Diamond-like carbon films and process for production thereof
Assignee: Applied Biosystems Inc
•
Filing: 1986-03-20
•
Granted: 1987-03-03
•
Expires: 2006-03-20
Abstract
Abstract Improved diamond-like carbon films of improved properties are deposited on various substrates utilizing a plasma assisted chemical vapor transport process (PACVT) process in which hydrogen is employed as the reactive process feedgas and in which the deposition process is conducted in a controllably energetic ion bombardment of the surface on which the films are grown by introducing the hydrogen feedgas into the reactor volume through a porous graphite electrode into a defined plasma geometry.
Inventors
- 👤 N. Venkataramanan
- 👤 Charles B. Zarowin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:16
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/26
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
49 words
In a plasma assisted chemical vapor transport process for the deposition of a diamond-like carbon film on a substrate in a plasma reaction chamber the improvement comprising employing hydrogen gas as the process gas and introducing said hydrogen gas into a plasma reaction chamber through a porous graphite electrode.
Claim 2
Dependent Claim
49 words
In a plasma assisted chemical vapor transport process for the deposition of a diamond-like carbon film on a substrate in a plasma reaction chamber the improvement comprising employing hydrogen gas as the process gas and introducing said hydrogen gas into a plasma reaction chamber through a porous graphite electrode.
Claim 3
Dependent Claim
43 words
The process of claim 1 wherein the plasma reaction chamber has a defined plasma geometry such that the power density in the plasma varies nearly linearly with power supplied and the plasma reactor chamber maintains an essentially uniform gas pressure in the reactor.
Claim 4
Dependent Claim
26 words
The process of claim 2 wherein the power density in the plasma is more than 5 watts/cm 3 and the gas pressure is about 2 Torr.
Claim 5
Dependent Claim
29 words
The process of claim 2 wherein the hydrogen gas is introduced through a process graphite electrode having a gas flow impedance on the order of about 10 -2 sec/cc.
Claim 6
Dependent Claim
87 words
A plasma assisted chemical vapor transport process for the production of a diamond-like carbon film comprising: (a) introducing into a plasma reactor of fixed plasma geometry, a hydrogen feedgas through a porous graphite electrode, (b) forming a volatile hydrocarbon reaction product by reaction of the hydrogen with carbon at the electrode surface, (c) transporting the volatile hydrocarbon reaction product to a substrate mounted on a second electrode (d) depositing a diamond-like carbon film on said substrate from said volatile hydrocarbon product in a reverse heterogeneous chemical reaction.
Claim 7
Dependent Claim
87 words
A plasma assisted chemical vapor transport process for the production of a diamond-like carbon film comprising: (a) introducing into a plasma reactor of fixed plasma geometry, a hydrogen feedgas through a porous graphite electrode, (b) forming a volatile hydrocarbon reaction product by reaction of the hydrogen with carbon at the electrode surface, (c) transporting the volatile hydrocarbon reaction product to a substrate mounted on a second electrode (d) depositing a diamond-like carbon film on said substrate from said volatile hydrocarbon product in a reverse heterogeneous chemical reaction.
Claim 8
Dependent Claim
43 words
The process of claim 5 wherein the plasma reaction chamber has a defined plasma geometry such that the power density in the plasma varies nearly linearly with power supplied and the plasma reactor chamber maintains an essentially uniform gas pressure in the reactor.
Claim 9
Dependent Claim
26 words
The process of claim 5 wherein the power density in the plasma is more than 5 watts/cm 3 and the gas pressure is about 2 Torr.
Claim 10
Dependent Claim
29 words
The process of claim 5 wherein the hydrogen gas is introduced through a process graphite electrode having a gas flow impedance on the order of about 10 -2 sec/cc.
Claim 11
Dependent Claim
12 words
A diamond-like carbon film produced according to the process of claim 5.
Claim 12
Dependent Claim
83 words
The diamond-like carbon film of claim 9 having the following characteristics: (a) a transparency of more than 50% for wavelengths above about 200 nm and more than 90% above about 400 nm for films of a thickness of about 1/2 μm, (b) an index of refraction of about 2 at 850 nm, (c) a hardness of about sapphire, (d) chemical inertness to concentrated HNO 3 , hot KOH solution and HF solution, and (e) a resistivity of about 10 11 ohm-cm at MV/cm.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-02 | 1990-09-01 | 1991-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-02 | 1994-09-01 | 1995-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-02 | 1998-09-01 | 1999-03-03 | $7700.00 | Window Closed / Lapsed |