Surface preparation of ceramic substrates for metallization
Assignee: AMP-AKZO Corp A CORP OF
•
Filing: 1984-12-07
•
Granted: 1987-03-03
•
Expires: 2004-12-07
Abstract
Abstract A process for preparing a ceramic substrate for metallization wherein a surface of the ceramic substrate is contacted with an admixture comprised of an inert solid material and a composition containing one or more alkali metal compounds. The admixture and the substrate are heated at least to a temperature at which the alkali metal composition becomes molten. The molten alkali metal composition is kept in contact with the ceramic surface for a time period sufficient to etch the surface and thus prepare it for adherent deposition of metal. The presence of the inert solid material in the admixture prevents coalescence of the alkali metal composition on the ceramic surface. Uniform surface coverage with catalyst and metal and an adherent bond of metal to the ceramic surface are ensured by treatment with the admixture. Furthermore, an article comprised of metal directly and adherently bonded onto a ceramic substrate is provided.
Inventors
- 👤 Michael A. DeLuca
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 17:49
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B37/00; C04B37/003; C04B37/006; C04B37/02; C04B37/023; C04B37/026; C04B41/45; C04B41/52; C04B41/53; C04B41/80; C04B41/81; C04B41/89; C04B41/91; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/1851; H; H05; H05K; H05K3/00; H05K3/38; H05K3/381; H10; H10W; H10W70/00; H10W70/01; H10W70/05; C04B2111/00; C04B2111/20; C04B2111/26; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/123; C04B2237/124; C04B2237/125; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/343; C04B2237/345; C04B2237/346; C04B2237/36; C04B2237/365; C04B2237/368; C04B2237/40; C04B2237/50; C04B2237/52; C04B2237/55; C04B2237/59; C04B2237/592; C04B2237/70; C04B2237/708; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K2203/00; H05K2203/11; H05K2203/1105; H05K3/10; H05K3/18; H05K3/181; Y; Y10; Y10S; Y10S205/00; Y10S205/92
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
156 words
In a process for metallizing a surface of a ceramic substrate which includes adhesion promoting the surface with an alkali metal composition containing one or more alkali metal compounds and subsequently depositing metal on the adhesion promoted surface, the improvement in said adhesion promoting step which comprises: providing an admixture comprised of said alkali metal composition and an inert solid material which is not dissolved or melted by the molten alkali metal composition up to and during the adhesion promotion step; contacting the ceramic surface with the admixture; heating the admixture and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten and which is sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition, the presence of the inert solid material in the admixture preventing coalescence of the alkali metal composition on the ceramic surface during the adhesion promotion.
Claim 2
Dependent Claim
156 words
In a process for metallizing a surface of a ceramic substrate which includes adhesion promoting the surface with an alkali metal composition containing one or more alkali metal compounds and subsequently depositing metal on the adhesion promoted surface, the improvement in said adhesion promoting step which comprises: providing an admixture comprised of said alkali metal composition and an inert solid material which is not dissolved or melted by the molten alkali metal composition up to and during the adhesion promotion step; contacting the ceramic surface with the admixture; heating the admixture and the substrate for a time period and at or above a temperature at which the alkali metal composition becomes molten and which is sufficient to adhesion promote the ceramic surface and render it receptive to subsequent adherent metal deposition, the presence of the inert solid material in the admixture preventing coalescence of the alkali metal composition on the ceramic surface during the adhesion promotion.
Claim 3
Dependent Claim
32 words
The process of claim 1, further comprising the step of forming the admixture by dispersing an inert solid material in finely divided form in an aqueous solution of an alkali metal compound.
Claim 4
Dependent Claim
27 words
The process of claim 1, further comprising the step of forming the admixture by grinding one or more alkali metal compounds and the inert solid material together.
Claim 5
Dependent Claim
31 words
The process of claim 1, further comprising the step of forming the admixture by dispersing the inert solid material in finely divided form in a melt of the alkali metal composition.
Claim 6
Dependent Claim
29 words
The process of claim 1, further comprising the step of forming the admixture by impregnating a fibrous base comprised of the inert solid material with the alkali metal composition.
Claim 7
Dependent Claim
34 words
The process of claim 1, wherein the ceramic substrate is selected from aluminas and beryllias and the ceramic surface is adhesion promoted for a time period between about 5 minutes and about 20 minutes.
Claim 8
Dependent Claim
34 words
The process of claim 1, wherein the ceramic substrate is selected from titanates, mullite, forsterite, steatites and porcelains and the ceramic surface is adhesion promoted for a time period less than about 5 minutes.
Claim 9
Dependent Claim
27 words
The process of claim 1, wherein the admixture is aged the equivalent of at least 12 hours at room temperature before being contacted with the ceramic surface.
