Method of manufacture of a molded friction pad
Assignee: Motors Liquidation Co
•
Filing: 1985-02-11
•
Granted: 1987-03-24
•
Expires: 2005-02-11
Abstract
Abstract A method of forming a friction pad utilizing two distinct compounds. One of the compounds has a high fiber content and the other has a high flow characteristic. The compounds are placed in respective layers in a mold and are compressed to form a composite piece which is placed in a second mold cavity along with a perforated metal plate. Heat and pressure are then applied to the composite piece in the second mold cavity to cause the high flow characteristic compound to flow and enclose the metal plate such that the two compounds and the metal plate are firmly bonded into an integral friction pad.
Inventors
- 👤 Chinh T. Nguyen
- 👤 Stanley E. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:59
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/68; B29C70/70; B29C37/00; B29C37/0078; B29C37/0082; B29C37/0085; B29C43/00; B29C43/02; B29C43/14; B29C43/18; B29C43/20; B29C43/203; B29C70/02; B29C70/021; B29C70/023; F; F16; F16G; F16G5/00; F16G5/16; F16G5/18; B29K; B29K2105/00; B29K2105/06; B29K2105/12; B29K2705/00; B29L; B29L2031/00; B29L2031/16; B29L2031/748; B29L2031/7482
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
245 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds in two separate individual layers at a ratio of four parts of the first compound and one part of the second compound in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity to form a composite piece; removing the composite piece from the mold cavity; placing a multi-perforate metal plate in a second cavity; supporting the metal plate in the second cavity on pins disposed in two of the perforations to provide a space between the bottom of the second cavity and the metal plate; placing the composite piece in the second cavity abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the second compound and to cause the two compounds to be firmly bonded together cooperating with the metal unit to form a friction pad; and removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain.
Claim 2
Independent Claim
245 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds in two separate individual layers at a ratio of four parts of the first compound and one part of the second compound in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity to form a composite piece; removing the composite piece from the mold cavity; placing a multi-perforate metal plate in a second cavity; supporting the metal plate in the second cavity on pins disposed in two of the perforations to provide a space between the bottom of the second cavity and the metal plate; placing the composite piece in the second cavity abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the second compound and to cause the two compounds to be firmly bonded together cooperating with the metal unit to form a friction pad; and removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain.
Claim 3
Independent Claim
267 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds in two separate individual layers at a ratio in the range of 3.5 to 4.0 parts of the first compound and 1.0 part of the second compound in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity to form a molded slug; removing the molded slug from the mold cavity; placing a multi-perforate metal plate in a second cavity; supporting the metal plate in the second cavity on pins disposed in two of the perforations to provide a space between the bottom of the second cavity and the metal plate; placing the molded slug in the second cavity with the second compound thereof abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the second compound and to cause the two compounds to be firmly bonded together and cooperating with the metal unit to form a friction pad; removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain; and curing the friction pad at an elevated temperature in an oven.
Claim 4
Independent Claim
267 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds in two separate individual layers at a ratio in the range of 3.5 to 4.0 parts of the first compound and 1.0 part of the second compound in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity to form a molded slug; removing the molded slug from the mold cavity; placing a multi-perforate metal plate in a second cavity; supporting the metal plate in the second cavity on pins disposed in two of the perforations to provide a space between the bottom of the second cavity and the metal plate; placing the molded slug in the second cavity with the second compound thereof abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the second compound and to cause the two compounds to be firmly bonded together and cooperating with the metal unit to form a friction pad; removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain; and curing the friction pad at an elevated temperature in an oven.
Claim 5
Independent Claim
207 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds at a ratio in the range of 3.5-4.0:1 in two separate layers in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity; removing the composite piece from the mold cavity; placing a perforated metal plate in a second cavity; supporting the metal plate on pins disposed in the second cavity to provide a space between the bottom of the cavity and the metal plate; placing the composite piece in the second cavity abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the compounds to form a friction pad; and removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain.
Claim 6
Independent Claim
207 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds at a ratio in the range of 3.5-4.0:1 in two separate layers in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity; removing the composite piece from the mold cavity; placing a perforated metal plate in a second cavity; supporting the metal plate on pins disposed in the second cavity to provide a space between the bottom of the cavity and the metal plate; placing the composite piece in the second cavity abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the compounds to form a friction pad; and removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain.
Claim 7
Independent Claim
203 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds in two separate layers at a 3.67:1 ratio in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity; removing the composite piece from the mold cavity; placing a perforated metal plate in a second cavity; supporting the metal plate on pins disposed in the second cavity to provide a space between the bottom of the cavity and the metal plate; placing the composite piece in the second cavity abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the compounds to form a friction pad; and removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain.
Claim 8
Independent Claim
203 words
A method of forming a friction pad for use with a drive chain from a first high fiber content friction compound and second compound having a high flow characteristic, both said compounds having the same resin, and a metal plate to provide structural support in the drive chain; said method comprising: placing the compounds in two separate layers at a 3.67:1 ratio in a mold cavity; applying pressure through a plunger to the compounds in the mold cavity; removing the composite piece from the mold cavity; placing a perforated metal plate in a second cavity; supporting the metal plate on pins disposed in the second cavity to provide a space between the bottom of the cavity and the metal plate; placing the composite piece in the second cavity abutting the metal insert; applying heat and pressure to the second cavity to cause the second compound to flow through the perforations and around the outer edges of the metal plate to enclose the metal plate in the compounds to form a friction pad; and removing the friction pad from the second cavity, said support pins leaving openings in said friction pad to permit connection with said metal plate at assembly to the drive chain.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-23 | 1990-09-22 | 1991-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-23 | 1994-09-22 | 1995-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-23 | 1998-09-22 | 1999-03-24 | $7700.00 | Window Closed / Lapsed |