Abstract
Abstract A method of re-shaping polyimide and modified polyimide foam sheets into selected shapes. Polyimide foam sheets can be made by any of a number of methods, some of which produce sheets of selected thicknesses directly and others of which produce blocks or buns of foam which are sliced into sheets. A sheet is placed in a mold having the desired configuration, such as a half-pipe. The sheet is compressed to about 0 to 99% of the original thickness with heating of one or both major surfaces of the sheet to a temperature of from about 250° to 320° C. for about 0.5 to 5 minutes. Upon removal from the mold, the polyimide foam is found to be self-supporting and to have taken on the mold shape. A moisture impervious densified skin is found on the heated side(s).
Inventors
- 👤 John V. Long
- 👤 John Gagliani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:23
CPC Classifications
B; B29; B29B; B29B11/00; B29B11/14; B29B11/02; B29C; B29C44/00; B29C44/02; B29C44/04; B29C44/0407; B29C44/0446; B29C49/00; B29C49/071; B29C51/00; B29C51/002; B29C2949/00; B29C2949/07; B29C2949/0715; B29K; B29K2079/00; B29K2105/00; B29K2105/04; B29K2105/25; B29K2105/253; B29K2105/256; Y; Y10; Y10S; Y10S264/00; Y10S264/14; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249988; Y10T428/249989
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
127 words
The method of reshaping polyimide foam sheets which comprises the steps of: providing a sheet of polyimide foam; placing one major surface of said sheet into contact with a first mold surface; bringing a second mold surface at least into substantially complete contact with the second major surface of said sheet and compressing and reshaping the sheet; heating at least one major surface of said sheet to a temperature of from about 220° to 320° C. for about 0.5 to 5 minutes while allowing the balance of said sheet to remain at a lower temperature; and removing the reshaped foam sheet from the mold; whereby a self-sustaining foam structure having a higher density, moisture impervious, fire blocking and abrasion resistant skin on the heated foam surface results.
Claim 2
Independent Claim
127 words
The method of reshaping polyimide foam sheets which comprises the steps of: providing a sheet of polyimide foam; placing one major surface of said sheet into contact with a first mold surface; bringing a second mold surface at least into substantially complete contact with the second major surface of said sheet and compressing and reshaping the sheet; heating at least one major surface of said sheet to a temperature of from about 220° to 320° C. for about 0.5 to 5 minutes while allowing the balance of said sheet to remain at a lower temperature; and removing the reshaped foam sheet from the mold; whereby a self-sustaining foam structure having a higher density, moisture impervious, fire blocking and abrasion resistant skin on the heated foam surface results.
Claim 3
Dependent Claim
38 words
The method according to claim 1 wherein both major surfaces of said foam sheet are heated to a temperature of from about 220° to 320° C. and a higher density skin is formed on both major foam surfaces.
Claim 4
Dependent Claim
24 words
The method according to claim 1 wherein said foam sheets are provided by slicing sheets of uniform desired thickness from a thicker foam bun.
Claim 5
Dependent Claim
50 words
The method according to claim 1 wherein said foam sheet has discrete areas of greater thickness and said mold surfaces are spaced a substantially uniform distance apart, whereby the final reshaped foam product has substantially uniform thickness, with regions of higher density corresponding to the thicker original foam sheet areas.
Claim 6
Dependent Claim
51 words
The method according to claim 1 wherein said foam sheet has substantially uniform original thickness, and at least one of said mold surfaces has at least one raised area extending toward the other mold surface, whereby the final reshaped foam product has thinner, higher density areas corresponding to said raised areas.
Claim 7
Dependent Claim
163 words
In the method of preparing polyimide foam sheets having a desired configuration, which comprises the steps of reacting a tetracarboxylic acid dianhydride with an oxoimine in a solvent, adding a diamine, drying the solution to a powder, heating the powder in a mold to cause the powder to foam and produce a foam bun and slicing said bun into sheets having desired thicknesses, the improvement comprising the further steps of: placing one major surface of one of said sheets into contact with a first mold surface; bringing a second mold surface at least into substantially complete contact with a second major surface of said sheet and compressing and reshaping the sheet; heating at least one major surface of said sheet to a temperature of from about 220° to 320° C. for about 0.5 to 5 minutes; and removing the reshaped foam sheet from the mold; whereby a self-sustaining foam structure having a higher density, moisture impervious skin on the heated foam surface results.
Claim 8
Dependent Claim
163 words
In the method of preparing polyimide foam sheets having a desired configuration, which comprises the steps of reacting a tetracarboxylic acid dianhydride with an oxoimine in a solvent, adding a diamine, drying the solution to a powder, heating the powder in a mold to cause the powder to foam and produce a foam bun and slicing said bun into sheets having desired thicknesses, the improvement comprising the further steps of: placing one major surface of one of said sheets into contact with a first mold surface; bringing a second mold surface at least into substantially complete contact with a second major surface of said sheet and compressing and reshaping the sheet; heating at least one major surface of said sheet to a temperature of from about 220° to 320° C. for about 0.5 to 5 minutes; and removing the reshaped foam sheet from the mold; whereby a self-sustaining foam structure having a higher density, moisture impervious skin on the heated foam surface results.