Claim 10
Dependent Claim
24 words
The process of claim 1, wherein the adhesion promotion step is carried out at a temperature between about 150° C. and about 1200° C.
Claim 11
Dependent Claim
31 words
The process of claim 1, wherein the inert solid material is an alumina and the ceramic surface is adhesion promoted at a temperature between about 450° C. and about 700° C.
Claim 12
Dependent Claim
23 words
The process of claim 10, wherein the ceramic surface is adhesion promoted at a temperature between about 550° C. and about 650° C.
Claim 13
Dependent Claim
31 words
The process of claim 1, wherein the ceramic substrate is silicon carbide-beryllium oxide and the ceramic surface is adhesion promoted at a temperature between about 450° C. and about 700° C.
Claim 14
Dependent Claim
30 words
The process of claim 1, wherein the inert solid material is titanate and the titanate surface is adhesion promoted at a temperature between about 170° C. and about 450° C.
Claim 15
Dependent Claim
51 words
The process of claim 13, wherein the inert solid material is a titanate containing glasses which rapidly dissolve in the molten alkali metal composition or a titanate containing more than 10 percent glass and the ceramic surface is adhesion promoted at a temperature between about 170° C. and about 250° C.
Claim 16
Dependent Claim
32 words
The process of claim 1, wherein the inert solid material is silicon nitride and the silicon nitride surface is adhesion promoted at a temperature between about 250° C. and about 350° C.
Claim 17
Dependent Claim
34 words
The process of claim 1, wherein said molten alkali metal composition further includes up to about 50% by weight of one or more materials which depress the melting point of said alkali metal composition.
Claim 18
Dependent Claim
34 words
The process of claim 16, wherein said molten alkali metal composition further includes up to about 20% by weight of one or more materials which depress the melting point of said alkali metal composition.
Claim 19
Dependent Claim
23 words
The process of claim 1, wherein said alkali metal composition comprises an alkali metal compound selected from hydroxide, carbonates, nitrates and mixtures thereof.
Claim 20
Dependent Claim
19 words
The process of claim 18, wherein said alkali metal compound is selected from carbonates and nitrates and mixtures thereof.
Claim 21
Dependent Claim
27 words
The process of claim 1, wherein said alkali metal composition comprises an alkali metal compound selected from sodium hydroxide, potassium hydroxide, and sodium carbonate and potassium nitrate.
Claim 22
Dependent Claim
40 words
The process of claim 1, wherein a first metal layer is electrolessly formed on the adhesion promoted ceramic surface and said layer is further plated up to the desired thickness with one or more metals employing electroless or electroplating methods.
Claim 23
Dependent Claim
18 words
The process of claim 1, wherein the ceramic surface is adhesion promoted at a temperature above 150° C.
Claim 24
Dependent Claim
18 words
The process of claim 1, wherein the ceramic surface is adhesion promoted at a temperature above 300° C.
Claim 25
Dependent Claim
23 words
The process of claim 1, wherein the ceramic surface is adhesion promoted at a temperature between about 300° C. and about 650° C.
Claim 26
Dependent Claim
123 words
In a process for adhesion promoting a surface of a ceramic substrate to receive an adherent metal deposit, which process includes adhesion promoting the surface with an alkali metal composition at an elevated temperature, the improvement which comprises: providing an admixture comprised of said alkali metal composition dispersed throughout one or more inert solid materials which will remain solid in the presence of the alkali metal composition in a molten state and which will prevent coalescence of the alkali metal composition on the ceramic surface at least until the alkali metal composition wets the ceramic surface; and contacting the ceramic surface with the admixture at a temperature above about 150° C. and for a time period sufficient to adhesion promote the ceramic surface.
Claim 27
Dependent Claim
123 words
In a process for adhesion promoting a surface of a ceramic substrate to receive an adherent metal deposit, which process includes adhesion promoting the surface with an alkali metal composition at an elevated temperature, the improvement which comprises: providing an admixture comprised of said alkali metal composition dispersed throughout one or more inert solid materials which will remain solid in the presence of the alkali metal composition in a molten state and which will prevent coalescence of the alkali metal composition on the ceramic surface at least until the alkali metal composition wets the ceramic surface; and contacting the ceramic surface with the admixture at a temperature above about 150° C. and for a time period sufficient to adhesion promote the ceramic surface.
Claim 28
Dependent Claim
18 words
The process of claim 25, wherein the ceramic surface has a surface roughness less than about 0.7 micrometers.
