Thermal casting process for the preparation of anisotropic membranes and the resultant membrane
Assignee: SOANE DAVID S DR
•
Filing: 1985-07-10
•
Granted: 1987-04-21
•
Expires: 2005-07-10
Abstract
Abstract A method for providing anisotropic polymer membranes from a binary polymer/solvent solution using a thermal inversion process. A homogeneous binary solution is cast onto a support and cooled in such a way as to provide a differential in cooling rate across the thickness of the resulting membrane sheet. Isotropic or anisotropic structures of selected porosities can be produced, depending on the initial concentration of polymer in the selected solvent and on the extent of the differential in cooling rate. This differential results in a corresponding gradation in pore size. The method may be modified to provide a working skin by applying a rapid, high-temperature pulse to redissolve a predetermined thickness of the membrane at one of its faces and then freezing the entire structure.
Inventors
- 👤 Gerard T. M. Caneba
- 👤 David S. Soong
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:29
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0083; B01D67/0002; B01D67/0023; B01D67/003; B29; B29C; B29C67/00; B29C67/20; B29C67/202; C; C08; C08J; C08J9/00; C08J9/28; B01D2323/00; B01D2323/08; B01D2323/082; B01D2323/12; B01D2325/00; B01D2325/04; C08J2201/00; C08J2201/04; C08J2201/052
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
133 words
A method for making an anisotropic polymer membrane, comprising the steps of: providing a binary solution at an initial temperature having a predetermined concentration of a polymeric component dissolved in a solvent; casing said binary solution onto a substrate so that a predetermined shape is formed, said shape having a first face, an oppositely disposed second face, and an interior therebetween; and, reducing said initial temperature adjacent said first face at a first cooling rate, while reducing said initial temperature at said second face at a second cooling rate, said second cooling rate being slower than said first cooling rate, so that as said initial temperature at said first face is reduced, said interior develops a graded pore size distribution, with pores decreasing in size from said second face toward said first face.
Claim 2
Independent Claim
133 words
A method for making an anisotropic polymer membrane, comprising the steps of: providing a binary solution at an initial temperature having a predetermined concentration of a polymeric component dissolved in a solvent; casing said binary solution onto a substrate so that a predetermined shape is formed, said shape having a first face, an oppositely disposed second face, and an interior therebetween; and, reducing said initial temperature adjacent said first face at a first cooling rate, while reducing said initial temperature at said second face at a second cooling rate, said second cooling rate being slower than said first cooling rate, so that as said initial temperature at said first face is reduced, said interior develops a graded pore size distribution, with pores decreasing in size from said second face toward said first face.
Claim 3
Dependent Claim
15 words
The method of claim 1, wherein said polymeric component and said solvent are substantially polar.
Claim 4
Dependent Claim
25 words
The method of claim 2, wherein said initial temperature of said binary solution is selected so as to ensure substantial homogeneity prior to said casting.
Claim 5
Dependent Claim
44 words
The method of claim 3, wherein said polymeric component comprises a polymerized hydrocarbon compound containing at least one functional group selected from the group consisting of esters, amides, carboxylic acids, carboxylic acid salts, aldehydes, ketones, alcohols, halogen substituentss, nitro groups, cyano groups and amines.
Claim 6
Dependent Claim
21 words
The method of claim 4, wherein said polymeric component is selected from the group consisting of acrylates, polyamides and cellulose esters.
Claim 7
Dependent Claim
21 words
The method of claim 5, wherein said polymeric component is selected from the group consisting of polymethylmethacrylate, nylon and cellulose triacetate.
Claim 8
Dependent Claim
11 words
The method of claim 1, wherein said solvent is substantially viscous.
Claim 9
Dependent Claim
20 words
The method of claim 7, wherein said solvent has a viscosity ranging from about 5 centipoise to about 15 centipoise.
Claim 10
Dependent Claim
21 words
The method of claim 8, wherein said solvent is selected from the group consisting of 1,1-tetrahydrothiophene dioxide, glycerol, dimethylsulfoxide, and n-methyl-2-pyrrolidone.
Claim 11
Dependent Claim
30 words
The method of claim 1, wherein said concentration of said polymeric component in said binary solution is selected so that substantial structural integrity and a predetermined pore size are provided.
Claim 12
Dependent Claim
21 words
The method of claim 10, wherein said concentration ranges from about ten percent by weight to about twenty percent by weight.
Claim 13
Dependent Claim
14 words
The method of claim 11, wherein said concentration is about ten percent by weight.
Claim 14
Independent Claim
145 words
A method for making a skinned polymer membrane, said membrane being either isotropic or anisotropic, comprising the steps of: providing a binary solution having a predetermined concentration of a polymeric component dissolved in a solvent; casting asid binary solution onto a substrate so that a predetermined shape is provided having a first face, an oppositely disposed second face, and an interior therebetween; reducing said initial temperature adjacent said first face at a first cooling rate, while reducing said initial temperature adjacent said second face at a second cooling rate, said first and second cooling rates being determined by the desired degree of an anisotropy and porosity; dissolving a predetermined thickness of said interior adjacent said first face of said symmetric membrane; reducing the temperature at said first face, whereby said dissolved thickness of said interior coagulates to form a relatively nonporous skin on said membrane.
Claim 15
Independent Claim
145 words
A method for making a skinned polymer membrane, said membrane being either isotropic or anisotropic, comprising the steps of: providing a binary solution having a predetermined concentration of a polymeric component dissolved in a solvent; casting asid binary solution onto a substrate so that a predetermined shape is provided having a first face, an oppositely disposed second face, and an interior therebetween; reducing said initial temperature adjacent said first face at a first cooling rate, while reducing said initial temperature adjacent said second face at a second cooling rate, said first and second cooling rates being determined by the desired degree of an anisotropy and porosity; dissolving a predetermined thickness of said interior adjacent said first face of said symmetric membrane; reducing the temperature at said first face, whereby said dissolved thickness of said interior coagulates to form a relatively nonporous skin on said membrane.
Claim 16
Dependent Claim
23 words
The method of claim 13, wherein said dissolving of said predetermined thickness comprises application of a rapid, high-temperature pulse to said first face.
Claim 17
Dependent Claim
19 words
The method of claim 14, wherein said concentration ranges from about 4 wt. % to about 20 wt. %.
Claim 18
Dependent Claim
11 words
An anisotropic polymeric membrane prepared by the method of claim 1.
Claim 19
Dependent Claim
11 words
A skinned polymer membrane prepared by the method of claim 13.
References Cited (Backward Citations)
US3945926A
Cited
US4035459A
Cited
US4247498A
Cited
US4264447A
Cited
US4387024A
Cited
US4333972A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |