Process for producing an electrolyte retaining matrix of electrical insulating long fibers
Assignee: Hitachi Ltd
•
Filing: 1986-04-23
•
Granted: 1987-04-14
•
Expires: 2006-04-23
Abstract
Abstract A fuel cell provided with an electrolyte retaining plate made of electrical insulating long fibers such as lithium aluminate long fibers which have preferably a length of 100 to 400 mu m and a diameter of 1 to 4 mu m, are interlocked each other and have vacant spaces for filling an electrolyte can be constructed and operated safely without damaging the electrolyte retaining plate for a long period of time.
Inventors
- 👤 Hideo Okada
- 👤 Masato Takeuchi
- 👤 Sigeru Okabe
- 👤 Hiroshi Tobita
- 👤 Shimpei Matsuda
- 👤 Kohki Tamura
- 👤 Fumito Nakajima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:57
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/14; H01M8/141; H01M8/142; H01M8/02; H01M8/0289; H01M2008/147; H01M2300/00; H01M2300/0017; H01M2300/0048; H01M2300/0051; H01M8/0293; H01M8/0295; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108; Y10T29/49115
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
77 words
A process for producing an electrolyte retaining matrix which comprises: contacting a self-supporting alumina felt or plate, made of alumina long fibers that have been interlocked with each other, with a lithium salt; heating the alumina felt or plate in contact with the lithium salt to form a lithium aluminate matrix by the reaction of alumina with the lithium salt; and impregnating the lithium aluminate matrix with an alkali carbonate electrolyte to fill spaces in the matrix.
Claim 2
Dependent Claim
77 words
A process for producing an electrolyte retaining matrix which comprises: contacting a self-supporting alumina felt or plate, made of alumina long fibers that have been interlocked with each other, with a lithium salt; heating the alumina felt or plate in contact with the lithium salt to form a lithium aluminate matrix by the reaction of alumina with the lithium salt; and impregnating the lithium aluminate matrix with an alkali carbonate electrolyte to fill spaces in the matrix.
Claim 3
Dependent Claim
29 words
A process according to claim 1, wherein the alumina long fibers have sufficient length to provide the interlocking of the long fibers to enable the matrix to be self-supporting.
Claim 4
Dependent Claim
59 words
A process according to claim 1, wherein the lithium salt is dusted on the alumina felt or plate to contact the felt or plate with the salt, and wherein the heating is performed at a temperature of at least the melting point of the lithium salt in contact with the alumina long fibers of the alumina felt or plate.
Claim 5
Dependent Claim
17 words
A process according to claim 1, wherein the heating is performed at a temperature of 400°-750° C.
Claim 6
Dependent Claim
34 words
A process according to claim 1, wherein said alumina felt or plate has been obtained by subjecting the interlocked alumina long fibers to sintering to enhance the mechanical strength of the felt or plate.
Claim 7
Dependent Claim
20 words
A process according to claim 5, wherein said sintering is performed at a temperature in the range of 800°-1600° C.
Claim 8
Dependent Claim
44 words
A process according to claim 1, wherein the lithium aluminate long fibers formed by the reaction of alumina with the lithium salt have a length of 100 μm or more and a ratio of length (l) to diameter (d), l/d, of 10 or more.
Claim 9
Dependent Claim
64 words
A process for producing an electrolyte retaining matrix which comprises: interlocking long fibers of electrical insulating material so as to form a matrix of interlocked insulating long fibers; and subjecting the interlocked insulating long fibers to sintering so as to enhance the mechanical strength of the matrix, the sintered matrix having vacant spaces for filling with an electrolyte, whereby the matrix formed is self-supporting.
Claim 10
Dependent Claim
64 words
A process for producing an electrolyte retaining matrix which comprises: interlocking long fibers of electrical insulating material so as to form a matrix of interlocked insulating long fibers; and subjecting the interlocked insulating long fibers to sintering so as to enhance the mechanical strength of the matrix, the sintered matrix having vacant spaces for filling with an electrolyte, whereby the matrix formed is self-supporting.
Claim 11
Dependent Claim
13 words
A process according to claim 8, wherein said insulating material is lithium aluminate.
Claim 12
Dependent Claim
19 words
A process according to claim 9, wherein said sintering is performed at a temperature between 800° and 1600° C.
Claim 13
Dependent Claim
30 words
A process according to claim 8, comprising the further step of impregnating the interlocked insulating long fibers with a molten electrolyte so as to fill vacant spaces in the matrix.
Claim 14
Dependent Claim
25 words
A process according to claim 11, wherein the further step of impregnating is performed after the interlocked insulating long fibers have been subjected to sintering.
Claim 15
Dependent Claim
15 words
A process according to claim 11, wherein said molten electrolyte is a molten carbonate electrolyte.
Claim 16
Dependent Claim
13 words
A process according to claim 13, wherein said insulating material is lithium aluminate.
References Cited (Backward Citations)
US3481737A
Cited
US3878296A
Cited
US4115632A
Cited
JPS5682583A
Cited
US4389467A
Cited
US4493879A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-13 | 1990-10-13 | 1991-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-13 | 1994-10-13 | 1995-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-13 | 1998-10-13 | 1999-04-14 | $7700.00 | Window Closed / Lapsed |