Claim 29
Dependent Claim
126 words
A process for producing a printed circuit on a surface of a ceramic substrate comprising: (a) contacting the ceramic surface, with a molten alkali metal composition comprised of an alkali metal compound and an inert solid material in finely divided form to adhesion promote the surface, the inert solid material remaining solid in the presence of the alkali metal composition in a molten state and preventing coalescence of the alkali metal compositions at least until the alkali metal composition wets the ceramic surface; (b) treating the ceramic surface to activate it for electroless metal deposition; (c) depositing metal onto the activated surface; and (d) removing portions of the deposited metal to produce a metal printed circuit conductor pattern adhering to the surface of the ceramic substrate.
Claim 30
Dependent Claim
126 words
A process for producing a printed circuit on a surface of a ceramic substrate comprising: (a) contacting the ceramic surface, with a molten alkali metal composition comprised of an alkali metal compound and an inert solid material in finely divided form to adhesion promote the surface, the inert solid material remaining solid in the presence of the alkali metal composition in a molten state and preventing coalescence of the alkali metal compositions at least until the alkali metal composition wets the ceramic surface; (b) treating the ceramic surface to activate it for electroless metal deposition; (c) depositing metal onto the activated surface; and (d) removing portions of the deposited metal to produce a metal printed circuit conductor pattern adhering to the surface of the ceramic substrate.
Claim 31
Dependent Claim
153 words
A process for producing a metallized conductor pattern on a surface of a ceramic substrate having a surface roughness less than about 0.7 micrometers, the process comprising: contacting the surface with a molten alkali metal composition comprised of one or more alkali metal compounds and inert inorganic oxide particles in finely divided form for a time period sufficient to adhesion promote said surface, the inert inorganic oxide particles not being dissolved or melted by the molten alkali metal composition up to and during the adhesion promotion; rinsing said surface with an aqueous solution; neutralizing said surface with an acid; repeating said rinsing step; contacting said surface with an activator solution providing stannous tin ions and precious metal ions, to render said surface receptive to electroless deposition of a metal; and contacting said surface or selected parts thereof with a metal depositing solution for a time period sufficient to form a metal layer thereon.
Claim 32
Dependent Claim
153 words
A process for producing a metallized conductor pattern on a surface of a ceramic substrate having a surface roughness less than about 0.7 micrometers, the process comprising: contacting the surface with a molten alkali metal composition comprised of one or more alkali metal compounds and inert inorganic oxide particles in finely divided form for a time period sufficient to adhesion promote said surface, the inert inorganic oxide particles not being dissolved or melted by the molten alkali metal composition up to and during the adhesion promotion; rinsing said surface with an aqueous solution; neutralizing said surface with an acid; repeating said rinsing step; contacting said surface with an activator solution providing stannous tin ions and precious metal ions, to render said surface receptive to electroless deposition of a metal; and contacting said surface or selected parts thereof with a metal depositing solution for a time period sufficient to form a metal layer thereon.
Claim 33
Dependent Claim
126 words
A process for bonding a first ceramic article to a second ceramic article provided with metallization, or to a metal article, comprising the steps of: adhesion promoting at least a portion of the surface of the first ceramic article with a molten alkali metal composition comprising one or more alkali metal compounds and an inert solid material which is not dissolved or melted by the alkali metal composition up to and during the adhesion promotion; adsorbing catalyst on the treated surface of the first ceramic article; depositing a coating of metal on the treated surface with a metal depositing bath; and metallurgically joining the metal coated portion of the first ceramic article to a metallized portion of the second ceramic article or to the metal article.
Claim 34
Dependent Claim
126 words
A process for bonding a first ceramic article to a second ceramic article provided with metallization, or to a metal article, comprising the steps of: adhesion promoting at least a portion of the surface of the first ceramic article with a molten alkali metal composition comprising one or more alkali metal compounds and an inert solid material which is not dissolved or melted by the alkali metal composition up to and during the adhesion promotion; adsorbing catalyst on the treated surface of the first ceramic article; depositing a coating of metal on the treated surface with a metal depositing bath; and metallurgically joining the metal coated portion of the first ceramic article to a metallized portion of the second ceramic article or to the metal article.
References Cited (Backward Citations)
US3309760A
Cited
US3296012A
Cited
US3672986A
Cited
US3628999A
Cited
US3690921A
Cited
US3925578A
Cited
US3772078A
Cited
US3907621A
Cited
US3772056A
Cited
US3930963A
Cited
US3959547A
Cited
US3993802A
Cited
US3994727A
Cited
JPS5319932A
Cited
DE3032508A1
Cited
JPS58167447A
Cited
US4428986A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-02 | 1990-09-01 | 1991-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-02 | 1994-09-01 | 1995-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-02 | 1998-09-01 | 1999-03-03 | $7700.00 | Window Closed / Lapsed |