Olefin polymerization with polyphosphate supported chromium catalysts
Assignee: Phillips Petroleum Co
•
Filing: 1985-06-05
•
Granted: 1987-02-03
•
Expires: 2005-06-05
Abstract
Abstract A catalyst support based on aluminum polyphosphate or polyphosphoric acid-impregnated alumina is provided by two alternative techniques. In the first embodiment, an aluminum polyphosphate composition is heated in a dry atmosphere and thereafter impregnated with a zerovalent chromium component under anhydrous conditions. The resulting catalyst is active for olefin polymerization. In the second embodiment, alumina is impregnated with a polyphosphoric acid composition. This resulting polyphosphoric acid impregnated alumina can be used as a support for zerovalent chromium or can be impregnated with a chromium component and oxidized to give an active hexavalent chromium species. The resulting catalysts are advantageous because of their unusual sensitivity to hydrogen thus allowing great leeway in molecular weight control.
Inventors
- 👤 Marvin M. Johnson
- 👤 Max P. McDaniel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 23:30
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
63 words
A polymerization process comprising contacting at least one mono-1-olefin containing 2 to 8 carbon atoms per molecule under polymerization conditions with the catalyst comprising: a zerovalent organochromium compound on a predominantly aluminum polyphosphate support said zerovalent organochromium compound being present in an amount sufficient to give 0.001 to 10 weight percent chromium based on the weight of said support plus said chromium compound.
Claim 2
Dependent Claim
63 words
A polymerization process comprising contacting at least one mono-1-olefin containing 2 to 8 carbon atoms per molecule under polymerization conditions with the catalyst comprising: a zerovalent organochromium compound on a predominantly aluminum polyphosphate support said zerovalent organochromium compound being present in an amount sufficient to give 0.001 to 10 weight percent chromium based on the weight of said support plus said chromium compound.
Claim 3
Dependent Claim
11 words
A process according to claim 1 wherein said mono-1-olefin is ethylene.
Claim 4
Dependent Claim
25 words
A process according to claim 1 wherein said at least one mono-1-olefin comprises ethylene and a comonomer selected from propylene, 1-butene, 1-pentene, 1-hexene, and 1-octene.
Claim 5
Dependent Claim
15 words
A process according to claim 1 wherein said polymerization is carried out under slurry conditions.
Claim 6
Dependent Claim
52 words
A process according to claim 1 wherein said aluminum polyphosphate has a phosphorus to aluminum atom ratio within the range of 0.2 to 2, said organochromium compound being present in an amount sufficient to give 0.1 to 5 weight percent chromium based on the weight of said support plus said chromium compound.
Claim 7
Dependent Claim
53 words
A process according to claim 1 wherein said aluminum polyphosphate is a mixture comprising aluminum orthophosphate, aluminum pyrophosphate, aluminum triphosphate, aluminum tetraphosphate, and aluminum pentaphosphate, said chromium compound being present in an amount sufficient to give 0.1 to 5 weight percent chromium based on the weight of said support plus said chromium compound.
Claim 8
Dependent Claim
46 words
A process according to claim 1 wherein said zerovalent organochromium compound is a substituted or unsubstituted diarene chromium compound, said chromium compound being present in an amount sufficient to give 0.1 to 5 percent chromium based on the weight of said support plus said organochromium compound.
Claim 9
Dependent Claim
13 words
A process according to claim 7 wherein said organochromium compound is dicumene chromium.
Claim 10
Dependent Claim
76 words
A process according to claim 1 wherein said catalyst is used in conjunction with an organoaluminum or organoboron cocatalyst in an amount so as to give an atom ratio of aluminum or boron to chromium within the range of 0.1:1 to 10:1, said catalyst being further characterized by having said organochromium compound present in an amount sufficient to give 0.1 to 5 weight percent chromium based on the weight of said support plus said organochromium compound.
Claim 11
Dependent Claim
11 words
A process according to claim 9 wherein said cocatalyst is triethylborane.
Claim 12
Dependent Claim
47 words
A process according to claim 1 wherein said catalyst consists essentially of said organochromium compound and said aluminum polyphosphate, said organochromium compound being present in an amount sufficient to give 0.1 to 5 weight percent chromium based on the weight of said support plus said organochromium compound.
Claim 13
Dependent Claim
79 words
A process according to claim 1 wherein said aluminum polyphosphate has an atom ratio of phosphorus to aluminum within the range of 0.2 to 2, said aluminum polyphosphate is a mixture comprising aluminum orthophosphate, aluminum pyrophosphate, aluminum triphosphate, aluminum tetraphosphate, and aluminum pentaphosphate, and wherein said organochromium compound is dicumene chromium, said organochromium compound being present in an amount sufficient to give 0.1 to 5 weight percent chromium based on the weight of said support plus said organochromium compound.
References Cited (Backward Citations)
US2773921A
Cited
US2921081A
Cited
US4147758A
Cited
US4364841A
Cited
US4364842A
Cited
US4397765A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-02 | 1990-08-04 | 1991-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-02 | 1994-08-04 | 1995-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-02 | 1998-08-04 | 1999-02-03 | $7700.00 | Window Closed / Lapsed |