Carbon fibre gun barrel
Assignee: Department of National Defence
•
Filing: 1985-02-25
•
Granted: 1987-03-03
•
Expires: 2005-02-25
Abstract
Abstract A barrel section for a lightweight firearm such as a recoilless gun which is subjected to extremely high transient internal pressures and temperatures on firing is formed from an epoxy-resin impregnated carbon fibre material. The material, in the form of an elongated tow is wound on a mandrel, cured and then removed from the mandrel for subsequent operations such as machining and assembly. During manufacture, a gas-erosion preventing layer is formed on the mandrel and a plurality of layers of tow are helically-wound thereon at a helix angle theta =tan-1( sigma axial/ sigma hoop) where sigma axial and sigma hoop are the axial and hoop stresses produced in the barrel section by axial and hoop loads respectively. Lightweight recoilless guns using barrels in accordance with the invention are lighter and less costly to fabricate than conventional guns and are capable of firing upwards of 30 rounds before excessive erosion causes the firearm to be unusable. This is in comparison to a capability of firing only 5 to 10 rounds before failure for conventional guns. Failure is usually the result of the high pressures and temperatures encountered during firing, upwards of 9,000 p.s.i. and 3,000 DEG K.
Inventors
- 👤 David H. Gladstone
- 👤 Raymond Langlois
- 👤 William J. Robertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:22
CPC Classifications
B; B29; B29C; B29C53/00; B29C53/80; B29C53/8008; B29C53/805; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/16; B29C70/20; B29C70/205; B29C70/207; F; F41; F41A; F41A21/00; F41A21/02; B29K; B29K2063/00; B29K2307/00; B29L; B29L2031/00; B29L2031/777
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
131 words
A barrel section for a lightweight weapon system subjected to high transient internal pressures and temperatures on firing, comprising a cured resin-treated multi-filament carbon fibre material which has been provided in a plurality of superimposed layers along the length of said section whereby at least the innermost layer of said material is configured to resist hot gas erosion on firing, the remaining layers comprise a tow of said material helically-wound at an average helix angle with respect to the barrel section axis of θ=tan -1 (σ axial /σ hoop ) where σ axial and σ hoop are the axial and hoop stresses produced in the barrel section by axial and hoop loads respectively, and the thickness of the remaining layers provides a hoop stiffness equivalent to that of a steel barrel.
Claim 2
Dependent Claim
131 words
A barrel section for a lightweight weapon system subjected to high transient internal pressures and temperatures on firing, comprising a cured resin-treated multi-filament carbon fibre material which has been provided in a plurality of superimposed layers along the length of said section whereby at least the innermost layer of said material is configured to resist hot gas erosion on firing, the remaining layers comprise a tow of said material helically-wound at an average helix angle with respect to the barrel section axis of θ=tan -1 (σ axial /σ hoop ) where σ axial and σ hoop are the axial and hoop stresses produced in the barrel section by axial and hoop loads respectively, and the thickness of the remaining layers provides a hoop stiffness equivalent to that of a steel barrel.
Claim 3
Dependent Claim
20 words
The barrel section of claim 1, wherein θ lies in the range of 70° to 78° to the section axis.
Claim 4
Dependent Claim
15 words
The barrel section of claim 1, wherein θ is approximately 71° to the section axis.
Claim 5
Dependent Claim
26 words
The barrel section of claim 1, including, adjacent one end thereof, a plurality of external threads for connection to a breech portion of said weapon system.
Claim 6
Dependent Claim
26 words
The barrel section of claim 1, wherein the wall thickness of the barrel section is sufficient to provide said barrel section with a desired hoop stiffness.
Claim 7
Dependent Claim
21 words
The barrel section of claim 1 wherein at least said innermost layer comprises a fabric formed of said carbon fibre material.
Claim 8
Dependent Claim
31 words
The barrel section of claim 6 wherein the outer diameter of said section progressively decreases from a zone adjacent a breech end thereof to a zone adjacent a muzzle end thereof.
Claim 9
Dependent Claim
38 words
The barrel section of claim 1 wherein at least the innermost four layers comprise a portion of said tow which has been hoop-wound at approximately 90° to said barrel section axis, the remaining layers comprising said helically-wound layers.
Claim 10
Dependent Claim
48 words
The barrel section of claim 8 including a plurality of longitudinally extending spiral rifling grooves within said section, said grooves being defined by a plurality of inwardly directed projections formed from elongated rovings of said tow and bound to said barrel section during the curing of said resin.
