Method for improving the adhesion of elastomers to a coated substrate
Assignee: Wacker Chemie AG
•
Filing: 1985-04-05
•
Granted: 1987-01-20
•
Expires: 2005-04-05
Abstract
Abstract A method for improving the adhesion of elastomers derived from compositions which are crosslinked by a condensation reaction and which are based on diorganopolysiloxanes containing rod-shaped copolymers formed by the free-radical copolymerization of styrene and (meth)acrylic acid ester in the presence of the diorganopolysiloxanes, to an undercoating consisting of an epoxy resin and pitch or tar, which comprises applying a primer having SiC-bonded organic groups to the undercoating prior to the application of the crosslinkable composition, in which the primer consists of a solution of (a) a copolymer of a (meth)acrylic acid ester free of silicon atoms and a (meth)acryloxyalkylsilane containing at least one SiOC-bonded monovalent organic group; and (b) a silane which contains a SiC-bonded organic group having at least one amino or imino group and which contains at least one SiOC-bonded monovalent organic group and/or a partial hydrolyzate of such silane in an organic solvent.
Inventors
- 👤 Karl-Heinrich Wegehaupt
- 👤 Hans-Rudolf Pfeffer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:51
CPC Classifications
C; C09; C09D; C09D151/00; C09D151/08; C09D151/085; C09D143/00; C09D143/04; C09D5/00; C09D5/16; C09D5/1693; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
140 words
A method for improving the adhesion of elastomers derived from compositions which are crosslinked by a condensation reaction and are based on diorganopolysiloxanes containing rod-shaped copolymers formed by the free-radical copolymerization of styrene and (meth)acrylic acid ester in the presence of the diorganopolysiloxanes, to an undercoating based on epoxy resin and pitch or tar, which comprises applying to the undercoating a primer composition containing in an organic solvent, (a) a copolymer of a (meth)acrylic acid ester free of silicon atoms and a (meth)acryloxyalkylsilane having at least one SiOC-bonded monovalent organic group; and (b) a silane which contains a SiC-bonded organic group having at least one amino or imino group and which contains at least one SiOC-bonded monovalent organic group, or a partial hydrolyzate of such a silane, or mixtures thereof and thereafter applying a crosslinkable composition to said primer composition.
Claim 2
Independent Claim
140 words
A method for improving the adhesion of elastomers derived from compositions which are crosslinked by a condensation reaction and are based on diorganopolysiloxanes containing rod-shaped copolymers formed by the free-radical copolymerization of styrene and (meth)acrylic acid ester in the presence of the diorganopolysiloxanes, to an undercoating based on epoxy resin and pitch or tar, which comprises applying to the undercoating a primer composition containing in an organic solvent, (a) a copolymer of a (meth)acrylic acid ester free of silicon atoms and a (meth)acryloxyalkylsilane having at least one SiOC-bonded monovalent organic group; and (b) a silane which contains a SiC-bonded organic group having at least one amino or imino group and which contains at least one SiOC-bonded monovalent organic group, or a partial hydrolyzate of such a silane, or mixtures thereof and thereafter applying a crosslinkable composition to said primer composition.
Claim 3
Dependent Claim
87 words
The method of claim 1, wherein the (meth)acrylic acid ester free of silicon atoms used in the formation of copolymer (a) has the formula (H.sub.2 C═CRCOO).sub.n R.sup.1 in which R is selected from the group consisting of hydrogen and the methyl group and R 1 is a hydrocarbon group which contains 1 to 10 carbon atoms, n is equal to 1 or 2, and when n is 1, R 1 is a monovalent hydrocarbon group and when n is 2, R 1 is a divalent hydrocarbon group.
Claim 4
Dependent Claim
84 words
The method of claim 1, wherein the (meth)acryloxyalkylsilane used in the formation of copolymer (a) has the formula H.sub.2 C═CRCOOR.sup.2 R.sup.3.sub.m Si(OR.sup.4).sub.3-m in which R is selected from the group consisting of hydrogen and the methyl group, R 2 is an alkylene group having from 1 to 6 carbon atoms, R 3 is a monovalent hydrocarbon group having from 1 to 6 carbon atoms, R 4 is an alkyl group having from 1 to 5 carbon atoms and m is 0, 1 or 2.
Claim 5
Dependent Claim
35 words
The method of claim 1, wherein from 4 to 20 parts by weight of (meth)acrylic acid ester free of silicon atoms are used per part by weight of (meth)acryloxyalkylsilane in the formation of copolymer (a).
Claim 6
Dependent Claim
97 words
The method of claim 1, wherein the silane (b) has the formula R.sup.5 NHR.sup.2 Si(OR.sup.6).sub.3 in which R 2 is an alkylene group having from 1 to 6 carbon atoms, R 5 is selected from the group consisting of hydrogen and a group having the formula H 2 N(CH 2 )p, where p is equal to 2 or 3 and R 6 is selected from the group consisting of a monovalent hydrocarbon group and a monovalent hydrocarbon group substituted by an amino or alkoxy group having a total of from 1 to 10 carbon atoms per group.
