Compositions and methods for preparing an edible film of lower water vapor permeability
Assignee: General Mills Inc
•
Filing: 1985-06-03
•
Granted: 1987-04-28
•
Expires: 2005-06-03
Abstract
Abstract Disclosed are edible film coating compositions of low moisture permeability and their methods of preparation. The compositions comprise cross-linked, refined shellac and hydroxypropyl cellulose (HPC) in a weight ratio of 1:0.001 to 1:2. Highly preferred compositions additionally comprise mono- or di-carboxylic acid adducts such as adipic, succinic, lauric, or stearic acids in a weight ratio of acid to combined weight of shellac and cellulose of 1:33 to 1:10. In the preferred method of preparing, the shellac is cross-linked in a dry, molten mixture with the HPC by heating at 130° to 175° C. for 2 to 15 minutes. The coating compound while molten is dissolved in a food grade solvent, applied to a substrate, and dried. The coating compositions are particularly useful as a moisture barrier in composite food articles having phases in contact which differ substantially in water activity. Effective films range from 0.1 to 5 mils in thickness.
Inventors
- 👤 Jonathan Seaborne
- 👤 David C. Egberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 15:26
CPC Classifications
A; A23; A23G; A23G3/00; A23G3/34; A23G3/343; A23B; A23B4/00; A23B4/10; A23B7/00; A23B7/16; A23C; A23C19/00; A23C19/14; A23C19/16; A23C19/163; A23G9/00; A23G9/32; A23G9/322; A23P; A23P20/00; A23P20/10; A23P20/105; A23P20/19; C; C09; C09D; C09D101/00; C09D101/08; C09D101/26; C09D101/28; C09D101/284; A23G2200/00
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
168 words
A method for preparing an edible low water vapor permeable film, comprising the steps of: A. dissolving in an edible solvent to form a mixed solution 1. unbleached, refined edible shellac, and 2. a first reactant member selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose and mixtures thereof, wherein the weight ratio of edible shellac to member ranges from about 1:0.001 to 1:2, wherein the concentration of the solution ranges from about 1% to 30% by weight, wherein said solution additionally comprises an acid catalyst selected from the group consisting of citric, tartaric, hydrochloric, malic and mixtures thereof, and wherein the weight ratio of acid catalyst to the combined weight of shellac and hydroxypropyl cellulose ranges from about 0.001:1 to 0.1:1; B. applying the solution to a substrate to form a coated substrate; and C. heating the coated substrate at a temperature of about 130° to 175° C. for about 2 to 15 minutes whereby the solvent is evaporated to form a cured edible film.
Claim 2
Independent Claim
168 words
A method for preparing an edible low water vapor permeable film, comprising the steps of: A. dissolving in an edible solvent to form a mixed solution 1. unbleached, refined edible shellac, and 2. a first reactant member selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose and mixtures thereof, wherein the weight ratio of edible shellac to member ranges from about 1:0.001 to 1:2, wherein the concentration of the solution ranges from about 1% to 30% by weight, wherein said solution additionally comprises an acid catalyst selected from the group consisting of citric, tartaric, hydrochloric, malic and mixtures thereof, and wherein the weight ratio of acid catalyst to the combined weight of shellac and hydroxypropyl cellulose ranges from about 0.001:1 to 0.1:1; B. applying the solution to a substrate to form a coated substrate; and C. heating the coated substrate at a temperature of about 130° to 175° C. for about 2 to 15 minutes whereby the solvent is evaporated to form a cured edible film.
Claim 3
Dependent Claim
41 words
The method of claim 1 wherein the solution additionally comprises an edible non-substituted mono- or di-carboxylic organic acid, and wherein the weight ratio of organic acid to the combined weight of shellac and hydroxypropyl cellulose ranges from about 0.001:1 to 0.25:1.
Claim 4
Dependent Claim
22 words
The method of claim 2 wherein the weight ratio of the first reactant member to shellac ranges from about 0.05 to 0.1:1.
Claim 5
Dependent Claim
13 words
The method of claim 3 wherein the first reactant member is hydroxypropyl cellulose.
