Plasma gas discharge treatment for improving the biocompatibility of biomaterials
Assignee: Washington Research Foundation
•
Filing: 1985-03-11
•
Granted: 1987-04-07
•
Expires: 2005-03-11
Abstract
Abstract A method of treating articles to improve their biocompatibility is disclosed. A substrate material is positioned within a reactor vessel and exposed to plasma gas discharge in the presence of an atmosphere of an inert gas and then in the presence of an organic gas, such as a halocarbon or halohydrocarbon gas, capable of forming a thin, biocompatible surface covalently bonded to the surface of the substrate. The method is particularly useful in the treatment of vascular graft materials to improve their biocompatibility.
Inventors
- 👤 Allan S. Hoffman
- 👤 Andrew Garfinkle
- 👤 Buddy D. Ratner
- 👤 Stephen R. Hanson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:28
CPC Classifications
B; B05; B05D; B05D1/00; B05D1/62; A; A61; A61F; A61F2/00; A61F2/02; A61F2/04; A61F2/06; A61L; A61L27/00; A61L27/50; A61L27/507; A61L33/00; A61L33/0076; A61L33/0088; A61L33/0094; B05D3/00; B05D3/14; B05D3/141; B05D3/142; C; C08; C08L; C08L27/00; C08L27/02; C08L27/12; Y; Y10; Y10S; Y10S128/00; Y10S128/22; Y10T; Y10T428/00; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T442/00; Y10T442/20; Y10T442/2525
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
108 words
A method of making a vascular prosthesis from a polymeric substrate material whose surface exposed to blood is treated to render it both thrombi- and emboli-resistant over extended periods of time, comprising: exposing the surface of the substrate material to be exposed to blood to plasma gas discharge in the presence of a fluorinated hydrocarbon gas, whereby deposition occurs on said material, in the presence of the plasma gas discharge, forming a thin, covalently bound deposition on the surface of the material of a fluorocarbon polymer with short chain-length fluorocarbon polymer side or end groups without otherwise changing the mechanical behavior of the material or its surface texture.
Claim 2
Independent Claim
108 words
A method of making a vascular prosthesis from a polymeric substrate material whose surface exposed to blood is treated to render it both thrombi- and emboli-resistant over extended periods of time, comprising: exposing the surface of the substrate material to be exposed to blood to plasma gas discharge in the presence of a fluorinated hydrocarbon gas, whereby deposition occurs on said material, in the presence of the plasma gas discharge, forming a thin, covalently bound deposition on the surface of the material of a fluorocarbon polymer with short chain-length fluorocarbon polymer side or end groups without otherwise changing the mechanical behavior of the material or its surface texture.
Claim 3
Dependent Claim
45 words
The method according to claim 1, wherein said fluorinated hydrocarbon gas is present at a pressure of 0.10-1.0 torr, and said substrate and gas atmosphere are subjected to glow discharge energy ranging from 5-100 watts for a time ranging from 5 minutes to 1 hour.
Claim 4
Dependent Claim
13 words
The method according to claim 1, wherein the fluorinated hydrocarbon gas is tetrafluoroethylene.
Claim 5
Independent Claim
84 words
A method of making a vascular prothesis from a polymeric substrate whose surface is treated to render it both thrombi- and emboli-resistant over extended peiods of time, said treatment comprising: exposing the material to plasma gas discharge in the presence of a fluorinated hydrocarbon gas; discontinuing the plasma gas discharge; and allowing the material to remain in the atmosphere of the halocarbon gas, whereby deposition of a fluorocarbon polymer with short chain-length fluorocarbon polymer side or end groups on said plasma exposed surfaes results.
Claim 6
Independent Claim
84 words
A method of making a vascular prothesis from a polymeric substrate whose surface is treated to render it both thrombi- and emboli-resistant over extended peiods of time, said treatment comprising: exposing the material to plasma gas discharge in the presence of a fluorinated hydrocarbon gas; discontinuing the plasma gas discharge; and allowing the material to remain in the atmosphere of the halocarbon gas, whereby deposition of a fluorocarbon polymer with short chain-length fluorocarbon polymer side or end groups on said plasma exposed surfaes results.
Claim 7
Dependent Claim
14 words
The method of claim 4 wherein the vascular prosthesis material is woven polyethylene terephthalate.
Claim 8
Dependent Claim
21 words
The method of claim 4 wherein the vascular prosthesis material is a porous fluorohydrocarbon and the fluorinated hydrocarbon gas is tetrafluoroethylene.
Claim 9
Dependent Claim
12 words
The method of claim 4 wherein the fluorinated hydrocarbon gas is tetrafluoroethylene.
