Information medium adapted to be written by thermo-optical means and method of manufacturing same
Assignee: Alcatel Thomson Gigadisc SA
•
Filing: 1985-08-02
•
Granted: 1987-04-21
•
Expires: 2005-08-02
Abstract
Abstract An information medium adapted to be written by thermo-optical means comprising a heat-sensitive structure adapted to store information to be read by optical means. This includes a thin metal layer, which, when incident writing radiation impinges on it, causes a transient localized temperature rise. Above a temperature threshold this causes a change in the optical characteristics of the heat-sensitive structure. The information medium is manufactured by a method involving depositing a continuous thin film of polycrystalline aggregate over an acceptor surface of the aforementioned structure by means of an incident flux of particles of a precious metal and a transition metal. In order to obtain a defined metallic composition, these metal particles are extracted from at least one target exposed to bombardment by other particles resulting from an electrical discharge in a rare gas at reduced pressure and confined by a magnetic field. The acceptor surface collects these metal particles with a residual energy content giving rise to a density of nucleation sites increased relative to that for a similar deposit obtained by vacuum evaporation. The maximum distance between the target and the acceptor surface is preferably not more than twenty centimeters, and advantageously not more than ten centimeters.
Inventors
- 👤 Alain Benhamou
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:36
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/20; C23C14/205; G; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/242; G11B7/243; Y; Y10; Y10S; Y10S428/00; Y10S428/913; Y10T; Y10T428/00; Y10T428/25; Y10T428/256; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31504; Y10T428/31678; Y10T428/31692
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
219 words
Metal layer for an information medium adapted to be written by thermo-optical means and comprising a heat-sensitive structure adapted to store information to be read by optical means and having a thermal recording metal layer with an overall thickness between 100 and 300 A which, when incident writing radiation impinges on it, causes a transient localize temperature rise which, above a temperature threshold, causes a change in the optical characteristics of said heat-sensitive structure, manufactured by a method wherein said thermal recording metal layer is formed by depositing a continuous thin film of polycrystalline aggregate over an acceptor surface of said structure by means of an incident influx of particles of a precious metal and a transition metal more readily oxidized then said precious metal, in which method, in order to obtain a defined metallic composition, said metal particles are extracted from target means exposed to bombardment by other particles resulting from an electrical discharge in a rare gas at reduced pressure and confined by a magnetic field, said acceptor surface collecting said metal particles with a residual energy content giving rise to a density of nucleation sites increased relative to that for a similar deposit obtained by vacuum evaporation; said target means having an exposed area of said precious metal and an exposed area of said transition metal.
Claim 2
Dependent Claim
219 words
Metal layer for an information medium adapted to be written by thermo-optical means and comprising a heat-sensitive structure adapted to store information to be read by optical means and having a thermal recording metal layer with an overall thickness between 100 and 300 A which, when incident writing radiation impinges on it, causes a transient localize temperature rise which, above a temperature threshold, causes a change in the optical characteristics of said heat-sensitive structure, manufactured by a method wherein said thermal recording metal layer is formed by depositing a continuous thin film of polycrystalline aggregate over an acceptor surface of said structure by means of an incident influx of particles of a precious metal and a transition metal more readily oxidized then said precious metal, in which method, in order to obtain a defined metallic composition, said metal particles are extracted from target means exposed to bombardment by other particles resulting from an electrical discharge in a rare gas at reduced pressure and confined by a magnetic field, said acceptor surface collecting said metal particles with a residual energy content giving rise to a density of nucleation sites increased relative to that for a similar deposit obtained by vacuum evaporation; said target means having an exposed area of said precious metal and an exposed area of said transition metal.
Claim 3
Dependent Claim
26 words
Metal layer according to claim 1, wherein the concentration by weight of said transition metal exceeds the limit of solubility by volume in said precious metal.
Claim 4
Dependent Claim
16 words
Metal layer according to claim 2, wherein the grain texture is varied by pre-writing heat treatment.
