Method for the preparation of a laminate
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1986-01-17
•
Granted: 1987-01-20
•
Expires: 2006-01-17
Abstract
Abstract A method is proposed for the preparation of a laminate with improved mechanical strength such as the cloth-to-cloth adhesive bonding strength using a prepreg based on a fabric sheet of aromatic polyamide fibers and an adhesive preferably selected from polyimide-based and epoxy resin-based adhesives, in which the fabric sheet is pretreated by exposure to low-temperature plasma of preferably a gas mixture composed of oxygen and nitrogen under a reduced pressure of 0.5 to 20 Torr. The improvement is derived presumably from the increase in the wettability and affinity of the fibers to the adhesive as is suggested by the remarkable increase of adhesive pick-up.
Inventors
- 👤 Susumu Ueno
- 👤 Kouiti Kuroda
- 👤 Hirokazu Nomura
- 👤 Shigeru Tateno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:32
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; B29; B29C; B29C59/00; B29C59/14; B32B38/00; B32B38/0008; B32B5/28; B32B7/00; B32B7/04; B32B7/12; C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; D; D06; D06M; D06M10/00; D06M10/02; D06M10/025; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/0353; H05K1/0366; B29C2059/147; B29C70/00; B29C70/04; B29C70/28; B29C70/30; B29C70/34; B29K; B29K2063/00; B29K2079/00; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2277/00; B29K2277/10; B29K2313/00; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/04; B32B2260/046; B32B2262/00; B32B2262/02; B32B2262/0261; B32B2310/00; B32B2310/08; B32B2310/0806; B32B2310/0868; D06M2101/00; D06M2101/16; D06M2101/30; D06M2101/34; D06M2101/36; D06M2200/00; D06M2200/50; H05K2201/00; H05K2201/01; H05K2201/0137; H05K2201/0154; H05K2201/02; H05K2201/0275; H05K2201/0278; H05K2203/00; H05K2203/09; H05K2203/095
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
145 words
A method for the preparation of a laminate based on fabric sheets of aromatic polyamide fibers which comprises the steps of: (a) subjecting the fabric sheet of the aromatic polyamide fibers to exposure to an atmosphere of low temperature plasma under continuous introduction of a plasma-supporting gas into the atmosphere under a gaseous pressure in the range from 0.05 to 20 Torr generated by impressing a high-frequency electric power between a grounded electrode and an input electrode; (b) impregnating the thus plasma-treated fabric sheet with a resinous binder selected from the group consisting of polyimide resins and epoxy resins to give a resin-impregnated prepreg sheet; (c) laying a plural number of the resin-impregnated prepreg sheets one on the other into a pile; and (d) pressing the pile of the resin-impregnated prepregs at an elevated temperature so as to convert the prepregs into an integral laminate.
Claim 2
Independent Claim
145 words
A method for the preparation of a laminate based on fabric sheets of aromatic polyamide fibers which comprises the steps of: (a) subjecting the fabric sheet of the aromatic polyamide fibers to exposure to an atmosphere of low temperature plasma under continuous introduction of a plasma-supporting gas into the atmosphere under a gaseous pressure in the range from 0.05 to 20 Torr generated by impressing a high-frequency electric power between a grounded electrode and an input electrode; (b) impregnating the thus plasma-treated fabric sheet with a resinous binder selected from the group consisting of polyimide resins and epoxy resins to give a resin-impregnated prepreg sheet; (c) laying a plural number of the resin-impregnated prepreg sheets one on the other into a pile; and (d) pressing the pile of the resin-impregnated prepregs at an elevated temperature so as to convert the prepregs into an integral laminate.
Claim 3
Dependent Claim
47 words
The method as claimed in claim 1 wherein the resinous binder is a polyimide resin and the resin pick-up in the prepreg is in the range from 50 to 250 parts by weight per 100 parts by weight of the fabric sheet of the aromatic polyamide fibers.
Claim 4
Dependent Claim
47 words
The method as claimed in claim 1 wherein the resinous binder is an epoxy resin and the resin pick-up in the prepreg is in the range from 40 to 150 parts by weight per 100 parts by weight of the fabric sheet of the aromatic polyamide fibers.
Claim 5
Dependent Claim
19 words
The method as claimed in claim 1 wherein the plasma-supporting gas is a gaseous mixture of nitrogen and oxygen.
Claim 6
Dependent Claim
33 words
The method as claimed in claim 4 wherein the mixing ratio of nitrogen and oxygen in the gaseous mixture of nitrogen and oxygen is in the range from 5:95 to 95:5 by volume.
Claim 7
Dependent Claim
57 words
The method as claimed in claim 1 wherein the distance between the surfaces of the grounded electrode and the input electrode is in the range from 30 to 500 mm and the high-frequency electric power impressed therebetween is in the range from 3 to 100 kilowatts per square meter of the surface area of the input electrode.
Claim 8
Dependent Claim
37 words
The method as claimed in claim 1 wherein the rate of introduction of the plasma-supporting gas is in the range from 0.002 to 0.2 liter/minute at N.T.P. per kilowatt of the electric power impressed between the electrodes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-19 | 1990-07-21 | 1991-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-19 | 1994-07-21 | 1995-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-19 | 1998-07-21 | 1999-01-20 | $7700.00 | Window Closed / Lapsed |