Deposition processes: incorporating solvent dye into electrophoretic resin on metal surface
Assignee: Solvay Solutions UK Ltd
•
Filing: 1985-05-07
•
Granted: 1987-04-07
•
Expires: 2005-05-07
Abstract
Abstract A process for the deposition of a film of an electrophoretic resin upon the surface of a substrate which comprises the steps of (i) electrophoretically depositing from a bath comprising water, a water miscible organic solvent and the resin, a film of the resin upon the surface of the substrate (ii) immersing said film in a solution of a solvent dye in a solvent medium comprising water, a water miscible organic solvent and a hydrotrope, the amount of said solvent dye dissolved in said solvent medium being sufficient for the absorption into the resin film of sufficient dye to impart the desired coloration to the resin film, the amount of said hydrotrope and said solvent being sufficient so that said amount of such solvent dye will dissolve in the solvent medium and (iii) curing the resin.
Inventors
- 👤 Stanley Renton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 01:43
CPC Classifications
B; B05; B05D; B05D3/00; B05D3/10; C; C08; C08J; C08J7/00; C08J7/04; C08J7/06; C08J7/065; C09; C09D; C09D5/00; C09D5/44; Y; Y10; Y10S; Y10S8/00; Y10S8/938
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
168 words
A process for the deposition of a film of an electrophoretic resin upon the surface of a metal substrate which comprises the steps of (i) electrophoretically depositing from a bath comprising water, a water miscible organic solvent and an anaphoretic or cataphoretic resin, a film of the resin upon the surface of the metal substrate (ii) immersing said film in a solution of a solvent dye in a solvent medium comprising water, a water miscible organic solvent and a hydrotrope, the amount of said solvent dye dissolved in said solvent medium being sufficient for the absorption into the resin film of sufficient dye to impart the desired colouration to the resin film, the amount of said hydrotrope and said solvent being (a) sufficient so that said amount of such solvent dye will dissolve in the solvent medium, and (b) such that said desired coloration is imparted to said resin film while immersed in said solvent medium without significant damage to the resin film and (iii) curing the resin.
Claim 2
Dependent Claim
168 words
A process for the deposition of a film of an electrophoretic resin upon the surface of a metal substrate which comprises the steps of (i) electrophoretically depositing from a bath comprising water, a water miscible organic solvent and an anaphoretic or cataphoretic resin, a film of the resin upon the surface of the metal substrate (ii) immersing said film in a solution of a solvent dye in a solvent medium comprising water, a water miscible organic solvent and a hydrotrope, the amount of said solvent dye dissolved in said solvent medium being sufficient for the absorption into the resin film of sufficient dye to impart the desired colouration to the resin film, the amount of said hydrotrope and said solvent being (a) sufficient so that said amount of such solvent dye will dissolve in the solvent medium, and (b) such that said desired coloration is imparted to said resin film while immersed in said solvent medium without significant damage to the resin film and (iii) curing the resin.
Claim 3
Dependent Claim
35 words
The process of claim 1, wherein the electrophoretic resin is an epoxy/urea formaldehyde resin, an acrylic resin or a blend of (a) said epoxy/urea formaldehyde resin or (b) said acrylic resin with a polyester resin.
Claim 4
Dependent Claim
23 words
The process of claim 1, wherein the resin film after curing which is deposited in step (i) is at least one micron thick.
Claim 5
Dependent Claim
18 words
The process of claim 3, wherein the resin film after curing is from 1 to 20 microns thick.
Claim 6
Dependent Claim
18 words
The process of claim 4, wherein the resin film after curing is from 5 to 10 microns thick.
Claim 7
Dependent Claim
37 words
The process of claim 1, wherein the solvent medium in which the solvent dye is dissolved, comprises water and a water miscible organic solvent selected from the group consisting of water soluble alcohols, glycol ethers and ketones.
Claim 8
Dependent Claim
11 words
The process of claim 6, wherein said organic solvent is butoxyethanol.
Claim 9
Dependent Claim
37 words
The process of claim 6, wherein the bath from which the resin is deposited in step (i) and the solvent medium in which the solvent is dissolved in step (ii) both contain the same water miscible solvent.
