Crosslinked vinyl polymer compositions and process for preparing molded shaped articles
Assignee: Henkel Corp
•
Filing: 1984-09-10
•
Granted: 1987-03-10
•
Expires: 2004-09-10
Abstract
Abstract Liquid molding compositions are provided which include methylol amino compounds and vinyl polymers that can crosslink with such amino compounds. These liquid molding compositions are used to treat fibrous substrates, and, by drying, heating, and molding, a molded, shaped article is produced having a substrate with from about 5 to about 85% by weight of a crosslinked vinyl polymer, from about 1 to 15% by weight of a methylol amino compound that the vinyl polymer is crosslinked to, and less than 10% by weight water.
Inventors
- 👤 John A. Thompson
- 👤 Christopher B. Keogh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 20:58
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08J5/00; C08J5/04; C08L; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08J2325/00; C08J2325/02; C08J2325/04; C08J2325/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
84 words
A liquid composition for treating and molding fibrous substrates into shaped articles comprising: (a) from about 40% to about 60% by weight of carboxylated polystyrene having a glass transition temperature in excess of 35° C.; (b) from about 2.5% to about 12% of an alkylated melamine formaldehyde resin; (c) from about 15 to about 60% by weight water; (d) a sufficient amount of a fugitive base to maintain an alkaline pH, and (e) from about 15 to about 25% by weight of polyvinyl acetate.
Claim 2
Dependent Claim
84 words
A liquid composition for treating and molding fibrous substrates into shaped articles comprising: (a) from about 40% to about 60% by weight of carboxylated polystyrene having a glass transition temperature in excess of 35° C.; (b) from about 2.5% to about 12% of an alkylated melamine formaldehyde resin; (c) from about 15 to about 60% by weight water; (d) a sufficient amount of a fugitive base to maintain an alkaline pH, and (e) from about 15 to about 25% by weight of polyvinyl acetate.
Claim 3
Dependent Claim
26 words
A composition as described in claim 1 wherein the fugitive base is sufficient to maintain the ph of the composition equal to or greater than 8.5.
Claim 4
Dependent Claim
26 words
A composition as described in claim 1 wherein the fugitive base (C) is selected from the group consisting of 2-amino-2-methyl-1 propanol, ammonia, methylamine, triethanolamine and ethylamine.
Claim 5
Dependent Claim
170 words
A liquid composition for treating and molding fibrous substrates into shaped articles consisting essentially of: (a) from about 5% to about 25% of a vinyl acrylate polymer having a minimum glass transition temperature of 35° C., said acrylate polymer being crosslinkable with melamine formaldehyde, and being a copolymer of: (1) an acrylate monomer selected from the group consisting of methyl acrylate and methylmethacrylate and mixtures thereof, and (ii) ethyl acrylate, and (iii) an acrylic acid monomer from the group consisting of acrylic acid and methacrylic acid and mixtures thereof wherein the weight ratio of (i) to (ii) is about 2:1 to about 1:2 and a weight ratio of (i) to (ii) to (iii) is about 50:1 to about 8:1; (b) from about 20 to about 45% by weight of polyvinyl acetate; (c) from about 2.5% to about 8% by wieght of an alkylated melamine formaldehyde resin; (d) from about 15 to about 60% by weight water; and (e) a sufficient amount of a fugitive base to maintain an alkaline pH.
Claim 6
Dependent Claim
170 words
A liquid composition for treating and molding fibrous substrates into shaped articles consisting essentially of: (a) from about 5% to about 25% of a vinyl acrylate polymer having a minimum glass transition temperature of 35° C., said acrylate polymer being crosslinkable with melamine formaldehyde, and being a copolymer of: (1) an acrylate monomer selected from the group consisting of methyl acrylate and methylmethacrylate and mixtures thereof, and (ii) ethyl acrylate, and (iii) an acrylic acid monomer from the group consisting of acrylic acid and methacrylic acid and mixtures thereof wherein the weight ratio of (i) to (ii) is about 2:1 to about 1:2 and a weight ratio of (i) to (ii) to (iii) is about 50:1 to about 8:1; (b) from about 20 to about 45% by weight of polyvinyl acetate; (c) from about 2.5% to about 8% by wieght of an alkylated melamine formaldehyde resin; (d) from about 15 to about 60% by weight water; and (e) a sufficient amount of a fugitive base to maintain an alkaline pH.