Claim 11
Independent Claim
163 words
A method of producing a barrel section for a lightweight weapon system subjected to high transient internal pressures and temperatures on firing, comprising the steps of: (a) preparing an epoxy resin-treated multi-filament carbon fibre material; (b) winding said material on a mandrel configured to the internal configuration of the desired barrel section to create initially at least one layer of said material configured to resist hot gas erosion on firing and subsequently a plurality of superimposed layers of a tow of said material helically wound about the at least one layer at a helix angle with respect to the mandrel axis of θ=tan -1 (σ axial /σ hoop ) where σ axial and σ hoop are the desired axial stresses respectively of the barrel section and winding the tow of material in sufficient thickness to provide a hoop stiffness equivalent to that of a steel barrel; (c) curing said superimposed layers of material; and (d) removing said mandrel from the cured barrel section.
Claim 12
Independent Claim
163 words
A method of producing a barrel section for a lightweight weapon system subjected to high transient internal pressures and temperatures on firing, comprising the steps of: (a) preparing an epoxy resin-treated multi-filament carbon fibre material; (b) winding said material on a mandrel configured to the internal configuration of the desired barrel section to create initially at least one layer of said material configured to resist hot gas erosion on firing and subsequently a plurality of superimposed layers of a tow of said material helically wound about the at least one layer at a helix angle with respect to the mandrel axis of θ=tan -1 (σ axial /σ hoop ) where σ axial and σ hoop are the desired axial stresses respectively of the barrel section and winding the tow of material in sufficient thickness to provide a hoop stiffness equivalent to that of a steel barrel; (c) curing said superimposed layers of material; and (d) removing said mandrel from the cured barrel section.
Claim 13
Dependent Claim
18 words
The method of claim 10 wherein said gas erosion resisting layer comprises a fabric formed from said material.
Claim 14
Dependent Claim
22 words
The method of claim 10, wherein said helix angle θ is in the range of 70° to 78° to said mandrel axis.
Claim 15
Dependent Claim
17 words
The method of claim 10, wherein said helix angle θ is approximately 71° to said mandrel axis.
Claim 16
Dependent Claim
36 words
The method of claim 10 including the step of machining a plurality of external threads in the outer surface of said barrel section adjacent one end thereof, for connection to a breech portion of said firearm.
Claim 17
Dependent Claim
55 words
The method of claim 10, comprising the step of, during step (b) decreasing the axial length of succeeding helically wound layers from adjacent a muzzle end of said barrel section whereby the external diameter of said barrel section progressively increases from a minimum adjacent said muzzle end to a maximum adjacent the other end thereof.
Claim 18
Dependent Claim
33 words
The method of claim 10, wherein the desired hoop stiffness of the barrel section is the product of the wall thickness and the modulus of elasticity of said material in the hoop direction.
Claim 19
Dependent Claim
34 words
The method of claim 10 wherein a portion of said tow is initially hoop-wound on said mandrel at about 90° to the mandrel axis to create at least four hot gas erosion resisting layers.
Claim 20
Dependent Claim
77 words
The method of claim 17 wherein said mandrel is generally cylindrical in cross-section and includes a plurality of circumferentially spaced apart and longitudinally extending spiral grooves in the outer surface thereof and, prior to step (b), a plurality of rovings of said tow is positioned to fill each such groove whereby during step (c) said rovings are bound to said hoop-wound layers of tow to create inwardly directed projections within said barrel section defining rifling grooves therebetween.
Claim 21
Dependent Claim
52 words
The method of claim 17 wherein step (a) includes the steps of winding a tow of multi-filament carbon-fibre material on a spool, positioning said spool adjacent a winding machine adapted to perform step (b), and passing said tow through epoxy-resin applying means as it is fed from said spool to said machine.
Claim 22
Dependent Claim
26 words
The method of claim 17 including the step of maintaining said tow under a tension of approximately 8 lbs as it is wound on said mandrel.
References Cited (Backward Citations)
US2847786A
Cited
US3298279A
Cited
US3517585A
Cited
FR1597423A
Cited
US3641870A
Cited
US4485721A
Cited
DE3212721A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-02 | 1990-09-01 | 1991-03-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-02 | 1994-09-01 | 1995-03-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-02 | 1998-09-01 | 1999-03-03 | $7700.00 | Window Closed / Lapsed |