Abstract
Abstract In one embodiment of the present invention, silicon spheres are fabricated by applying a slurry of metallurgical grade silicon, or other suitable material, on the surface of a substrate capable of maintaining integrity beyond the melting point of silicon. The layer of metallurgical grade silicon is then patterned to provide regions of metallurgical grade silicon of uniform size. The substrate and metallurgical grade silicon are then heated beyond the melting point of silicon. The metallurgical grade silicon then beads to the surface as relatively pure silicon and forms silicon spheres due to the high cohesion of silicon. The structure is then cooled below the melting point of silicon and the silicon spheres then crystallize. The silicon spheres are then removed from the surface of the substrate and are further processed using techniques disclosed in copending U.S. patent application Ser. Nos. 647,551 and 647,578 to further purify the crystalline silicon spheres.
Inventors
- 👤 David E. Witter
- 👤 Jules D. Levine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:49
CPC Classifications
C; C30; C30B; C30B11/00; C30B11/002; B; B22; B22F; B22F1/00; B22F1/06; B22F1/065; C30B29/00; C30B29/60; Y; Y10; Y10S; Y10S117/00; Y10S117/915
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
133 words
A process for forming crystalline spheres of a crystallizable material, comprising the steps of: forming a layer of a paste of the crystallizable material on a planar surface of a substrate capable of withstanding temperatures in excess of the melting point of the crystallizable material; patterning said layer on the surface of said substrate; heating said patterned layer beyond the melting point of said crystallizable material and supplying an atmosphere which can react with said crystallizable material to form a coating that does not wet said layer thus causing said material to bead as coated spheres at the surface of said patterned layer; cooling said crystallizble material thus causing the beaded crystallizable material to crystallize into crystalline spheres; and removing said crystalline spheres from the surface of said patterned layer of crystallizable material.
Claim 2
Dependent Claim
133 words
A process for forming crystalline spheres of a crystallizable material, comprising the steps of: forming a layer of a paste of the crystallizable material on a planar surface of a substrate capable of withstanding temperatures in excess of the melting point of the crystallizable material; patterning said layer on the surface of said substrate; heating said patterned layer beyond the melting point of said crystallizable material and supplying an atmosphere which can react with said crystallizable material to form a coating that does not wet said layer thus causing said material to bead as coated spheres at the surface of said patterned layer; cooling said crystallizble material thus causing the beaded crystallizable material to crystallize into crystalline spheres; and removing said crystalline spheres from the surface of said patterned layer of crystallizable material.
Claim 3
Dependent Claim
12 words
A process as in claim 1 wherein said crystallizable material is silicon.
Claim 4
Dependent Claim
12 words
A process as in claim 1 wherein said substrate comprises silicon carbide.
Claim 5
Dependent Claim
28 words
A process as in claim 1 wherein said paste of crystallizable material is formed by depositing and patterning a slurry of crystallizable material using a silk screen process.
Claim 6
Dependent Claim
23 words
A process as in claim 1 wherein only the top surface of said layer of crystallizable material is patterned to provide nucleation sites.
Claim 7
Dependent Claim
36 words
A process as in claim 2 wherein said paste of silicon is formed on the surface of said substrate by mixing silicon powder and water, and applying the resulting compound to the surface of said substrate.
Claim 8
Dependent Claim
37 words
A process as in claim 2 wherein said paste of silicon is formed on the surface of said substrate by mixing silicon powder and isopropyl alcohol, and applying the resulting compound to the surface of said substrate.
Claim 9
Dependent Claim
37 words
A process as in claim 2 wherein said paste of silicon is formed on the surface of said substrate by mixing silicon powder and alpha terpineol, and applying the resulting compound to the surface of said substrate.
Claim 10
Dependent Claim
34 words
A process as in claim 2 wherein said patterning forms said layer into a plurality of approximately equal regions with each of said regions having a boundary with a single sharp corner for nucleation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-19 | 1990-07-21 | 1991-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-19 | 1994-07-21 | 1995-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-19 | 1998-07-21 | 1999-01-20 | $7700.00 | Window Closed / Lapsed |