US4656206A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermoplastic polymer compositions
Assignee: Bip Chemicals Ltd
•
Filing: 1985-12-16
•
Granted: 1987-04-07
•
Expires: 2005-12-16
Abstract
Abstract A pigmented thermoplastic polymer masterbatch composition comprises a polyester of melting point above 200° C. based on polyethylene terephthalate, a second polymer to plasticize the polyester, and pigment in an amount of at least 20 parts per 100 parts of composition. The second polymer can be also a toughening agent for the PET and can be a polycarprolactone, or a copolymer of ethylene with acrylic acid or vinyl acetate.
Inventors
- 👤 Moira A. Carter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 15:02
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/22; C08J3/226; C08J2367/00; C08J2367/02
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
80 words
A pigmented thermoplastic polymer masterbatch composition comprising a polyester having a melting point above 200° C. based on polyethylene terephthalate repeating units, a second solid polymer capable of plasticising sand polyester and having a melting point in the range of 50° C. to 120° C., and at least 20 parts by weight of pigment per hundred parts by weight of composition, the amount of said second polymer being sufficient to facilitate wetting out of the pigment in the polymer composition.
Claim 2
Dependent Claim
80 words
A pigmented thermoplastic polymer masterbatch composition comprising a polyester having a melting point above 200° C. based on polyethylene terephthalate repeating units, a second solid polymer capable of plasticising sand polyester and having a melting point in the range of 50° C. to 120° C., and at least 20 parts by weight of pigment per hundred parts by weight of composition, the amount of said second polymer being sufficient to facilitate wetting out of the pigment in the polymer composition.
Claim 3
Dependent Claim
22 words
A composition according to claim 1 in which the second polymer has a toughening effect when compounded in minor proportions with PET.
Claim 4
Dependent Claim
14 words
A composition according to claim 1, in which the second polymer is a polycaprolactone.
Claim 5
Dependent Claim
20 words
A composition according to claim 3 in which the polycaprolactone has a molecular weight in the range 20,500 to 100,000.
Claim 6
Dependent Claim
22 words
A composition according to claim 1, in which the second polymer is a copolymer of ethylene with acrylic acid or vinyl acetate.
Claim 7
Dependent Claim
32 words
A composition according to claim 1 in which the amount of said second polymer is in the range 2 to 20 parts by weight per 100 parts by weight of total polymer.
Claim 8
Dependent Claim
20 words
A composition according to claim 1 in which the amount of pigment is in the range 30 to 60 p.b.w.
Claim 9
Dependent Claim
33 words
A method for pigmenting a moulding composition comprising a polyester based on polyethylene terephthalate repeating units, which comprises dry blending said moulding composition with a pigmented masterbatch composition as claimed in claim 1.
Claim 10
Dependent Claim
89 words
A pigmented thermoplastic polymer masterbatch composition comprising a polyester of melting point above 200° C. consisting essentially of polyethylene terephthalate, a second solid polymer having a melting point in the range of 50° C. to 120° C. which has a toughening effect on polyethylene terephthalate when compounded in minor proportions therewith and a pigment in an amount of at least 20 parts by weight per 100 parts by weight of total polymer in the composition and being sufficient to facilitate wetting out of the pigment in the polymer composition.
Claim 11
Dependent Claim
89 words
A pigmented thermoplastic polymer masterbatch composition comprising a polyester of melting point above 200° C. consisting essentially of polyethylene terephthalate, a second solid polymer having a melting point in the range of 50° C. to 120° C. which has a toughening effect on polyethylene terephthalate when compounded in minor proportions therewith and a pigment in an amount of at least 20 parts by weight per 100 parts by weight of total polymer in the composition and being sufficient to facilitate wetting out of the pigment in the polymer composition.
Claim 12
Dependent Claim
59 words
A pigmented thermoplastic polymer masterbatch composition according to claim 9 in which the second polymer is selected from the group consisting of polycaprolactone, and copolymers of ethylene with acrylic acid or vinyl acetate, and the amount of pigment in the composition is in the range of 30 to 60 parts by weight per hundred parts by weight of composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-06 | 1990-10-06 | 1991-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-06 | 1994-10-06 | 1995-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-06 | 1998-10-06 | 1999-04-07 | $7700.00 | Window Closed / Lapsed |