Assignee: Ashland LLC
•
Filing: 1986-03-04
•
Granted: 1987-02-17
•
Expires: 2006-03-04
Abstract
Abstract The process of this invention uses a single primer and a fast curing two component adhesive sealant to adhere automotive glass surfaces to coated metal surfaces.
Inventors
- 👤 Jeffrey W. Saracsan
- 👤 Stephen M. Oswalt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:03
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/061; B32B27/00; B32B27/04; B32B37/00; B32B37/12; B32B7/00; B32B7/04; B32B7/12; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; C08G18/70; C08G18/72; C08G18/77; C08G18/776; C09; C09J; C09J5/00; C09J5/02; B32B37/14; B32B37/24; B32B2037/243; B32B2605/00; B32B2605/006; C08G2190/00; C09J2400/00; C09J2400/10; C09J2400/16; C09J2400/166; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31554; Y10T428/31565
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
200 words
A method for joining and sealing a coated metal surface to a glass surface which comprises: (a) applying a primer to said metal surface and said glass surface, said primer comprising a dispersion of 10 to 20 parts by weight of a linear polyester resin, 4 to 5 parts by weight of a polyisocyanate cross-linking agent, 3 to 9 parts by weight of carbon black, and 66 to 83 parts by weight of a volatile organic solvent; (b) applying a sealant to either said primed glass surface or said primed coated metal surface, said sealant comprising a mixture of: (1) a prepolymer comprising a polyethylene oxide polypropylene oxide ether diol and diphenyl methane diisocyanate which has 3 to 15 percent free isocyanate groups; and (2) a curative comprising 20 to 40 parts by weight polyethylene oxide polypropylene oxide ether diol, 20 to 40 parts by weight polyethylene oxide polypropylene oxide ether triol, 15 to 60 parts by weight filler, 0.5 to 1.5 parts by weight diamine and catalytic amounts of an organotin catalyst, the weight ratio of said prepolymer to said curative ranging from 1:1 to 1:2, and (c) joining the metal and glass prepared in steps (a) and (b).
Claim 2
Independent Claim
200 words
A method for joining and sealing a coated metal surface to a glass surface which comprises: (a) applying a primer to said metal surface and said glass surface, said primer comprising a dispersion of 10 to 20 parts by weight of a linear polyester resin, 4 to 5 parts by weight of a polyisocyanate cross-linking agent, 3 to 9 parts by weight of carbon black, and 66 to 83 parts by weight of a volatile organic solvent; (b) applying a sealant to either said primed glass surface or said primed coated metal surface, said sealant comprising a mixture of: (1) a prepolymer comprising a polyethylene oxide polypropylene oxide ether diol and diphenyl methane diisocyanate which has 3 to 15 percent free isocyanate groups; and (2) a curative comprising 20 to 40 parts by weight polyethylene oxide polypropylene oxide ether diol, 20 to 40 parts by weight polyethylene oxide polypropylene oxide ether triol, 15 to 60 parts by weight filler, 0.5 to 1.5 parts by weight diamine and catalytic amounts of an organotin catalyst, the weight ratio of said prepolymer to said curative ranging from 1:1 to 1:2, and (c) joining the metal and glass prepared in steps (a) and (b).
Claim 3
Dependent Claim
36 words
The method of claim 1 wherein the prepolymer of step (b) comprises 40 to 60 parts polyethylene oxide polypropylene oxide ether diol, from 20 to 25 parts diphenyl methane diisocyanate and 15 to 40 parts filler.
Claim 4
Dependent Claim
84 words
The method of claim 2 wherein said primer comprises a dispersion of 15 parts linear polyester resin, 5 parts polyisocyanate, 6 parts carbon black and 74 parts volatile organic solvent, said prepolymer comprises 50 parts polyethylene oxide polypropylene oxide ether diol, 25 parts diphenyl methane diisocyanate and 25 parts filler and said curative comprises 30 parts polyethylene oxide polypropylene oxide ether diol, 30 parts polyethylene oxide polypropylene oxide ether triol, 0.8 parts piperazine, 0.1 parts dibutyltin dialkyl acid catalyst and 39.1 parts talc filler.
Claim 5
Dependent Claim
15 words
The method of claim 1 wherein the polyisocyanate crosslinking agent of step (a) is tris(p-isocyanato-phenyl)-thiophosphate.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein said coated metal surface is a clear enamel coated metal surface.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein said coated metal surface is a phenolic primer coated metal surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-16 | 1990-08-18 | 1991-02-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-16 | 1994-08-18 | 1995-02-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-16 | 1998-08-18 | 1999-02-17 | $7700.00 | Window Closed / Lapsed |