Assignee: Cleveland Advanced Manufacturing Program
•
Filing: 1984-09-17
•
Granted: 1987-03-24
•
Expires: 2004-09-17
Abstract
Abstract A molding medium and process for making it, preferably for use in the evaporative pattern casting process, is disclosed. The molding medium comprises, in one embodiment, a base granular molding material having spherically shaped grains wherein the individual grains of the material are coated with a refractory material. Preferably the grains are coated first with a binding agent and then mixed with a refractory material, which may be zirconium oxide. After coating, the material is fired at a high temperature, crushed and screened to size, according to one method. Alternatively, the base molding material may itself be a refractory material, in which case the refractory material is mixed with a binding agent to agglomerate the base material into substantially spherical particles and a refractory coating need not be applied. In either embodiment, substantially spherical free-flowing particles are produced having a low angle of repose. This allows the molding medium to come into close contact with the pattern of the object to be cast. Furthermore, the use of a refractory coating for the particles of the molding medium or a refractory material for the molding medium itself eliminates the need for a refractory wash or coating on the pattern.
Inventors
- 👤 Leslie D. Rikker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:42
CPC Classifications
B; B22; B22C; B22C9/00; B22C9/02; B22C9/04; B22C9/046; B22C1/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
162 words
In a process for forming castings comprising the steps of producing a pattern of the product to be cast from a material which is gasifiable substantially without residue upon subjection to a molten casting charge and having a shape conforming to the product to be cast, surrounding the pattern in a casting box with a molding material comprising unbound particulate material and pouring a charge of molten metal into the casting box to evaporate the pattern and produce a casting in the shape of the pattern, the improvement comprising the step of forming said molding material of a particulate material having a refractory component wherein said particulate material comprises particles having a substantially spherical shape formed by man and not found in nature, said refractory component eliminating the need for a refractory wash coat to be applied to said pattern, said spherical shape of said particles allowing substantially uniform pressure to be applied by said molding material to surfaces of said pattern.
Claim 2
Dependent Claim
162 words
In a process for forming castings comprising the steps of producing a pattern of the product to be cast from a material which is gasifiable substantially without residue upon subjection to a molten casting charge and having a shape conforming to the product to be cast, surrounding the pattern in a casting box with a molding material comprising unbound particulate material and pouring a charge of molten metal into the casting box to evaporate the pattern and produce a casting in the shape of the pattern, the improvement comprising the step of forming said molding material of a particulate material having a refractory component wherein said particulate material comprises particles having a substantially spherical shape formed by man and not found in nature, said refractory component eliminating the need for a refractory wash coat to be applied to said pattern, said spherical shape of said particles allowing substantially uniform pressure to be applied by said molding material to surfaces of said pattern.
Claim 3
Dependent Claim
22 words
The improvement recited in claim 1 wherein said step of forming comprises the step of coating the particles with a refractory material.
Claim 4
Dependent Claim
25 words
The improvement recited in claim 2, further comprising the step of coating the particles with a binding agent prior to coating with a refractory material.
Claim 5
Dependent Claim
14 words
The improvement recited in claim 1 wherein said particulate material comprises a refractory material.
Claim 6
Dependent Claim
15 words
The improvement recited in claim 1, further comprising the step of firing said particulate material.
Claim 7
Dependent Claim
147 words
A process for forming castings comprising the steps of: producing a pattern of the product to be cast from a material which is gasifiable substantially without residue upon subjection to a molten casting charge and having a shape conforming to the product to be cast; surrounding the pattern in a casting box with a molding material comprising unbound particulate material, said particulate material having a refractory component and comprising particles having a substantially spherical shape formed by man and not found in nature, said refractory component eliminating the need for a refractory wash coat to be applied to the pattern, said spherical shape of said particles allowing substantially uniform pressure to be applied by said molding material to surfaces of said pattern; and pouring the charge of molten metal into the casting box to evaporate the pattern and produce a casting in the shape of the pattern.
Claim 8
Dependent Claim
147 words
A process for forming castings comprising the steps of: producing a pattern of the product to be cast from a material which is gasifiable substantially without residue upon subjection to a molten casting charge and having a shape conforming to the product to be cast; surrounding the pattern in a casting box with a molding material comprising unbound particulate material, said particulate material having a refractory component and comprising particles having a substantially spherical shape formed by man and not found in nature, said refractory component eliminating the need for a refractory wash coat to be applied to the pattern, said spherical shape of said particles allowing substantially uniform pressure to be applied by said molding material to surfaces of said pattern; and pouring the charge of molten metal into the casting box to evaporate the pattern and produce a casting in the shape of the pattern.
Claim 9
Dependent Claim
22 words
The process recited in claim 6 wherein said step of surrounding comprises surrounding the pattern with particles coated with a refractory material.
Claim 10
Dependent Claim
25 words
The process recited in claim 7 further comprising the step of coating the particles with a binding agent prior to coating with a refractory material.
Claim 11
Dependent Claim
23 words
The process recited in claim 6 wherein said step of surrounding comprises surrounding the pattern with a particulate material comprising a refractory material.
Claim 12
Dependent Claim
15 words
The process recited in claim 6, further comprising the step of firing said particulate material.
References Cited (Backward Citations)
US2701902A
Cited
US2829060A
Cited
US2830343A
Cited
US3069292A
Cited
US3148422A
Cited
US3169288A
Cited
US3314116A
Cited
US3270382A
Cited
US3498360A
Cited
US3351123A
Cited
US3157924A
Cited
GB1281082A
Cited
US3934637A
Cited
JPS5087104A
Cited
US4010791A
Cited
US4243420A
Cited
JPS5711746A
Cited
DE3136888A1
Cited
US4491482A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-23 | 1990-09-22 | 1991-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-23 | 1994-09-22 | 1995-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-23 | 1998-09-22 | 1999-03-24 | $7700.00 | Window Closed / Lapsed |