Claim 6
Dependent Claim
11 words
The method of claim 4 wherein the shellac is virgin shellac.
Claim 7
Dependent Claim
17 words
The method of claim 5 wherein the film ranges from about 1 to 5 mil in thickness.
Claim 8
Dependent Claim
50 words
The method of claim 6 wherein the organic acid is selected from the group consisting of adipic acid, succinic acid, oleic acid, lauric acid, stearic acid and mixtures thereof and in a weight ratio of second reactant to combined weight of shellac and hydroxypropyl cellulose of about 0.001 to 0.1:1.
Claim 9
Dependent Claim
68 words
An edible coating composition having a low water vapor permeability, comprising: a heat cured reaction product comprising A. unbleached, edible shellac, and B. a reactant member selected from the group consisting of hydroxypropyl cellulose and hydroxypropyl methyl cellulose and mixtures thereof, wherein the ratio of the reactant member and shellac ranges from 0.001 to 2:1, and wherein the product has an average molecular weight of at least 2,000.
Claim 10
Dependent Claim
68 words
An edible coating composition having a low water vapor permeability, comprising: a heat cured reaction product comprising A. unbleached, edible shellac, and B. a reactant member selected from the group consisting of hydroxypropyl cellulose and hydroxypropyl methyl cellulose and mixtures thereof, wherein the ratio of the reactant member and shellac ranges from 0.001 to 2:1, and wherein the product has an average molecular weight of at least 2,000.
Claim 11
Dependent Claim
60 words
The edible coating composition of claim 8, wherein the reaction product additionally comprises: C. a second reactant member comprising a nonsubstituted edible mono- or di-carboxylic organic acid and wherein the weight ratio of second reactant member to combined weight of shellac and first reactant ranges from about 0.0001 to 0.25:1 and wherein the shellac is refined and carbon black decolorized.
Claim 12
Dependent Claim
52 words
The edible coating composition of claim 9, additionally comprising: D. an acid catalyst member selected from the group consisting of citric, malic, hydrochloric, tartaric acids and mixtures thereof and wherein the weight ratio of acid catalyst member to the combined weight of shellac and first reactant ranges from about 1:10 to 400.
Claim 13
Dependent Claim
22 words
The edible coating composition of claim 10 wherein the shellac is virgin shellac, and wherein the first reactant member is hydroxypropyl cellulose.
Claim 14
Dependent Claim
42 words
The edible coating composition of claim 11, wherein the weight ratio of shellac to hydroxypropyl cellulose ranges from about 1:0.05 to 0.1, and wherein the second reactant member is selected from the group consisting of stearic, lauric, adipic acids and mixtures thereof.
Claim 15
Dependent Claim
82 words
An edible film having a low water vapor permeability, said film comprising: a heat cured reaction product comprising, A. unbleached, edible shellac, and B. a first reactant member selected from the group consisting of hydroxypropyl cellulose and hydroxypropyl methyl cellulose and mixtures thereof, wherein the ratio of first reactant member and shellac ranges from 0.001 to 2:1, and wherein the product has an average molecular weight of at least 2,000 and wherein the film ranges from 1 to 5 mil in thickness.
Claim 16
Dependent Claim
82 words
An edible film having a low water vapor permeability, said film comprising: a heat cured reaction product comprising, A. unbleached, edible shellac, and B. a first reactant member selected from the group consisting of hydroxypropyl cellulose and hydroxypropyl methyl cellulose and mixtures thereof, wherein the ratio of first reactant member and shellac ranges from 0.001 to 2:1, and wherein the product has an average molecular weight of at least 2,000 and wherein the film ranges from 1 to 5 mil in thickness.
Claim 17
Dependent Claim
57 words
The edible film of claim 13, wherein the product additionally comprises: C. a second reactant member comprising an edible non-substituted mono- or di-carboxylic organic acid, wherein the shellac is refined and carbon black decolorized, and wherein the weight ratio of second reactant member to combined weight of shellac and first reactant range from about 0.0001 to 0.25:1.