Claim 7
Dependent Claim
29 words
The method of claim 1, wherein the copolymer (a) is present in an amount of from 5 to 35 parts by weight per part by weight of silane (b).
Claim 8
Dependent Claim
16 words
The method of claim 1, wherein the organic solvent is a mixture containing toluene and isobutanol.
Claim 9
Dependent Claim
17 words
The method of claim 1, wherein the organic solvent is a mixture containing toluene, isobutanol and acetone.
Claim 10
Dependent Claim
148 words
A coated substrate having an epoxy resin and pitch or tar coating thereon, a primer having SiC-bonded organic groups over said epoxy resin and pitch or tar coat and an overcoat over said primer of a composition which is crosslinked to form an elastomer by a condensation reaction, in which the elastomer is based on diorganopolysiloxanes containing rod-shaped copolymers formed from the free-radical copolymerization of styrene and (meth)acrylic acid ester in the presence of the diorganopolysiloxanes, said primer is obtained from an organic solvent solution containing (a) a copolymer of a (meth)acrylic acid ester free of silicon atoms and a (meth)acryloxyalkylsilane having at least one SiOC-bonded monovalent organic group; and (b) a silane which contains a SiC-bonded organic group having at least one amino or imino group and which contains at least one SiOC-bonded monovalent organic group, or a partial hydrolyzate of such a silane, or mixtures thereof.
Claim 11
Dependent Claim
148 words
A coated substrate having an epoxy resin and pitch or tar coating thereon, a primer having SiC-bonded organic groups over said epoxy resin and pitch or tar coat and an overcoat over said primer of a composition which is crosslinked to form an elastomer by a condensation reaction, in which the elastomer is based on diorganopolysiloxanes containing rod-shaped copolymers formed from the free-radical copolymerization of styrene and (meth)acrylic acid ester in the presence of the diorganopolysiloxanes, said primer is obtained from an organic solvent solution containing (a) a copolymer of a (meth)acrylic acid ester free of silicon atoms and a (meth)acryloxyalkylsilane having at least one SiOC-bonded monovalent organic group; and (b) a silane which contains a SiC-bonded organic group having at least one amino or imino group and which contains at least one SiOC-bonded monovalent organic group, or a partial hydrolyzate of such a silane, or mixtures thereof.
Claim 12
Dependent Claim
88 words
The coated substrate of claim 9, wherein the (meth)acrylic acid ester free of silicon atoms used in the formation of copolymer (a) has the formula (H.sub.2 C═CRCOO).sub.n R.sup.1 in which R is selected from the group consisting of hydrogen and the methyl group and R 1 is a hydrocarbon group which contains 1 to 10 carbon atoms, n is equal to 1 or 2, and when n is 1, R 1 is a monovalent hydrocarbon group and when n is 2, R 1 is a divalent hydrocarbon group.
Claim 13
Dependent Claim
85 words
The coated substrate of claim 9, wherein the (meth)acryloxyalkylsilane used in the formation of copolymer (a) has the formula H.sub.2 C═CRCOOR.sup.2 R.sup.3.sub.m Si(OR.sup.4).sub.3-m in which R is selected from the group consisting of hydrogen and the methyl group, R 2 is an alkylene group having from 1 to 6 carbon atoms, R 3 is a monovalent hydrocarbon group having from 1 to 6 carbon atoms, R 4 is an alkyl group having from 1 to 5 carbon atoms and m is 0, 1 or 2.
Claim 14
Dependent Claim
36 words
The coated substrate of claim 9, wherein from 4 to 20 parts by weight of (meth)acrylic acid ester free of silicon atoms are used per part by weight of (meth)acryloxyalkylsilane in the formation of copolymer (a).
Claim 15
Dependent Claim
98 words
The coated substrate of claim 9, wherein the silane (b) has the formula R.sup.5 NHR.sup.2 Si(OR.sup.6).sub.3 in which R 2 is an alkylene group having from 1 to 6 carbon atoms, R 5 is selected from the group consisting of hydrogen and a group having the formula H 2 N(CH 2 )p, where p is equal to 2 or 3 and R 6 is selected from the group consisting of a monovalent hydrocarbon group and a monovlent hydrocarbon group substituted by an amino or alkoxy group having a total of from 1 to 10 carbon atoms per group.
Claim 16
Dependent Claim
30 words
The coated substrate of claim 9, wherein the copolymer (a) is present in an amount of from 5 to 35 parts by weight per part by weight of silane (b).
Claim 17
Dependent Claim
17 words
The coated substrate of claim 9, wherein the organic solvent is a mixture containing toluene and isobutanol.
Claim 18
Dependent Claim
18 words
The coated substrate of claim 9, wherein the organic solvent is a mixture containing toluene, isobutanol and acetone.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-19 | 1990-07-21 | 1991-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-19 | 1994-07-21 | 1995-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-19 | 1998-07-21 | 1999-01-20 | $7700.00 | Window Closed / Lapsed |