Composite desiccant structure
Assignee: United States Department of Energy
•
Filing: 1985-12-30
•
Granted: 1987-02-24
•
Expires: 2005-12-30
Abstract
Abstract A composite formed of small desiccant particles retained in a dark matrix composed of a porous binder containing a transition metal oxide with pores to provide moisture transport with respect to the particles, and metallic fibers to remove the heat of condensation during dehumidification and provide heat for the removal of moisture during regeneration. The moisture absorbing properties of the composite may be regenerated by exposure of the dark matrix to solar radiation with dehumidification occurring at night.
Inventors
- 👤 Anthony V. Fraioli
- 👤 William W. Schertz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 10:42
CPC Classifications
F; F24; F24F; F24F3/00; F24F3/12; F24F3/14; F24F3/1411; B; B01; B01D; B01D53/00; B01D53/26; B01D53/261; F24F2203/00; F24F2203/10; F24F2203/1032; F24F2203/1036
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
126 words
A composite useful for dehumidifying purposes and comprising a matrix of a porous binder as a solid web containing a transition metal oxide having internal surfaces defining pores and a plurality of desiccant particles embedded in the matrix, the desiccant particles having diameters in the range of about 1-300 μm, constituting a major portion of the composite and being selected from the group consisting of silica gel, zeolite, alumina, activated carbon and mixtures thereof, the composite being in sheet-like form with exterior surfaces, a portion of the particles being below the exterior surfaces and covered by other particles, the transition metal oxide in the web being capable of transmitting moisture along the pore surfaces between desiccant particles and between the exterior surfaces and the desiccant particles.
Claim 2
Dependent Claim
126 words
A composite useful for dehumidifying purposes and comprising a matrix of a porous binder as a solid web containing a transition metal oxide having internal surfaces defining pores and a plurality of desiccant particles embedded in the matrix, the desiccant particles having diameters in the range of about 1-300 μm, constituting a major portion of the composite and being selected from the group consisting of silica gel, zeolite, alumina, activated carbon and mixtures thereof, the composite being in sheet-like form with exterior surfaces, a portion of the particles being below the exterior surfaces and covered by other particles, the transition metal oxide in the web being capable of transmitting moisture along the pore surfaces between desiccant particles and between the exterior surfaces and the desiccant particles.
Claim 3
Dependent Claim
47 words
The composite of claim 1 having a major surface and the matrix exposed over at least a major portion of said surface, the matrix being a light absorber and being heated when exposed to solar radiation to cause entrained moisture to be removed by desorption and evaporation.
Claim 4
Dependent Claim
25 words
The composite of claim 1 containing a minor amount of metallic fibers distributed in the matrix for heat transfer to and from the desiccant particles.
Claim 5
Dependent Claim
11 words
The composite of claim 3 wherein the desiccant is silica gel.
Claim 6
Dependent Claim
10 words
The composite of claim 3 wherein the desiccant is zeolite.
Claim 7
Dependent Claim
22 words
The composite of claim 1 wherein the transition metal oxide is manganese dioxide and the binder composition includes a rigid silicate web.
Claim 8
Dependent Claim
25 words
The composite of claim 6 containing a minor amount of metallic fibers distributed in the matrix for heat transfer to and from the desiccant particles.
Claim 9
Dependent Claim
23 words
The composite of claim 7 wherein the desiccant is silica gel with the particles having diameters in the range of about 1-150 μm.
Claim 10
Dependent Claim
19 words
The composite of claim 8 containing a minor amount of nonmetallic fibers distributed in the matrix for structural reinforcement.
Claim 11
Independent Claim
107 words
A method of producing a composite in sheet-like form useful for dehumidifying air comprising the steps of: providing a liquid binder containing a transition metal oxide, forming a mixture of the liquid binder composition and a plurality of desiccant particles embedded in the binder composition and having diameters in the range of about 1-300 μm, and treating the binder composition to form a binder in the form of rigid solid web containing the transition metal oxide and interconnecting the particles, the web and particles being in sheet-like form having exterior surfaces with a portion of the particles being below the exterior surfaces and covered by other particles.
Claim 12
Independent Claim
107 words
A method of producing a composite in sheet-like form useful for dehumidifying air comprising the steps of: providing a liquid binder containing a transition metal oxide, forming a mixture of the liquid binder composition and a plurality of desiccant particles embedded in the binder composition and having diameters in the range of about 1-300 μm, and treating the binder composition to form a binder in the form of rigid solid web containing the transition metal oxide and interconnecting the particles, the web and particles being in sheet-like form having exterior surfaces with a portion of the particles being below the exterior surfaces and covered by other particles.
Claim 13
Dependent Claim
28 words
The method of claim 10 wherein the forming step includes incorporating metallic fibers within the binder composition to provide heat transfer paths to and from the desiccant particles.
Claim 14
Dependent Claim
70 words
The method of claim 11, wherein the forming and treating steps form a first structure and the method further includes the steps of dividing the first structure into a plurality of second particles, forming a second mixture of said second particles and a second liquid binder composition, and treating the second binder composition to form a second binder in the form of a rigid solid web interconnecting the second particles.
Claim 15
Dependent Claim
32 words
The method of claim 12 wherein the forming of said second mixture includes incorporating metallic fibers within the second binder composition to provide heat transfer paths to and from the second particles.
Claim 16
Dependent Claim
56 words
The method of claim 13 wherein the forming of said second mixture includes incorporating heat degradable fibers in said second binder composition, and said method includes the step subsequent to the second treating step of heating the second mixture to remove at least a portion of the degradable fibers to form additional pores in the composite.
Claim 17
Dependent Claim
22 words
The method of claim 14 wherein the forming of said second mixture includes the step of incorporating metallic rods in the mixture.
References Cited (Backward Citations)
GB320450A
Cited
US2138689A
Cited
US2138690A
Cited
US2265389A
Cited
US2979157A
Cited
US2462952A
Cited
US2882243A
Cited
US2882244A
Cited
US2842223A
Cited
US3015368A
Cited
US3151951A
Cited
US3141729A
Cited
US3218367A
Cited
US3387767A
Cited
US3925248A
Cited
US3713281A
Cited
JPS4966592A
Cited
JPS5083290A
Cited
JPS5137091A
Cited
US4026680A
Cited
US4185969A
Cited
US4242112A
Cited
US4341539A
Cited
JPS5726331A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-23 | 1990-08-25 | 1991-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-23 | 1994-08-25 | 1995-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-23 | 1998-08-25 | 1999-02-24 | $7700.00 | Window Closed / Lapsed |