Claim 18
Dependent Claim
52 words
The edible film of claim 14, wherein the product additionally comprises: D. an acid catalyst selected from the group consisting of citric, malic, hydrochloric, tartaric acids and mixtures thereof and wherein the weight ratio of acid catalyst to the combined weight of shellac and first reactant ranges from about 1:10 to 400.
Claim 19
Dependent Claim
21 words
The edible film of claim 15 wherein the shellac is virgin shellac, and wherein the first reactant member is hydroxypropyl cellulose.
Claim 20
Dependent Claim
43 words
The edible film of claim 16 wherein the weight ratio of shellac to hydroxypropyl cellulose ranges from about 1:0.05 to 0.1, and wherein the second reactant member is selected from the group consisting of strearic, succinic, oleic, lauric, adipic acids and mixtures thereof.
Claim 21
Independent Claim
134 words
A method for preparing a heat sensitive substrate coated with an edible film of low moisture permeability comprising: A. heating in a dry state a mixture comprising: 1. unbleached edible shellac, 2. a first reactant member selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose and mixtures thereof, and wherein the weight ratio of shellac to member ranges from about 1:0.001 to 1:2, in a dry state to a temperature of about 130° to 175° C. for a period of about 2 to 15 minutes, to form a cross-linked reaction product coating composition; B. dissolving the coating composition while still molten in a food grade solvent with agitation to form a solution; C. applying the solution to a heat sensitive substrate to form a coated substrate; and D. drying the coated substrate.
Claim 22
Independent Claim
134 words
A method for preparing a heat sensitive substrate coated with an edible film of low moisture permeability comprising: A. heating in a dry state a mixture comprising: 1. unbleached edible shellac, 2. a first reactant member selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose and mixtures thereof, and wherein the weight ratio of shellac to member ranges from about 1:0.001 to 1:2, in a dry state to a temperature of about 130° to 175° C. for a period of about 2 to 15 minutes, to form a cross-linked reaction product coating composition; B. dissolving the coating composition while still molten in a food grade solvent with agitation to form a solution; C. applying the solution to a heat sensitive substrate to form a coated substrate; and D. drying the coated substrate.
Claim 23
Dependent Claim
16 words
The method of claim 18 wherein the solvent is ethanol and wherein the substrate is edible.
Claim 24
Dependent Claim
22 words
The method of claim 19 wherein the weight ratio of the first reactant member to shellac ranges from about 0.05 to 0.1:1.
Claim 25
Dependent Claim
13 words
The method of claim 20 wherein the first reactant member is hydroxypropyl cellulose.
Claim 26
Dependent Claim
11 words
The method of claim 21 wherein the shellac is virgin shellac.
Claim 27
Dependent Claim
17 words
The method of claim 22 wherein the film ranges from about 1 to 5 mil in thickness.
Claim 28
Dependent Claim
54 words
The method of claim 23 wherein the solution additionally comprises a second reactant member selected from the group consisting of adipic acid, succinic acid, oleic acid, lauric acid, stearic acid and mixtures thereof and in a weight ratio of second reactant to combined weight of shellac and hydroxypropyl cellulose of about 0.0001 to 0.25:1.
Claim 29
Dependent Claim
9 words
The product prepared by the method of claim 18.
Claim 30
Dependent Claim
9 words
The product prepared by the method of claim 19.
Claim 31
Dependent Claim
9 words
The product prepared by the method of claim 22.
Claim 32
Dependent Claim
9 words
The product prepared by the method of claim 24.
Claim 33
Dependent Claim
82 words
A coated food article comprising: A. a food substrate having a surface, B. a film overlaying said surface, said film comprising a heat cured thermo-plastic resin product comprising 1. refined, unbleached, edible shellac, and 2. a first reactant member selected from the group consisting of hydroxypropyl cellulose and hydroxypropyl methyl cellulose and mixtures thereof, wherein the ratio of first reactant member and shellac ranges from 0.001 to 2:1 and wherein the resin product has an average molecular weight of at least 2,000.
