Process for crosslinking and extending conjugated diene-containing polymers
Assignee: National Aeronautics and Space Administration
•
Filing: 1986-03-11
•
Granted: 1987-04-28
•
Expires: 2006-03-11
Abstract
Abstract This invention relates to a process using a Diels-Alder reaction which increases the molecular weight and/or crosslinks polymers by reacting the polymers with bisunsaturated dienophiles. The polymer comprises at least 75% by weight based on the reaction product, has a molecular weight of at least 5000 and a plurality of conjugated 1,3-diene systems incorporated into the molecular structure. A dienophile reaction with the conjugated 1,3-diene of the polymer is at least 1% by weight based on the reaction product. Examples of the polymer include polyesters, polyamides, polyethers, polysulfones and copolymers thereof. The bisunsaturated dienophiles may include bis-maleimide, bisnadimides, bis maleic and bis tumaric esters and amides. The method of this invention for expanding the molecular weight chains of the polymers, preferably thermoplastics, is advantageous for processing or fabricating thermoplastics. A low molecular weight thermoplastic is converted to a high molecular weight plastic having improved strength and toughness for use in the completed end use article.
Inventors
- 👤 Vernon L. Bell
- 👤 Stephen J. Havens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 18:03
CPC Classifications
C; C08; C08G; C08G61/00; C08G63/00; C08G63/91; C08G65/00; C08G65/02; C08G65/32; C08G65/329; C08G75/00; C08G75/20
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
85 words
A process for improving the properties of a polymer using a Diels-Alder reaction which comprises reacting: (a) a polymer selected from the group consisting of polyesters, polyamides, polyethers, polysulfones and copolymers thereof having a plurality of conjugated 1,3-diene systems incorporated into the molecular structure of the polymers, said polymer having a molecular weight of at least 5000; and (b) at least 1% by weight based on the weight of the polymer of a bis-unsaturated dienophile which is reactive with the conjugated 1,3-dienes of the polymer.
Claim 2
Dependent Claim
85 words
A process for improving the properties of a polymer using a Diels-Alder reaction which comprises reacting: (a) a polymer selected from the group consisting of polyesters, polyamides, polyethers, polysulfones and copolymers thereof having a plurality of conjugated 1,3-diene systems incorporated into the molecular structure of the polymers, said polymer having a molecular weight of at least 5000; and (b) at least 1% by weight based on the weight of the polymer of a bis-unsaturated dienophile which is reactive with the conjugated 1,3-dienes of the polymer.
Claim 3
Dependent Claim
15 words
The process according to claim 1, wherein the molecular weight of the polymer is increased.
Claim 4
Dependent Claim
11 words
The process according to claim 1, wherein the polymer is crosslinked.
Claim 5
Dependent Claim
17 words
The process according to claim 1, wherein the molecular weight is increased and the polymer is crosslinked.
Claim 6
Dependent Claim
24 words
The process according to claim 1, wherein the dienophile is selected from the group consisting of bismaleimides, bis-nadimides, bis-maleic and bis-fumaric esters and amides.
Claim 7
Dependent Claim
51 words
The process according to claim 1, wherein the polyester is a copolyester containing about 50 percent of adipic acid ester groups and about 50 mole percent of trans,trans(t,t)-muconic acid ester groups synthesized by reacting equimolar quantities of diacid chlorides of adipic and t,t-muconic acid with two molar quantities of bisphenol A.
Claim 8
Dependent Claim
11 words
The process according to claim 1, wherein the dienophile is N,N'-bis-maleimido-4,4'-diphenylmethane.
Claim 9
Dependent Claim
34 words
The process according to claim 1, wherein the polyester is a copolyester comprising about 75 mole percent of adipic acid and 25 mole percent of t,t-muconic acid reacted by interfacial condensation with bisphenol A.
Claim 10
Dependent Claim
20 words
The process according to claim 7, wherein a quantity of N,N'-bis-maleimido-4,4'-diphenylmethane reacts with all conjugated diene groups in the polyester.