Claim 10
Dependent Claim
69 words
A surface modified vascular graft material whose treated surface, when exposed to blood, is both thrombi- and emboli-resistant over extended periods of time, comprising: a fabric of polyethylene terephthalate material having a thin, covalently bonded coating on the surface thereof composed principally of a fluorocarbon polymer with short chain-length fluorocarbon side or end groups resulting from an electric glow discharge polymerization process conducted in a fluorinated hydrocarbon gaseous atmosphere.
Claim 11
Dependent Claim
69 words
A surface modified vascular graft material whose treated surface, when exposed to blood, is both thrombi- and emboli-resistant over extended periods of time, comprising: a fabric of polyethylene terephthalate material having a thin, covalently bonded coating on the surface thereof composed principally of a fluorocarbon polymer with short chain-length fluorocarbon side or end groups resulting from an electric glow discharge polymerization process conducted in a fluorinated hydrocarbon gaseous atmosphere.
Claim 12
Independent Claim
79 words
A method of making surface modified articles of a polymeric substrate material whose modified surface, when exposed to blood, is both thrombi- and emboli-resistant over extended periods of time, comprising: exposing the surface of the substrate material to plasma gas discharge in the presence of at least one fluorinated hydrocarbon gas, forming a thin, covalently bonded coating on the substrate material consisting of fluorocarbon polymer with side or end groups of less than three carbon atoms in chain length.
Claim 13
Independent Claim
79 words
A method of making surface modified articles of a polymeric substrate material whose modified surface, when exposed to blood, is both thrombi- and emboli-resistant over extended periods of time, comprising: exposing the surface of the substrate material to plasma gas discharge in the presence of at least one fluorinated hydrocarbon gas, forming a thin, covalently bonded coating on the substrate material consisting of fluorocarbon polymer with side or end groups of less than three carbon atoms in chain length.
Claim 14
Dependent Claim
10 words
A biomedical article made by the method of claim 9.
Claim 15
Dependent Claim
22 words
The method of claim 9, including cleaning and drying the substrate material under vacuum prior to exposure to the plasma gas discharge.
Claim 16
Dependent Claim
26 words
The method of claim 9, wherein the plasma gas discharge is generated by applying high radio frequency energy to a substrate contained in a reactor vessel.
Claim 17
Dependent Claim
33 words
The process of claim 12 wherein the high radio frequency energy applied ranges from 5-50 watts and wherein the presence of the gas within the reactor vessel ranges from 0.10 to 1.0 torr.
Claim 18
Independent Claim
158 words
A method of making surface modified substrate materials whose modified surface, when exposed to blood, is both thrombi- and emboli-resistant over extended periods of time, comprising: exposing the substrate material to plasma gas discharge in the presence of an inert gas for a period of time sufficient to etch and activate the surface of the substrate; and exposing the substrate material to plasma gas discharge in the presence of a fluorinated hydrocarbon gas, whereby chemical deposition in the presence of the plasma discharge results in a fluorocarbon polymer with short chain-length fluorocarbon polymer side or end groups deposited on the substrate as a thin, covalently bound deposition, the plasma discharge causing ionization of the gas molecules, partial reaction of the ionized molecules to generate polymer molecules, and condensation of the polymer molecules on the substyrate to form a covalently bound deposition on the subatrate without otherwise changing the mechanical behavior of the substrate material or its surface texture.
Claim 19
Independent Claim
158 words
A method of making surface modified substrate materials whose modified surface, when exposed to blood, is both thrombi- and emboli-resistant over extended periods of time, comprising: exposing the substrate material to plasma gas discharge in the presence of an inert gas for a period of time sufficient to etch and activate the surface of the substrate; and exposing the substrate material to plasma gas discharge in the presence of a fluorinated hydrocarbon gas, whereby chemical deposition in the presence of the plasma discharge results in a fluorocarbon polymer with short chain-length fluorocarbon polymer side or end groups deposited on the substrate as a thin, covalently bound deposition, the plasma discharge causing ionization of the gas molecules, partial reaction of the ionized molecules to generate polymer molecules, and condensation of the polymer molecules on the substyrate to form a covalently bound deposition on the subatrate without otherwise changing the mechanical behavior of the substrate material or its surface texture.
Claim 20
Dependent Claim
17 words
The method of claim 14 wherein said inert gas is argon and said fluorinate hydrocarbon is tetrafluoroethylene.
References Cited (Backward Citations)
US3817701A
Cited
US3839743A
Cited
US4188426A
Cited
JPS54122529A
Cited
US4261806A
Cited
US4264750A
Cited
US4312575A
Cited
US4488954A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-06 | 1990-10-06 | 1991-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-06 | 1994-10-06 | 1995-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-06 | 1998-10-06 | 1999-04-07 | $7700.00 | Window Closed / Lapsed |