Assignee: CTS Corp
•
Filing: 1985-03-14
•
Granted: 1987-01-27
•
Expires: 2005-03-14
Abstract
Abstract This invention relates to thick film base metal resistive paints for firing on a substrate to form a resistor having a temperature coefficient of resistance within ±100 ppm/°C., while providing a means to selectively blend the resistive paint to provide a wide range of decade resistivities from less than 10 ohms/square to more than 1K ohms/square. The sheet resistance and TCR are controlled by mixing a glass frit from at least one of a first and second glass material; with TiSi 2 ; and at least one of Ti 5 Si 3 and AL 2 O 3 ; and a screening agent, for subsequent screening onto a substrate and firing in an inert atmosphere at a peak temperature of about 900° C. The first glass material comprises, by weight, 5 to 10% SiO 2 ; 30 to 50% BaO; 40 to 60% B 2 O 3 and 1 to 5% CuO. The second glass material comprises, by weight, 50 to 70% B 2 O 3 ; 25 to 45% SrO; and 2 to 10% SiO 2 . The quantity of the glass material is increased to raise sheet resistance in ohms per square, and to lower the value of the TCR. The quantity of TiSi 2 is increased to lower sheet resistance in ohms per square, and to raise the TCR. The quantity to TiSi 2 is increased to lower sheet resistance in ohms per square, and to raise the TCR. The quantity of Ti 5 Si 3 is increased to lower the sheet resistance in ohms per square, and to lower the TCR. The quantity of Al 2 O 3 is increased to raise the sheet resistance in ohms per square, and to lower the TCR. The screening agent preferably has no carbon residue when pyrolytically decomposed during firing in an inert atmosphere.
Inventors
- 👤 Charles C. Y. Kuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:18
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/06; C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/064; C03C8/00; C03C8/22; C04; C04B; C04B41/00; C04B41/45; C04B41/50; C04B41/5053; C04B41/5062; C04B41/5071; C04B41/80; C04B41/81; C04B41/85; C04B41/87; H01C17/00; H01C17/06; H01C17/065; H01C17/06506; H01C17/06513; H01C17/0656; H01C17/06573; H01C17/0658; H01C17/22; H01C17/232; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49099; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24926
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
184 words
A base metal resistor paint having a controlled sheet resistance and TCR, which comprises: (a) mixing a glass frit selected from a quantity of at least one of a first and second glass material, the first glass material comprising 5 to 10% SiO 2 , 30 to 50% BaO, 40 to 60% B 2 O 3 and 1 to 5% CuO; and the second glass material comprising 50 to 70% B 2 O 3 , 25 to 40% SrO, and 2 to 10% SiO 2 ; (b) mixing 45 to 60% of the glass frit with from 10 to 30% of a mixture comprising TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 ; and (c) blending the glass frit and the mixture of TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 with from 18 to 35% of a screening agent to form a resistor paint therefrom, for subsequent screening upon a substrate and firing in an inert atmosphere to form a resistor exhibiting controlled sheet resistance and TCR.
Claim 2
Dependent Claim
184 words
A base metal resistor paint having a controlled sheet resistance and TCR, which comprises: (a) mixing a glass frit selected from a quantity of at least one of a first and second glass material, the first glass material comprising 5 to 10% SiO 2 , 30 to 50% BaO, 40 to 60% B 2 O 3 and 1 to 5% CuO; and the second glass material comprising 50 to 70% B 2 O 3 , 25 to 40% SrO, and 2 to 10% SiO 2 ; (b) mixing 45 to 60% of the glass frit with from 10 to 30% of a mixture comprising TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 ; and (c) blending the glass frit and the mixture of TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 with from 18 to 35% of a screening agent to form a resistor paint therefrom, for subsequent screening upon a substrate and firing in an inert atmosphere to form a resistor exhibiting controlled sheet resistance and TCR.
Claim 3
Dependent Claim
38 words
The paint of claim 1, in which the quantity of at least one of the first and second glass material is increased to raise sheet resistance in ohms per square, and to lower the value of the TCR.
Claim 4
Dependent Claim
27 words
The paint of claim 1, in which the quantity of TiSi 2 is increased to lower sheet resistance in ohms per square, and to raise the TCR.
Claim 5
Dependent Claim
30 words
The paint of claim 1, in which the quantity of Al 2 O 3 is increased to raise the sheet resistance in ohms per square, and to lower the TCR.
Claim 6
Dependent Claim
30 words
The paint of claim 1, in which the quantity of Ti 5 Si 3 is increased to lower the sheet resistance in ohms per square, and to lower the TCR.
Claim 7
Dependent Claim
53 words
The paint of claim 1, in which the ratio of Al 2 O 3 to TiSi 2 is from 0 to 10%; the ratio of Ti 5 Si 3 to TiSi 2 is from 0 to 75%; and the ratio of the resulting mixture to the glass frit is from 15 to 40%.
Claim 8
Dependent Claim
24 words
The paint of claim 1, in which the glass frit is ground to a particle size of less than 10 microns, prior to mixing.
Claim 9
Dependent Claim
21 words
The paint of claim 1, in which the screening agent forms no carbon residue when pyrolytically decomposed in an inert atmosphere.
Claim 10
Dependent Claim
16 words
The paint of claim 1, in which a binding resin is present in the screening agent.
Claim 11
Dependent Claim
32 words
The mixture of claim 1, in which 18 to 35% screening agent is added to the mixture to yield a consistent resistive paint for screening printing onto a substrate prior to firing.
Claim 12
Dependent Claim
16 words
The paint of claim 1, in which the temperature coefficient of resistance is within ±100 ppm/°C.