Claim 34
Dependent Claim
82 words
A coated food article comprising: A. a food substrate having a surface, B. a film overlaying said surface, said film comprising a heat cured thermo-plastic resin product comprising 1. refined, unbleached, edible shellac, and 2. a first reactant member selected from the group consisting of hydroxypropyl cellulose and hydroxypropyl methyl cellulose and mixtures thereof, wherein the ratio of first reactant member and shellac ranges from 0.001 to 2:1 and wherein the resin product has an average molecular weight of at least 2,000.
Claim 35
Dependent Claim
58 words
The article composition of claim 29, wherein the resin additionally comprises: 3. a second reactant member selected from the group consisting of adipic acid, succinic acid, oleic acid, lauric acid, strearic acid and mixtures thereof and wherein the weight ratio of second reactant member to combined weight of shellac and first reactant ranges from about 0.0001 to 0.25:1.
Claim 36
Dependent Claim
50 words
The article of claim 30 wherein the resin additionally comprises: 4. an acid catalyst selected from the group consisting of citric, malic, hydrochloric, tartaric acids and mixtures thereof and wherein the weight ratio of acid to the combined weight of shellac and first reactant ranges from about 1:10 to 400.
Claim 37
Dependent Claim
21 words
The article composition of claim 31 wherein the shellac is virgin shellac, and wherein the first reactant member is hydroxypropyl cellulose.
Claim 38
Dependent Claim
41 words
The article composition of claim 32 wherein the weight ratio of shellac to hydroxypropyl cellulose ranges from about 1:0.05 to 0.1, and wherein the second reactant member is selected from the group consisting of stearic, lauric, adipic acids and mixtures thereof.
Claim 39
Dependent Claim
17 words
The article of claim 33 wherein the film has a thickness of about 0.1 to 5 mil.
Claim 40
Dependent Claim
93 words
A composite food article, resistant to degradation by species migration food phases, comprising: A. a first food phase; B. a second food phase; said composite food article having a gradient between the first and second food phases; and C. an interjacent barrier phase comprising a film formed from an edible thermoplastic, heat cured resin, said resin comprising: 1. about 0.1% to 85% by weight of edible unbleached, refined shellac, 2. about 25% to 99.9% by weight of a member selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose and mixtures thereof.
Claim 41
Dependent Claim
93 words
A composite food article, resistant to degradation by species migration food phases, comprising: A. a first food phase; B. a second food phase; said composite food article having a gradient between the first and second food phases; and C. an interjacent barrier phase comprising a film formed from an edible thermoplastic, heat cured resin, said resin comprising: 1. about 0.1% to 85% by weight of edible unbleached, refined shellac, 2. about 25% to 99.9% by weight of a member selected from the group consisting of hydroxypropyl cellulose, hydroxypropyl methyl cellulose and mixtures thereof.
Claim 42
Dependent Claim
21 words
The article of claim 35 wherein the gradient is a moisture, acidity, flavor, soluble color, oxygen, oil concentration or protein concentration.
Claim 43
Dependent Claim
64 words
The article of claim 36 wherein the first food phase is selected from the group consisting of chocolate chips, muffins, pastry, cereal grains, candy, cookies, nuts, wafer pieces, waffles, pancakes, fruit and mixtures thereo, and wherein the second food phase is selected from the group consisting of, frostings, yogurt, ice cream, pudding, cheese, syrups, fruit glazes, fruit fillings, gels, meat emulsions and mixtures thereof.
References Cited (Backward Citations)
US2811453A
Cited
US2816061A
Cited
US2909434A
Cited
US2951763A
Cited
US3043747A
Cited
US3157518A
Cited
US3145111A
Cited
US3141778A
Cited
US3382078A
Cited
US3248232A
Cited
US3390049A
Cited
US3323922A
Cited
US3471303A
Cited
US3576663A
Cited
US3741795A
Cited
US3560222A
Cited
US4396633A
Cited
US4401681A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-27 | 1990-10-27 | 1991-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-27 | 1994-10-27 | 1995-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-27 | 1998-10-27 | 1999-04-28 | $7700.00 | Window Closed / Lapsed |