Metastable alloy materials produced by solid state reaction of compacted, mechanically deformed mixtures
Assignee: United States Department of Energy
•
Filing: 1984-08-31
•
Granted: 1987-02-03
•
Expires: 2004-08-31
Abstract
Abstract Bulk metastable, amorphous or fine crystalline alloy materials are produced by reacting cold-worked, mechanically deformed filamentary precursors such as metal powder mixtures or intercalated metal foils. Cold-working consolidates the metals, increases the interfacial area, lowers the free energy for reaction, and reduces at least one characteristic dimension of the metals. For example, the grains (13) of powder or the sheets of foil are clad in a container (14) to form a disc (10). The disc (10) is cold-rolled between the nip (16) of rollers (18,20) to form a flattened disc (22). The grains (13) are further elongated by further rolling to form a very thin sheet (26) of a lamellar filamentary structure (FIG. 4) containing filaments having a thickness of less than 0.01 microns. Thus, diffusion distance and time for reaction are substantially reduced when the flattened foil (28) is thermally treated in oven (32) to form a composite sheet (33) containing metastable material (34) dispersed in unreacted polycrystalline material (36).
Inventors
- 👤 Michael Atzmon
- 👤 William L. Johnson
- 👤 John D. Verhoeven
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:15
CPC Classifications
C; C22; C22C; C22C45/00; B; B22; B22F; B22F3/00; B22F3/006; B22F3/007; B22F2998/00; B22F2998/10; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/815; Y10S505/823; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
166 words
A method of forming solid, metastable, amporphous metal materials comprising the step of: forming a mixture of solid, metal precursors of the metastable, amorphous material, at least one of the precursors being in the form of individual, discrete, solid units and said mixture containing metals A and Z where A is an early transition metal selected from Group IIIB, IVB, or VB and Z is a late transition metal selected from Group VIIB, VIII or IB or the mixture is formed of a transition metal selected from IB, VIB, VIIB or VIII with a metalloid selected from Group IIIA, IVA, or VA; consolidating the mixture by cold working the consolidated mixture to reduce the thickness of the said discrete units of precursor by a factor of at least 10; and heating the cold-worked mixture at a temperature lower than the transformation temperature at which the metastable phase transforms into a more stable crystalline phase for a time sufficient to form a solid, metastable, amorphous, metal material.
Claim 2
Independent Claim
166 words
A method of forming solid, metastable, amporphous metal materials comprising the step of: forming a mixture of solid, metal precursors of the metastable, amorphous material, at least one of the precursors being in the form of individual, discrete, solid units and said mixture containing metals A and Z where A is an early transition metal selected from Group IIIB, IVB, or VB and Z is a late transition metal selected from Group VIIB, VIII or IB or the mixture is formed of a transition metal selected from IB, VIB, VIIB or VIII with a metalloid selected from Group IIIA, IVA, or VA; consolidating the mixture by cold working the consolidated mixture to reduce the thickness of the said discrete units of precursor by a factor of at least 10; and heating the cold-worked mixture at a temperature lower than the transformation temperature at which the metastable phase transforms into a more stable crystalline phase for a time sufficient to form a solid, metastable, amorphous, metal material.
Claim 3
Dependent Claim
31 words
A method according to claim 1 in which the metastable amorphous metal material is selected from YCu, YCo, YAu, YNi, YFe, ZrFe, ZrCu, ZrNi, ZrCo, TiNi, TiFe, TiCu, NbNi or AuLa.
Claim 4
Dependent Claim
24 words
A method according to claim 1 in which the unit is selected from the group consisting of films, foil, sheets, grains, spheres or rods.
Claim 5
Dependent Claim
31 words
A method according to claim 3 in which the mixture is cold-worked to reduce the thickness of at least one of the precursor units by a factor of at least 100.
Claim 6
Dependent Claim
25 words
A method according to claim 4 in which the mixture is cold-worked to deform at least one precursor unit into a lamellar or filamentary structure.
Claim 7
Dependent Claim
22 words
A method according to claim 5 in which the thickness of the lamella or filaments is reduced to 100 microns or less.
Claim 8
Dependent Claim
19 words
A method according to claim 6 in which the thickness of the lamella is no more than 10 microns.
Claim 9
Dependent Claim
19 words
A method according to claim 7 in which the thickness of the lamella is no more than 1 micron.
Claim 10
Dependent Claim
18 words
A method according to claim 1 in which the consolidatedd assembly is covered with an inert, deformable container.
Claim 11
Dependent Claim
16 words
A method according to claim 1 in which the container is a layer of metal cladding.
Claim 12
Dependent Claim
16 words
A method according to claim 1 in which the heating is conducted in an inert environment.
Claim 13
Dependent Claim
31 words
A method according to claim 11 in which the ratio of the rate of forming metastable material to the rate of forming stable crystalline phases is at least 10 2 .
Claim 14
Dependent Claim
16 words
A method according to claim 12 in which said ratio is at least 10 4 .
Claim 15
Dependent Claim
23 words
A method according to claim 3 in which the assembly comprises grains of metals having a particle size of 10 to 100 microns.
Claim 16
Dependent Claim
19 words
A method according to claim 3 in which the discrete units are in the form of foils or powders.
References Cited (Backward Citations)
US3473217A
Cited
US4362582A
Cited
US3681063A
Cited
US3733692A
Cited
US3815224A
Cited
US3876473A
Cited
US4094059A
Cited
US4093453A
Cited
US4148669A
Cited
US4285740A
Cited
US4224735A
Cited
US4250229A
Cited
US4431604A
Cited
US4564396A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-02 | 1990-08-04 | 1991-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-02 | 1994-08-04 | 1995-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-02 | 1998-08-04 | 1999-02-03 | $7700.00 | Window Closed / Lapsed |