Claim 13
Dependent Claim
24 words
The paint of claim 1, in which the TiSi 2 is ground to a particle size of less than 10 microns prior to mixing.
Claim 14
Dependent Claim
35 words
The paint of claim 1, in which at least one of the Ti 5 Si 3 and Al 2 O 3 are ground to a particle size of less than 10 microns, prior to mixing.
Claim 15
Dependent Claim
26 words
A base metal resistor paint of claim 1, wherein the resistor paint is screened upon a substrate and fired at a peak temperature of 900°±20° C.
Claim 16
Independent Claim
211 words
A method for preparing a base metal resistive paint for screening upon a substrate to form a resistive pattern thereon, which comprises: (a) mixing from 45 to 65% of a glass frit from at least one of a first and second glass material, the first glass material comprising 5 to 10% SiO 2 , 30 to 50% BaO, 40 to 60% B 2 O 3 and 1 to 5% CuO, and a second glass material comprising 50 to 70% B 2 O 3 , 25 to 40% SrO, and 2 to 10% SiO 2 ; (b) mixing from 45% to 65% of the glass frit with from 10 to 30% of a mixture comprising TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 ; (c) blending the glass frit and the mixture of TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 with from 18 to 35% of a screening agent having no carbon residue when pyrolytically decomposed in an inert atmosphere; (d) screening the resistive paint thus made onto a substrate; (e) drying the screened substrate in air; and (f) firing the screened substrate in an inert atmosphere at a peak temperature of 900° C.±20° C.
Claim 17
Independent Claim
211 words
A method for preparing a base metal resistive paint for screening upon a substrate to form a resistive pattern thereon, which comprises: (a) mixing from 45 to 65% of a glass frit from at least one of a first and second glass material, the first glass material comprising 5 to 10% SiO 2 , 30 to 50% BaO, 40 to 60% B 2 O 3 and 1 to 5% CuO, and a second glass material comprising 50 to 70% B 2 O 3 , 25 to 40% SrO, and 2 to 10% SiO 2 ; (b) mixing from 45% to 65% of the glass frit with from 10 to 30% of a mixture comprising TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 ; (c) blending the glass frit and the mixture of TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 with from 18 to 35% of a screening agent having no carbon residue when pyrolytically decomposed in an inert atmosphere; (d) screening the resistive paint thus made onto a substrate; (e) drying the screened substrate in air; and (f) firing the screened substrate in an inert atmosphere at a peak temperature of 900° C.±20° C.
Claim 18
Dependent Claim
25 words
The paint of claim 1, wherein the screened substrate is dried in air at a temperature of 100° C. to 150° C. prior to firing.
Claim 19
Dependent Claim
216 words
A thick film base metal resistor having a substrate with a a resistive paint screened and fired thereon, wherein the improvement comprises: (a) controllably blending a glass frit selected from at least one of a first and second glass material, the first glass material comprising 5 to 10% SiO 2 , 30 to 50% BaO, 40 to 60% B 2 O 3 and 1 to 5% CuO; and the second glass material comprising 50 to 70% B 2 O 3 , 25 to 45% SrO, and 2 to 10% SiO 2 ; (b) mixing 45 to 65% of the blended glass frit with 10 to 30% of a selected mixture comprising TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 ; (c) screening the resistive paint onto a substrate; (d) drying the screened substrate in air prior to firing; and (e) firing the screened substrate in an inert atmosphere at a peak firing temperature of approximately 900° C., wherein the selected quantity of the first and second glass material and the selected mixture of TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 , provide a means to control the sheet resistivity and the TCR of the base metal resistor made therefrom.
Claim 20
Dependent Claim
216 words
A thick film base metal resistor having a substrate with a a resistive paint screened and fired thereon, wherein the improvement comprises: (a) controllably blending a glass frit selected from at least one of a first and second glass material, the first glass material comprising 5 to 10% SiO 2 , 30 to 50% BaO, 40 to 60% B 2 O 3 and 1 to 5% CuO; and the second glass material comprising 50 to 70% B 2 O 3 , 25 to 45% SrO, and 2 to 10% SiO 2 ; (b) mixing 45 to 65% of the blended glass frit with 10 to 30% of a selected mixture comprising TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 ; (c) screening the resistive paint onto a substrate; (d) drying the screened substrate in air prior to firing; and (e) firing the screened substrate in an inert atmosphere at a peak firing temperature of approximately 900° C., wherein the selected quantity of the first and second glass material and the selected mixture of TiSi 2 and at least one of Ti 5 Si 3 and Al 2 O 3 , provide a means to control the sheet resistivity and the TCR of the base metal resistor made therefrom.
Claim 21
Dependent Claim
29 words
The resistor of claim 17, in which the quantity of the TiSi 2 is increased to lower the sheet resistance in ohms per square, and to increase the TCR.
Claim 22
Dependent Claim
43 words
The resistor of claim 17, in which the quantity of at least one of the second glass material, and the quantity of the A 2 O 3 is increased to raise the sheet resistance in ohms per square, and to lower the TCR.
Claim 23
Dependent Claim
52 words
The resistor of claim 17, in which the ratio of Al 2 O 3 to TiSi 2 is from 0 to 10%; the ratio of Ti 5 Si 3 to TiSi 2 is from 0 to 75%; and the ratio of the resulting mixture to glass frit is from 15 to 40%.
References Cited (Backward Citations)
US3027332A
Cited
US2891914A
Cited
US3498832A
Cited
US3661595A
Cited
US4039997A
Cited
GB1559523A
Cited
US4323484A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-26 | 1990-07-28 | 1991-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-26 | 1994-07-28 | 1995-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-26 | 1998-07-28 | 1999-01-27 | $7700.00 | Window Closed / Lapsed |