Claim 10
Dependent Claim
18 words
The process of claim 6, wherein the solvent medium comprises from 20 to 100 gms/liter of organic solvent.
Claim 11
Dependent Claim
17 words
The process of claim 7, wherein the solvent medium comprises from 75 to 150 gms/liter of butoxyethanol.
Claim 12
Dependent Claim
13 words
The process of claim 1, wherein the dye is a metallized Solvent Dye.
Claim 13
Dependent Claim
13 words
The process of claim 11, wherein the dye is a metallized azo dye.
Claim 14
Dependent Claim
25 words
The process of claim 11, wherein the dye is present in the solvent medium in a quantity of from 0.05 to 5.0 gms per liter.
Claim 15
Dependent Claim
19 words
The process of claim 13, wherein the dye is present in a quantity of from 0.1 to 2.0 gms/liter.
Claim 16
Dependent Claim
32 words
The process of claim 1, wherein the hydrotrope is an alkali metal or ammonium salt of an aromatic sulphonic acid containing a total of from 6 to 10 carbon atoms per molecule.
Claim 17
Dependent Claim
18 words
The process of claim 1, wherein the solvent medium contains from 1 to 500 gms/liter of a hydrotrope.
Claim 18
Dependent Claim
18 words
The process of claim 16, wherein the solvent medium comprises from 50 to 200 gms/liter of a hydrotrope.
Claim 19
Dependent Claim
37 words
The process of claim 2, wherein the solvent medium comprises a hydrotrope which is an alkali metal or ammonium salt of an aromatic sulphonic acid comprising a total of from 6 to 10 carbon atoms per molecule.
Claim 20
Dependent Claim
28 words
The process of claim 18, wherein the solvent medium comprises a water miscible organic solvent selected from the group consisting of water soluble alcohols, glycol ethers and ketones.
Claim 21
Dependent Claim
28 words
The process of claim 1, wherein the solvent medium comprises a water miscible organic solvent selected from the group consisting of water soluble alcohols, glycol ethers and ketones.
Claim 22
Dependent Claim
71 words
The process of claim 18, wherein the solvent medium comprises a water miscible organic solvent selected from the group consisting of water soluble alcohols, glycol ethers and ketones; the solvent medium comprises from 20 to 100 gms/liter of organic solvent; the dye is present in the solvent medium in a quantity of from 0.05 to 5.0 gms per liter; the solvent medium contains from 1 to 500 gms/liter of a hydrotrope.
Claim 23
Dependent Claim
71 words
The process of claim 18, wherein the solvent medium comprises a water miscible organic solvent selected from the group consisting of water soluble alcohols, glycol ethers and ketones; the solvent medium comprises from 75 to 150 gms/liter of organic solvent; the dye is present in the solvent medium in a quantity of from 0.1 to 2.0 gms per liter; the solvent medium contains from 50 to 200 gms/liter of a hydrotrope.
Claim 24
Dependent Claim
26 words
The process of claim 21, wherein the resin film after curing is from 1 to 20 microns thick, and the dye is a metallized Solvent Dye.
Claim 25
Dependent Claim
26 words
The process of claim 22, wherein the resin film after curing is from 5 to 10 microns thick, and the dye is a metallized azo dye.
Claim 26
Dependent Claim
25 words
The process of claim 24, wherein said dye is selected from the group consisting of Solvent Yellow 25, Solvent Orange 11 and Solvent Orange 59.
Claim 27
Dependent Claim
22 words
The process of claim 25, wherein butoxyethanol is used as the water miscible solvent in step (i) and also in step (ii).
Claim 28
Dependent Claim
25 words
The process of claim 1, wherein said dye is selected from the group consisting of Solvent Yellow 25, Solvent Orange 11 and Solvent Orange 59.
References Cited (Backward Citations)
US3619399A
Cited
US3839174A
Cited
GB1498144A
Cited
JPS53136048A
Cited
US4163702A
Cited
GB2145737A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-06 | 1990-10-06 | 1991-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-06 | 1994-10-06 | 1995-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-06 | 1998-10-06 | 1999-04-07 | $7700.00 | Window Closed / Lapsed |