Claim 9
Dependent Claim
38 words
The method according to claim 6 wherein both major surfaces of said foam sheet are heated to a temperature of from about 220° to 320° C. and a higher density skin is formed on both major foam surfaces.
Claim 10
Dependent Claim
24 words
The method according to claim 6 wherein said foam sheets are provided by slicing sheets of uniform desired thickness from a thicker foam bun.
Claim 11
Dependent Claim
50 words
The method according to claim 6 wherein said foam sheet has discrete areas of greater thickness and said mold surfaces are spaced a substantially uniform distance apart, whereby the final reshaped foam product has substantially uniform thickness, with regions of higher density corresponding to the thicker original foam sheet areas.
Claim 12
Dependent Claim
52 words
The method according to claim 6 wherein said foam sheet has substantially uniform original thickness, and at least one of said mold surfaces has at least one raised area extending toward to the other mold surface, whereby the final reshaped foam product has thinner, higher density areas corresponding to said raised areas.
Claim 13
Dependent Claim
190 words
In the method of preparing polyimide foam sheets having a desired configuration, which comprises the steps of reacting a tetracarboxylic acid dianhydride with a caprolactam in a mole ratio less than 1:1.5 in a solvent to produce an imidocaproic acid monomer, reacting said monomer with a diamine in a substantially stoichiometric ratio, drying the solution to a powder, heating said powder in a mold to cause it to foam and form a polyimide foam bun, removing said bun from said mold and slice it into foam sheets of desired thicknesses, the improvement comprising the further steps of: placing one major surface of one of said sheets into contact with a first mold surface; bringing a second mold surface at least into substantially complete contact with a second major surface of said sheet and compressing and reshaping the sheet; heating at least one major surface of said sheet to a temperature of from about 220° to 320° C. for about 0.5 to 5 minutes; and removing the reshaped foam sheet from the mold; whereby a self-sustaining foam structure having a higher density, moisture impervious skin on the heated foam surface results.
Claim 14
Dependent Claim
190 words
In the method of preparing polyimide foam sheets having a desired configuration, which comprises the steps of reacting a tetracarboxylic acid dianhydride with a caprolactam in a mole ratio less than 1:1.5 in a solvent to produce an imidocaproic acid monomer, reacting said monomer with a diamine in a substantially stoichiometric ratio, drying the solution to a powder, heating said powder in a mold to cause it to foam and form a polyimide foam bun, removing said bun from said mold and slice it into foam sheets of desired thicknesses, the improvement comprising the further steps of: placing one major surface of one of said sheets into contact with a first mold surface; bringing a second mold surface at least into substantially complete contact with a second major surface of said sheet and compressing and reshaping the sheet; heating at least one major surface of said sheet to a temperature of from about 220° to 320° C. for about 0.5 to 5 minutes; and removing the reshaped foam sheet from the mold; whereby a self-sustaining foam structure having a higher density, moisture impervious skin on the heated foam surface results.
Claim 15
Dependent Claim
38 words
The method according to claim 11 herein both major surfaces of said foam sheet are heated to a temperature of from about 220° to 320° C. and a higher density skin is formed on both major foam surfaces.
Claim 16
Dependent Claim
24 words
The method according to claim 11 wherein said foam sheets are provided by slicing sheets of uniform desired thickness from a thicker foam bun.
Claim 17
Dependent Claim
50 words
The method according to claim 11 wherein said foam sheet has discrete areas of greater thickness and said mold surfaces are spaced a substantially uniform distance apart, whereby the final reshaped foam product has substantially uniform thickness, with regions of higher density corresponding to the thicker original foam sheet areas.
Claim 18
Dependent Claim
52 words
The method according to claim 11 wherein said foam sheet has substantially uniform original thickness, and at least one of said mold surfaces has at least one raised area extending toward to the other mold surface, whereby the final reshaped foam product has thinner, higher density areas corresponding to said raised areas.
References Cited (Backward Citations)
US3484510A
Cited
US3553068A
Cited
US3534134A
Cited
US3518334A
Cited
US3534128A
Cited
US3554939A
Cited
US4265851A
Cited
US4315076A
Cited
US4361453A
Cited
US4394464A
Cited
US4407980A
Cited
US4476254A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-26 | 1990-07-28 | 1991-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-26 | 1994-07-28 | 1995-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-26 | 1998-07-28 | 1999-01-27 | $7700.00 | Window Closed / Lapsed |