerize said monomers to a high molecular weight polymer or copolymer; (e) heating said suspension at a temperature of 115° C. to about 135° C. to substantially complete the polymerization of the monomers to form the final particles having a bimodal or multimodal molecular weight distribution; and (f) cooling the suspension to room temperature and separating the final polymer particles from the suspension medium.
Claim 2
Independent Claim
185 words
A method of improving the mechanical properties of thermoplastic polymers comprising: (a) suspending styrene polymer particles in a suitable suspension medium with the aid of a suitable suspending agent system; (b) forming an emulsion of monoethylenically unsaturated monomer or monomers capable of swelling said styrene polymer particles, a multi-functional peroxide having a 10-hour half-life temperature of 40° C. to 140° C., with or without a mono-functional peroxide having a 10-hour half-life temperature of 95° C. to 110° C.; (c) adding said emulsion to said suspension to allow the monomers and peroxides to be absorbed into the polymer particles; (d) heating said suspension to a temperature of 80°-135° C. and maintaining the suspension at said temperature for 0.10 to 6 hours to polymerize said monomers to a high molecular weight polymer or copolymer; (e) heating said suspension at a temperature of 115° C. to about 135° C. to substantially complete the polymerization of the monomers to form the final particles having a bimodal or multimodal molecular weight distribution; and (f) cooling the suspension to room temperature and separating the final polymer particles from the suspension medium.
Claim 3
Dependent Claim
56 words
The method of claim 1 wherein before step (e) said suspension may be cooled to 25°-75° C., and steps (b), (c), and (d) may be repeated as often as desired to effect multiple absorption of the monomers and catalysts to increase the percentage of high molecular weight polymer or copolymer in the final styrene polymer particles.
Claim 4
Dependent Claim
49 words
The method of claim 1 wherein said styrene polymer is selected from the group consisting of polymers of styrene monomers, copolymers of styrenic monomers and methylmethacrylate, maleic anhydride, and acrylonitrile, rubber-modified polymers of styrene monomers or copolymers, and blends of styrene polymers or copolymers and polyphenylene oxide or polycarbonates.
Claim 5
Dependent Claim
36 words
The method of claim 1 wherein said monomers capable of swelling said styrene polymer particles are selected from the group consisting of styrene monomers, alkylacrylate and methacrylates, unsaturated nitriles, acrylic acid, methacrylic acid, and mixtures thereof.
Claim 6
Dependent Claim
28 words
The method of claim 3 wherein said styrene monomers are selected from the group consisting of styrene, alpha-methylstyrene, nuclear methylstyrene, para-tertbutylstyrene, monochlorostyrene and dichlorostyrene and mixtures of these.
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein said suitable suspension medium is selected from the group consisting of water, glycerol, and mixtures thereof.
Claim 8
Dependent Claim
41 words
The method of claim 1 wherein said suitable suspending agent system is selected from the group consisting of a finely divided difficultly water-soluble inorganic phosphate alone or in combination with an anionic surfactant, polyvinyl alcohol, hydroxyethyl cellulose, polyvinylpyrrolidone, and mixtures thereof.
Claim 9
Independent Claim
184 words
A method of improving the mechanical properties of thermoplastic polymers comprising: (a) suspending styrene polymer particles in a suitable suspension medium with the aid of a suitable suspending agent system; (b) forming an emulsion of monoethylenically unsaturated monomer or monomers capable of swelling said styrene polymer particles, a multi-functional peroxide having a 10-hour half-life temperature of 40° C. to 140° C., with or without a mono-functional peroxide having a 10-hour half-life temperature of 95° C. to 110° C.; (c) adding said emulsion to said suspension to allow the monomers and peroxides to be absorbed into the polymer particles; (d) heating said suspension to a temperature of 80°-135° C. and maintaining the suspension at said temperature for 0.10 to 6 hours to polymerize said monomers to a high molecular weight polymer or copolymer; (e) cooling the suspension to room temperature and separating the polymer particles from the suspension medium; and (f) vacuum stripping said particles at a temperature 115° C. to about 135° C. to substantially complete the polymerization of the monomers to form the final particles having a bimodal or multimodal molecular weight distribution.
Claim 10
Independent Claim
184 words
A method of improving the mechanical properties of thermoplastic polymers comprising: (a) suspending styrene polymer particles in a suitable suspension medium with the aid of a suitable suspending agent system; (b) forming an emulsion of monoethylenically unsaturated monomer or monomers capable of swelling said styrene polymer particles, a multi-functional peroxide having a 10-hour half-life temperature of 40° C. to 140° C., with or without a mono-functional peroxide having a 10-hour half-life temperature of 95° C. to 110° C.; (c) adding said emulsion to said suspension to allow the monomers and peroxides to be absorbed into the polymer particles; (d) heating said suspension to a temperature of 80°-135° C. and maintaining the suspension at said temperature for 0.10 to 6 hours to polymerize said monomers to a high molecular weight polymer or copolymer; (e) cooling the suspension to room temperature and separating the polymer particles from the suspension medium; and (f) vacuum stripping said particles at a temperature 115° C. to about 135° C. to substantially complete the polymerization of the monomers to form the final particles having a bimodal or multimodal molecular weight distribution.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-04 | 1990-11-03 | 1991-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-04 | 1994-11-03 | 1995-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-04 | 1998-11-03 | 1999-05-05 | $7700.00 | Window Closed / Lapsed |