US4640766A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the preparation of hydrocarbons
Assignee: Shell USA Inc
•
Filing: 1985-04-19
•
Granted: 1987-02-03
•
Expires: 2005-04-19
Abstract
Abstract C 4 - hydrocarbons are converted into syngas with a H 2 /CO molar ratio between 0.25 and 2.25 by reforming at a pressure above 10 bar in the presence of specified amounts of carbon dioxide and steam followed by conversion of the syngas into C 5 + hydrocarbons over a cobalt-containing catalyst or a catalyst combination comprising a cobalt-containing catalyst and having CO-shift activity.
Inventors
- 👤 Martin F. M. Post
- 👤 Swan T. Sie
- 👤 Ernst J. R. Sudholter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 10:46
CPC Classifications
C; C01; C01B; C01B3/00; C01B3/02; C01B3/32; C01B3/34; C07; C07C; C07C1/00; C07C1/02; C07C1/04; C07C1/0425; C07C1/043; C07C1/0435; C07C1/0455; C07C1/046; C07C1/0485; C07C2521/00; C07C2521/02; C07C2521/04; C07C2521/06; C07C2521/08; C07C2521/12; C07C2523/00; C07C2523/16; C07C2523/24; C07C2523/26; C07C2523/70; C07C2523/74; C07C2523/75; Y; Y02; Y02P; Y02P30/00; Y02P30/20; Y10; Y10S; Y10S208/00; Y10S208/95
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
232 words
A process for the preparation of C 5 + hydrocarbons suitable for the production of middle distillates from C 4 - hydrocarbons comprising: (a) reforming C 4 - hydrocarbons at a pressure higher than 10 bar in the presence of carbon dioxide and steam into a mixture of carbon monoxide and hydrogen having a H 2 /CO molar ratio between 0.25 and 2.25 by using a carbon dioxide/hydrocarbon ratio (a) higher than 0.1, but lower than 10 g mol CO 2 /g atom C, a steam/hydrocarbon ratio (b) higher than 0.1, but lower than 1 g mol H 2 O/g atoms C and a carbon dioxide/steam ratio chosen such that (2×a+3×b)>3, and (b) converting the product of (a) into a mixture of hydrocarbons substantially consisting of C 5 + hydrocarbons by contacting it at a temperature of 105°-305° C. and a pressure, substantially corresponding with that used in the reforming, with a cobalt catalyst comprising 3-60 pbw of cobalt and 0.1-100 pbw of at least one other metal chosen from the group formed by zirconium, titanium, and chromium per 100 pbw silica, alumina or silica-alumina, wherein said catalyst has been prepared by kneading and/or impregnation, and that when the H 2 /CO mixture has a H 2 /CO molar ratio lower than 1.5, the cobalt catalyst is used in a catalyst mixture with a copper and zinc containing composition having CO-shift activity.
Claim 2
Dependent Claim
232 words
A process for the preparation of C 5 + hydrocarbons suitable for the production of middle distillates from C 4 - hydrocarbons comprising: (a) reforming C 4 - hydrocarbons at a pressure higher than 10 bar in the presence of carbon dioxide and steam into a mixture of carbon monoxide and hydrogen having a H 2 /CO molar ratio between 0.25 and 2.25 by using a carbon dioxide/hydrocarbon ratio (a) higher than 0.1, but lower than 10 g mol CO 2 /g atom C, a steam/hydrocarbon ratio (b) higher than 0.1, but lower than 1 g mol H 2 O/g atoms C and a carbon dioxide/steam ratio chosen such that (2×a+3×b)>3, and (b) converting the product of (a) into a mixture of hydrocarbons substantially consisting of C 5 + hydrocarbons by contacting it at a temperature of 105°-305° C. and a pressure, substantially corresponding with that used in the reforming, with a cobalt catalyst comprising 3-60 pbw of cobalt and 0.1-100 pbw of at least one other metal chosen from the group formed by zirconium, titanium, and chromium per 100 pbw silica, alumina or silica-alumina, wherein said catalyst has been prepared by kneading and/or impregnation, and that when the H 2 /CO mixture has a H 2 /CO molar ratio lower than 1.5, the cobalt catalyst is used in a catalyst mixture with a copper and zinc containing composition having CO-shift activity.
Claim 3
Dependent Claim
24 words
The process of claim 1, wherein said process is applied to a feed in which the C 4 - hydrocarbons substantially consist of methane.
Claim 4
Dependent Claim
15 words
The process of claim 1, wherein said process is applied to natural gas as feed.
Claim 5
Dependent Claim
17 words
The process of claim 1, wherein said process is applied to a carbon dioxide contaminated natural gas.
Claim 6
Dependent Claim
28 words
The process of claim 1, wherein the reforming is carried out at a temperature of 700°-1000° C., a pressure of 10-75 bar and by using a nickel-containing catalyst.
Claim 7
Dependent Claim
34 words
The process of claim 1, wherein at least part of the steam, carbon dioxide or mixtures thereof present in the reaction products of (b) is separated therefrom and is recycled to the reforming step.
Claim 8
Dependent Claim
49 words
The process of claim 1, wherein the reforming is carried out by using a carbon dioxide/hydrocarbon ratio higher than 0.3 and lower than 4 g mol CO 2 /g atom C, and a steam/hydrocarbon ratio higher than 0.2 and lower than 0.8 g mol H 2 O/g atom C.
