Process for manufacturing optical disks by pressing
Assignee: CENTRE MONDIAL INFORMATIQUE ET RESSOURCE HUMAINE
•
Filing: 1984-07-02
•
Granted: 1987-04-21
•
Expires: 2004-07-02
Abstract
Abstract The invention provides a process for manufacturing optical disks by pressing and disks obtained by such a process, for improving the inherent flatness of the optical disk of the thick type, obtained by a process of pressing between a recorded master and another master, recorded or not depending on whether it is a question of a single or double side disk, this latter being formed from a stack of at least two thin sheets of thermoformable material subjected to a pressure-temperature cycle after which bonding together of the sheets and duplication of the information from the masters for information recording are obtained.
Inventors
- 👤 Jean-Pierre Lacotte
- 👤 Sylvain Kretschmer
- 👤 Pierre Oprandi
- 👤 Georges Broussaud
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 18:16
CPC Classifications
G; G11; G11B; G11B23/00; G11B23/0057; B; B29; B29C; B29C43/00; B29C43/02; B29C43/021; B29C43/20; B29C43/203; B29D; B29D17/00; B29D17/005; G11B7/00; G11B7/24; G11B7/26; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1039; Y10T156/1041; Y10T156/1043; Y10T156/1044
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
195 words
A process for manufacturing optical disks wherein reading of the disks may be carried out by transmission or reflection, said disks having given thickness greater than 300 micrometers and being recorded on at least one face by means of a compression press comprising a pair of jaws movable with respect to each other, each supporting respectively a first recorded master and a second master, countermaster or recorded master, said process comprising a step of positioning, between the masters, a stack of at least two sheets of identical thermoformable material closely placed in touch with each other whose total cumulated thickness is equal to said given thickness and the steps of subjecting this stack to a pressure-temperature cycle, said pressure being exerted by bringing the jaws of the press together for compressing the stack of thermoformable sheets and the temperature cycle comprising raising the temperature from ambient temperature so as to exceed the softening point of the material and returning to ambient temperature; so as to obtain, after these steps, bonding together of the sheets forming said stack and duplication of the recording on each recorded master on one of the main faces of the stack.
Claim 2
Dependent Claim
195 words
A process for manufacturing optical disks wherein reading of the disks may be carried out by transmission or reflection, said disks having given thickness greater than 300 micrometers and being recorded on at least one face by means of a compression press comprising a pair of jaws movable with respect to each other, each supporting respectively a first recorded master and a second master, countermaster or recorded master, said process comprising a step of positioning, between the masters, a stack of at least two sheets of identical thermoformable material closely placed in touch with each other whose total cumulated thickness is equal to said given thickness and the steps of subjecting this stack to a pressure-temperature cycle, said pressure being exerted by bringing the jaws of the press together for compressing the stack of thermoformable sheets and the temperature cycle comprising raising the temperature from ambient temperature so as to exceed the softening point of the material and returning to ambient temperature; so as to obtain, after these steps, bonding together of the sheets forming said stack and duplication of the recording on each recorded master on one of the main faces of the stack.
Claim 3
Dependent Claim
32 words
The process as claimed in claim 1, wherein said bonding and said duplicating of the recording are obtained simultaneously during raising of the temperature of the thermoformable material beyond said softening point.
Claim 4
Dependent Claim
73 words
The process as claimed in any one of claims 1 or 2, comprising an additional initial step during which each sheet of the stack is subjected to a pressure-temperature cycle between two smooth masters during which the temperature is raised from the ambient temperature to a temperature higher than the softening point of the thermoformable material forming it and brought back to the ambient temperature so as to improve the inherent flatness thereof.
Claim 5
Dependent Claim
75 words
The process as claimed in claim 1, further comprising an initial additional step during which the complete stack of the sheet of thermoformable material is subjected to a pressure-temperature cycle between two smooth masters during which the temperature is raised from the ambient temperature to a temperature greater than the softening point of the thermoformable material and brought back to ambient temperature, bonding together of the sheets of the stack being achieved after this step.
Claim 6
Dependent Claim
19 words
The process as claimed in claim 1 wherein each sheet of thermoformable material has a thickness of 150 micrometers.
Claim 7
Dependent Claim
54 words
The process as claimed in claim 1 wherein each sheet of thermoformable material is formed by a disk pre-form having a diameter greater than that of the optical disk to be produced and comprising a centering orifice pre cut-out for aligning the pre-forms with respect to each other so as to form said stack.
Claim 8
Dependent Claim
14 words
The process as claimed in claim 1 wherein said thermoformable material is polyvinyl chloride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |