Inert carbon fiber diaphragm
Assignee: Dow Chemical Co
•
Filing: 1985-10-04
•
Granted: 1987-03-03
•
Expires: 2005-10-04
Abstract
Abstract A diaphragm or membrane for use in electrolysis cells resistant to chemical action thereof is disclosed. In the preferred and illustrated embodiment, a fluoropolymer binder cooperative with a random mix of carbon fibers up to about 13 mm long and up to about 0.01 mm in diameter forms such diaphragm or membrane. The carbon fibers are preferably pliable, nonbrittle, resilient, electrically nonconductive, impervious to chemical attack, and are annealed up to a specified temperature.
Inventors
- 👤 Donald D. Waters
- 👤 Thomas K. Fletcher
- 👤 Stephen P. Krupp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:19
CPC Classifications
C; C25; C25B; C25B13/00; C25B13/04; C25B13/05; C25B13/08
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
92 words
A membrane for use in an electrochemical cell which the membrane is exposed to acid or base materials, the membrane consisting essentially of a felt of carbon fibers which are substantially electrically insulative having various lengths including fibers of up to about 13 mm long and a diameter of up to about 0.01 mm, said fibers bonded with fluoropolymer wherein the weight of the fluoropolymer is up to about 20 percent wherein the fluoropolymer serves as a binding agent securing the carbon fibers in a porous felt sheet having a specified weight.
Claim 2
Dependent Claim
92 words
A membrane for use in an electrochemical cell which the membrane is exposed to acid or base materials, the membrane consisting essentially of a felt of carbon fibers which are substantially electrically insulative having various lengths including fibers of up to about 13 mm long and a diameter of up to about 0.01 mm, said fibers bonded with fluoropolymer wherein the weight of the fluoropolymer is up to about 20 percent wherein the fluoropolymer serves as a binding agent securing the carbon fibers in a porous felt sheet having a specified weight.
Claim 3
Dependent Claim
18 words
The membrane of claim 1 wherein the fibers have a surface area of about 600 m 2 /gm.
Claim 4
Dependent Claim
20 words
The membrane of claim 1 wherein the fibers have a surface area of about 400 m 2 /gm and greater.
Claim 5
Dependent Claim
29 words
The membrane of claim 1 wherein the fibers have random lengths at least about 10 microns long and the membrane weight is up to about 0.23 gm/cm 2 .
Claim 6
Dependent Claim
13 words
The membrane of claim 4 wherein the fibers are nonbrittle to enable handling.
Claim 7
Dependent Claim
51 words
The membrane of claim 1 wherein the fibers are chemically resistant, are pliable and bendable and have at least one percent elongation and are mixed length fibers in a random felting of fibers and are also adhesively bonded by the fluoropolymer, being at least about 10 percent by weight of fluoropolymer.
Claim 8
Dependent Claim
24 words
The membrane of claim 1 wherein the fluoropolymer is between about 10 and about 15 percent by weight and is sintered in the membrane.
Claim 9
Dependent Claim
21 words
The membrane of claim 1 wherein the fibers are annealed and are heat resistant to temperatures up to about 1000° C.
Claim 10
Independent Claim
128 words
A method of forming a membrane for use in an electrolysis cell to divide the cell into two compartments, the method comprising the steps of: (a) making a slurry of a disposable solvent, a fluoropolymer binder, surfactant and carbon fibers, the carbon fibers being characterized by having a surface area per unit weight at least about 400 m 2 /gm, being electrically nonconductive and resistant to chemical attack by the chemicals in the electrolysis cell; (b) pouring the slurry on a supportive surface to form a layer thereon; (c) drying the slurry to form a felted membrane having carbon fibers in a felted pattern; and (d) heating the material to a temperature sufficient to achieve sintering of the fluoropolymer to bind the carbon fibers in the felted pattern.
Claim 11
Independent Claim
128 words
A method of forming a membrane for use in an electrolysis cell to divide the cell into two compartments, the method comprising the steps of: (a) making a slurry of a disposable solvent, a fluoropolymer binder, surfactant and carbon fibers, the carbon fibers being characterized by having a surface area per unit weight at least about 400 m 2 /gm, being electrically nonconductive and resistant to chemical attack by the chemicals in the electrolysis cell; (b) pouring the slurry on a supportive surface to form a layer thereon; (c) drying the slurry to form a felted membrane having carbon fibers in a felted pattern; and (d) heating the material to a temperature sufficient to achieve sintering of the fluoropolymer to bind the carbon fibers in the felted pattern.
Claim 12
Dependent Claim
16 words
The method of claim 9 including the step of removing the solvent by vacuum and heat.
Claim 13
Dependent Claim
28 words
The method of claim 9 including the step of mixing the fibers randomly between the lengths of at least about 10 microns and up to about 13 mm.
Claim 14
Dependent Claim
16 words
The method of claim 9 including the step of grinding the membrane after use to depletion.
References Cited (Backward Citations)
US3989615A
Cited
US4186076A
Cited
US4216073A
Cited
US4396663A
Cited
EP0033262A1
Cited
US4486276A
Cited
US4434206A
Cited
GB2136829A
Cited
US4505797A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-02 | 1990-09-01 | 1991-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-02 | 1994-09-01 | 1995-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-02 | 1998-09-01 | 1999-03-03 | $7700.00 | Window Closed / Lapsed |