Claim 7
Dependent Claim
19 words
A composition as defined in claim 1, wherein said carboxylated polystrene has a glass transition temperature of 103° C.
Claim 8
Dependent Claim
176 words
A liquid composition for treating and molding fibrous substrates into shaped articles comprising: (a) from about 5 to about 20% by weight of carboxylated polystyrene, having a glass transition temperature in excess of 35° C.; (b) from about 2.5 to about 7% by weight of an alkylated melamine formaldehyde resin; (c) from about 15 to about 60% by weight of water; (d) a sufficient amount of a fugitive base to maintain an alkaline pH; (e) from about 30 to about 45% by weight of a polyvinyl acetate; (f) from about 5 to about 15% by weight of a vinyl acrylate polymer having a glass transition temperature in excess of 35° C., said acrylate polymer being crosslinkable with melamine formaldehyde, and being a copolymer of: (i) methyl acrylate and methylmethacrylate and mixtures thereof, and (ii) ethyl acrylate, and (ii) acrylic acid and methacrylic acid and mixtures thereof in a weight ratio of (i) to (ii) of about 2:1 to about 1:2 and a weight ratio of (i) or (ii) to (iii) of about 50:1 to about 8:1.
Claim 9
Dependent Claim
176 words
A liquid composition for treating and molding fibrous substrates into shaped articles comprising: (a) from about 5 to about 20% by weight of carboxylated polystyrene, having a glass transition temperature in excess of 35° C.; (b) from about 2.5 to about 7% by weight of an alkylated melamine formaldehyde resin; (c) from about 15 to about 60% by weight of water; (d) a sufficient amount of a fugitive base to maintain an alkaline pH; (e) from about 30 to about 45% by weight of a polyvinyl acetate; (f) from about 5 to about 15% by weight of a vinyl acrylate polymer having a glass transition temperature in excess of 35° C., said acrylate polymer being crosslinkable with melamine formaldehyde, and being a copolymer of: (i) methyl acrylate and methylmethacrylate and mixtures thereof, and (ii) ethyl acrylate, and (ii) acrylic acid and methacrylic acid and mixtures thereof in a weight ratio of (i) to (ii) of about 2:1 to about 1:2 and a weight ratio of (i) or (ii) to (iii) of about 50:1 to about 8:1.
Claim 10
Dependent Claim
90 words
A liquid composition for treating and molding fibrous substrates into shaped articles comprising: (a) from about 15% to about 35% by weight of carboxylated polystyrene, having a glass transition temperature in excess of 35° C. and being crosslinkable with melamine formaldehyde; (b) from about 20 to about 30% by weight of polystyrene; (c) a sufficient amount of a fugitive base to maintain an alkaline pH; (d) from about 3 to about 10% by weight of an alkylated melamine resin; and (e) from about 15 to about 55% by weight water.
Claim 11
Dependent Claim
90 words
A liquid composition for treating and molding fibrous substrates into shaped articles comprising: (a) from about 15% to about 35% by weight of carboxylated polystyrene, having a glass transition temperature in excess of 35° C. and being crosslinkable with melamine formaldehyde; (b) from about 20 to about 30% by weight of polystyrene; (c) a sufficient amount of a fugitive base to maintain an alkaline pH; (d) from about 3 to about 10% by weight of an alkylated melamine resin; and (e) from about 15 to about 55% by weight water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-09 | 1990-09-08 | 1991-03-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-09 | 1994-09-08 | 1995-03-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-09 | 1998-09-08 | 1999-03-10 | $7700.00 | Window Closed / Lapsed |