Process for pre-resinating cellulose fibers for cellulose composite structures
Assignee: United Technologies Automotive Trim Inc
•
Filing: 1985-05-24
•
Granted: 1987-03-03
•
Expires: 2005-05-24
Abstract
Abstract An improved method of molding articles from air-laid webs wherein resin is deposited in a dry process onto cellulose fibers prior to air-laying. Cellulose material and a resin-containing airstream are simultaneously fed into a comminuting means such as a hammer mill. The cellulose particles thereby produced have a coating which adheres to the surface of the cellulose particles. The cellulose particles retain substantially all of the dry resin coating when pneumatically conveyed and air-laid into a web. The fiber web produced with the resin-coated particles is suitable for use in a conventional molding process whereby the web is molded under sufficient heat and pressure into a molded article having a uniform resin distribution resulting in improved strength and improved structural integrity.
Inventors
- 👤 Stanlake A. Mtangi
- 👤 David H. Fishman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:23
CPC Classifications
D; D21; D21H; D21H5/00; D21H5/26; D21H5/2607; D21H5/2628; B; B27; B27N; B27N1/00; B27N1/02; D21H17/00; D21H17/71; D21H23/00; D21H23/02; D21H23/04; D21H23/06; D21H23/08; D21H23/10
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
157 words
A method of molding objects from a resin containing cellulose particle fiber web, the fiber web is formed by an air-laying process wherein cellulose particles and resin are pneumatically conveyed and deposited on a surface to form a web, the improvement comprises, producing dry resin-coated cellulose particles by simultaneously feeding cellulose material and a dry resin-containing airstream, wherein the resin particle size is about 1 micron to about 5 microns, into at least one comminuting means and retaining the cellulose and resin in the comminuting means for a sufficient period of time so that the resin is uniformly deposited over the surface of the cellulose particles such that substantially all of the resin adheres to the particles during pneumatic conveying and air-laying to form a web, the web is molded at sufficient temperature and pressure thereby producing a molded article having a uniform distribution of resin such that the molded article has high strength and structural integrity.
Claim 2
Independent Claim
157 words
A method of molding objects from a resin containing cellulose particle fiber web, the fiber web is formed by an air-laying process wherein cellulose particles and resin are pneumatically conveyed and deposited on a surface to form a web, the improvement comprises, producing dry resin-coated cellulose particles by simultaneously feeding cellulose material and a dry resin-containing airstream, wherein the resin particle size is about 1 micron to about 5 microns, into at least one comminuting means and retaining the cellulose and resin in the comminuting means for a sufficient period of time so that the resin is uniformly deposited over the surface of the cellulose particles such that substantially all of the resin adheres to the particles during pneumatic conveying and air-laying to form a web, the web is molded at sufficient temperature and pressure thereby producing a molded article having a uniform distribution of resin such that the molded article has high strength and structural integrity.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein the comminuting means is a hammer mill.
Claim 4
Dependent Claim
11 words
The method of claim 1 wherein the cellulose material comprises newsprint.
Claim 5
Dependent Claim
13 words
The method of claim 1 wherein the resin comprises a thermosetting phenolic resin.
Claim 6
Dependent Claim
11 words
The method of claim 1 wherein the cellulose particles are fibers.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein the cellulose particles have an average length of about one-eighth inch.
Claim 8
Dependent Claim
23 words
The method of claim 1 wherein the cellulose particles retain at least about 98% of the resin when air-laid into a fiber web.
Claim 9
Dependent Claim
36 words
The method of claim 1 wherein at least one flame retardant material is entrained in the resin containing airstream and simultaneously fed into the comminuting means with the resin, thereby producing a flame resistant molded article.
Claim 10
Dependent Claim
31 words
The method of claim 1 wherein the web additionally comprises synthetic fiber, said fiber admixed with the resin-coated cellulose fiber to form a stream which is air-laid to form said web.
Claim 11
Dependent Claim
24 words
The method of claim 9 wherein the synthetic fiber is selected from the group consisting of glass fiber polyester, polypropylene, and a combination thereof.
References Cited (Backward Citations)
US3718536A
Cited
US3741863A
Cited
US4302488A
Cited
US4230585A
Cited
US4439477A
Cited
US4379194A
Cited
US4418031A
Cited
US4404250A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-02 | 1990-09-01 | 1991-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-02 | 1994-09-01 | 1995-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-02 | 1998-09-01 | 1999-03-03 | $7700.00 | Window Closed / Lapsed |