Claim 9
Dependent Claim
65 words
The process of claim 1, wherein the cobalt catalyst satisfies the relation: (3+4R)>(L/S)>(0.3+0.4R), wherein L=the total quantity of cobalt present on the catalyst, expressed as mg Co/ml catalyst, S=the surface area of the catalyst, expressed as m 2 /ml catalyst, and R=the weight ratio of the quantity of cobalt deposited on the catalyst by kneading to the total quantity of cobalt present on the catalyst.
Claim 10
Dependent Claim
73 words
The process of claim 1, wherein 100 ppw of carrier the cobalt catalyst comprises 15-50 ppw of cobalt and either 0.1-5 ppw of at least one other metal chosen from the group formed by zirconium, titanium and chromium if during its preparation cobalt is deposited first and said other metal next, or 5-40 ppw of at least one other metal if during its preparation said other metal is deposited first and cobalt next.
Claim 11
Dependent Claim
18 words
The process of claim 1, wherein the cobalt catalyst comprises zirconium as other metal and silica as carrier.
Claim 12
Dependent Claim
16 words
The process of claim 1, wherein (b) is carried out at a pressure of 10-100 bar.
Claim 13
Dependent Claim
21 words
The process of claim 1, wherein (b) is carried out at a temperature of 175°-275° C. and pressure of 10-75 bar.
Claim 14
Dependent Claim
106 words
The process as claimed in claim 1, wherein in the reforming a H 2 /CO mixture is obtained which has a H 2 /CO molar ratio (F) between 0.25 and 1.0 and that (b) is carried out by contacting this H 2 /CO mixture with a mixture of two catalysts, one of which is the cobalt catalyst and the other a copper and zinc containing composition having a Cu/Zn atomic ratio between 0.1 and 10, whereby in said catalyst mixture the two catalysts are present in a ratio so as to satisfy the relation ##EQU4## wherein M represents the (Cu+Zn)/Co atomic ratio in the catalyst mixture.
Claim 15
Dependent Claim
20 words
The process of claim 13, wherein the copper- and zinc-containing composition has a Cu/Zn atomic ratio between 0.25 and 4.0.
Claim 16
Dependent Claim
126 words
The process of claim 1, wherein in the reforming, a H 2 /CO mixture is obtained which has a H 2 /CO molar ratio (F) between 0.75 and 1.75 and that (b) is carried out in two steps by partly converting this H 2 /CO mixture in the first step over the cobalt catalyst under such conditions as to satisfy the relation ##EQU5## wherein C represents the H 2 +CO conversion as %mol, and after removal of the water formed in the first step of (b), at least the unconverted H 2 and CO are contacted in a second step with a catalyst or catalyst combination which in addition to activity for the conversion of a H 2 /CO mixture into hydrocarbons has a CO-shift activity.
Claim 17
Dependent Claim
46 words
The process of claim 15, wherein in the second step of (b) use is made of a mixture of two catalysts, one of which is the cobalt catalyst and the other a copper and zinc containing composition having a Cu/Zn atomic ratio between 0.1 and 10.
Claim 18
Dependent Claim
43 words
The process of claim 15, wherein in the second step of the hydrocarbon synthesis, use is made of a catalyst mixture in which the two catalysts are present such that the (Cu/Zn)/Co atomic ratio in the catalyst mixture lies between 0.5 and 5.
Claim 19
Dependent Claim
21 words
The process of claim 15, wherein the copper and zinc containing composition has a Cu/Zn atomic ratio between 0.25 and 4.
Claim 20
Dependent Claim
71 words
The process of claim 1, wherein in order to prepare middle distillates from the products prepared over the cobalt catalyst at least the part of said products whose initial boiling point lies above the final boiling point of the heaviest said middle distillates is subjected to hydrocracking by contacting it at elevated temperature and pressure with a catalyst containing one or more noble metals from Group VIII supported on a carrier.
Claim 21
Dependent Claim
27 words
The process of claim 19, wherein in the hydrocracking use is made of a catalyst containing 0.2-2 %w of one or more noble metals from Group VIII.
Claim 22
Dependent Claim
27 words
The process of claim 20, wherein in the hydrocracking use is made of a catalyst containing 0.2-1 %w of one or more noble metals from Group VIII.
Claim 23
Dependent Claim
28 words
The process of claim 19, wherein in the hydrocracking use is made of a catalyst containing platinum or palladium as Group VIII noble metal and silica-alumina as carrier.
Claim 24
Dependent Claim
23 words
The process of claim 19, wherein the hydrocracking is carried out at a temperature of 200°-400° C. and a pressure of 5-100 bar.
Claim 25
Dependent Claim
23 words
The process of claim 23, wherein the hydrocracking is carried out at a temperature of 250°-350° C. and a pressure of 10-75 bar.
References Cited (Backward Citations)
US3904744A
Cited
US4098339A
Cited
US4279830A
Cited
US4492772A
Cited
US4499209A
Cited
US4471145A
Cited
US4500417A
Cited
US4522939A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-02 | 1990-08-04 | 1991-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-02 | 1994-08-04 | 1995-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-02 | 1998-08-04 | 1999-02-03 | $7700.00 | Window Closed / Lapsed |