Claim 11
Dependent Claim
27 words
The process according to claim 9, which comprises forming a solution containing a copolyester having t-t,conjugated diene groups dissolved in 1,2-dichloroethane and adding to the solution N,N'-bismaleimido-4,4'-diphenylmethane.
Claim 12
Dependent Claim
25 words
The process according to claim 7, wherein a quantity of N,N'-bis-maleimido-4,4'-diphenylmethane reacts with at most about 27% of the conjugated diene groups in the polymer.
Claim 13
Dependent Claim
27 words
The process according to claim 11, wherein a polymer solution containing a copolymer having t,t-conjugated diene groups dissolved in toluene, 1,1,2,2,-tetrachloroethane and 1,2-dichloroethane is reacted with N,N'-bis-maleimido-4,4'-diphenylmethane.
Claim 14
Dependent Claim
23 words
The process according to claim 7, wherein a quantity of N,N'-bis-maleimido-4,4'-diphenylmethane reacts with about one-third of the conjugated diene groups in the polymer.
Claim 15
Dependent Claim
27 words
The process according to claim 13, which comprises reacting a copolymer poly (4,4'-isopropylidenediphenyl coadipate/t,t-mucanate (85/15)) solution having conjugated diene groups dissolved in toluene and 1,2-dichloroethane with N,N'-bis-maleimido-4,4'-diphenylmethane.
Claim 16
Dependent Claim
12 words
The process according to claim 1, wherein substantially no volatiles are released.
Claim 17
Dependent Claim
42 words
A low molecular weight aromatic polyester with an average molecular weight of about 10,000 and a degree of polymerization of about 48, produced according to the process of claim 1 by reacting 3,3'-methylenedibenzoyl dichloride with 4,4'-methylene diphenol in methylene chloride and triethylamine.
Claim 18
Dependent Claim
9 words
A product produced by the process of claim 1.
Claim 19
Dependent Claim
22 words
The process according to claim 1, wherein the weight ratio of the 1,3-diene containing polymer to dienophile ranges from 3.5 to 50.
Claim 20
Dependent Claim
98 words
A process using a Diels-Alder reaction which comprises reacting: (a) at least 1% by weight based on a reaction product of polymers having a molecular weight of at least 5000 and a plurality of conjugated 1,3-diene systems incorporated into the molecular structure, said polymer is selected from the group consisting of polyesters, polyamides, polyethers, polysulfones and copolymers thereof; and (b) at least 1% by weight based on the reaction product of a dienophile reactive with the conjugated 1,3-dienes of the polymer, said dienophile is selected from the group consisting of bismaleimide, bis-nadimides, bis-maleic and bis-tumaric esters and amides.
Claim 21
Dependent Claim
98 words
A process using a Diels-Alder reaction which comprises reacting: (a) at least 1% by weight based on a reaction product of polymers having a molecular weight of at least 5000 and a plurality of conjugated 1,3-diene systems incorporated into the molecular structure, said polymer is selected from the group consisting of polyesters, polyamides, polyethers, polysulfones and copolymers thereof; and (b) at least 1% by weight based on the reaction product of a dienophile reactive with the conjugated 1,3-dienes of the polymer, said dienophile is selected from the group consisting of bismaleimide, bis-nadimides, bis-maleic and bis-tumaric esters and amides.
Claim 22
Dependent Claim
15 words
The process according to claim 19, wherein the molecular weight of the polymer is increased.
Claim 23
Dependent Claim
11 words
The process according to claim 19, wherein the polymer is crosslinked.
Claim 24
Dependent Claim
17 words
The process according to claim 19, wherein the molecular weight is increased and the polymer is crosslinked.
References Cited (Backward Citations)
US3283032A
Cited
US3458460A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-27 | 1990-10-27 | 1991-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-27 | 1994-10-27 | 1995-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-27 | 1998-10-27 | 1999-04-28 | $7700.00 | Window Closed / Lapsed |