Claim 5
Dependent Claim
19 words
Metal layer according to claim 1, forming a polycrystalline aggregate having an average grain size not exceeding 70 Angstroms.
Claim 6
Dependent Claim
16 words
Metal layer according to claim 4, wherein said average grain size does not exceed 20 Angstroms.
Claim 7
Dependent Claim
24 words
Metal layer according to claim 1, wherein one of said transition and precious metals is in solid solution in the other of said metals.
Claim 8
Dependent Claim
18 words
Metal layer according to claim 6, wherein said precious metal is gold and said transition metal is chromium.
Claim 9
Dependent Claim
16 words
Metal layer according to claim 7, wherein the concentration by weight of gold is substantially 60%.
Claim 10
Dependent Claim
216 words
Method of manufacturing an information medium adapted to be written by thermo-optical means and comprising a heat-sensitive structure adapted to store information to be read by optical means and having a thermal recording metal layer with an overall thickness between 100 and 300 A which, when incident writing radiation impinges on it, causes a transient focalized temperature rise which, above a temperature threshold, causes a change in the optical characteristics of said heat-sensitive structure, said method comprising forming a thermal recording metal layer by depositing a continuous thin film of polycrystalline aggregate over an acceptor surface of said structure by means of an incident flux of particles of a precious metal and a transition metal more readily oxidized than said precious metal, in which method, in order to obtain a defined metallic composition, said metal particles are extracted from target means exposed to bombardment by other particles resulting from an electrical discharge in a rare gas at reduced pressure and confined by a magnetic field, said acceptor surface collecting said metal particles with a residual energy content giving rise to a density of nucleation sites increased relative to that for a similar deposit obtained by vacuum evacuation; said target means having an exposed area of said precious metal and an exposed area of said transition metal.
Claim 11
Dependent Claim
216 words
Method of manufacturing an information medium adapted to be written by thermo-optical means and comprising a heat-sensitive structure adapted to store information to be read by optical means and having a thermal recording metal layer with an overall thickness between 100 and 300 A which, when incident writing radiation impinges on it, causes a transient focalized temperature rise which, above a temperature threshold, causes a change in the optical characteristics of said heat-sensitive structure, said method comprising forming a thermal recording metal layer by depositing a continuous thin film of polycrystalline aggregate over an acceptor surface of said structure by means of an incident flux of particles of a precious metal and a transition metal more readily oxidized than said precious metal, in which method, in order to obtain a defined metallic composition, said metal particles are extracted from target means exposed to bombardment by other particles resulting from an electrical discharge in a rare gas at reduced pressure and confined by a magnetic field, said acceptor surface collecting said metal particles with a residual energy content giving rise to a density of nucleation sites increased relative to that for a similar deposit obtained by vacuum evacuation; said target means having an exposed area of said precious metal and an exposed area of said transition metal.
Claim 12
Dependent Claim
19 words
Method according to claim 9, wherein the maximum distance between said target and said acceptor surface is twenty centimeters.
Claim 13
Dependent Claim
19 words
Method according to claim 9, wherein the maximum distance between said target and said acceptor surface is ten centimeters.
Claim 14
Dependent Claim
12 words
Method according to claim 9, wherein said target functions as a cathode.
Claim 15
Dependent Claim
11 words
Method according to claim 9, wherein said transition metal is chromium.
Claim 16
Dependent Claim
11 words
Method according to claim 9, wherein said precious metal is gold.
Claim 17
Dependent Claim
11 words
Method according to claim 9, wherein said rare gas is argon.
Claim 18
Dependent Claim
14 words
Method according to claim 9, wherein said reduced pressure is substantially 3×10 -3 Torr.
Claim 19
Dependent Claim
39 words
Method according to claim 9, wherein said target means comprise A target fabricated from one of said metals; the surface of said target exposed to said bombardment being partially covered by elements fabricated from the other of said metals.
Claim 20
Dependent Claim
26 words
Method according to claim 17, wherein the exposed surface of said target is cylindrical and said magnetic field is parallel to the axis of said surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |