US4637839A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Treating autodeposited coating with Cr composition
Assignee: Henkel Corp
•
Filing: 1981-09-04
•
Granted: 1987-01-20
•
Expires: 2001-09-04
Abstract
Abstract In a process wherein a resinous coating is formed on a metallic surface by immersing the surface in an acidic aqueous coating composition containing dispersed particles of resin, wherein said composition forms on said surface a resinous coating which increases in thickness the longer the surface is immersed in the composition and wherein the resinous coating is contacted with an aqueous solution containing Cr to improve properties of the resinous coating, the improvement comprising contacting said resinous coating with an acidic aqueous solution prepared by combining a hexavalent Cr-containing compound, an aqueous mixture of hexavalent chromium/reduced chromium, and an acid or a soluble salt thereof.
Inventors
- 👤 Wilbur S. Hall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:07
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B05D7/142; B05D7/144; C; C09; C09D; C09D5/00; C09D5/08; C09D5/088
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
188 words
A coating process for forming on a metallic surface an autodeposited coating of the type which in fused form tends to have a glossy appearance comprising forming on the metallic surface an unfused autodeposited coating by contacting the metallic surface with an autodepositing coating composition comprising an aqueous acidic solution prepared from a ferric iron-containing compound and HF, and including dispersed resin particles, modifying the properties of the coating so that it has a uniformly matte appearance and improved corrosion resistance in its fused form by contacting the unfused coating with an acidic aqueous chromium-containing composition having a pH of no greater than about 4 and consisting essentially of the following dissolved ingredients: (A) ammonium, potassium or sodium dichromate in an amount equivalent to about 0.3 to about 3 g/l of Cr +6 ; (B) formaldehyde-reduced chromic acid in an amount equivalent to about 0.3 to about 3 g/l of chromium, with about 50 wt. % of the chromium being in reduced form; and (C) at least about 0.06 g of phosphoric acid for each gram of total chromium in said mix; and thereafter fusing the unfused coating.
Claim 2
Dependent Claim
188 words
A coating process for forming on a metallic surface an autodeposited coating of the type which in fused form tends to have a glossy appearance comprising forming on the metallic surface an unfused autodeposited coating by contacting the metallic surface with an autodepositing coating composition comprising an aqueous acidic solution prepared from a ferric iron-containing compound and HF, and including dispersed resin particles, modifying the properties of the coating so that it has a uniformly matte appearance and improved corrosion resistance in its fused form by contacting the unfused coating with an acidic aqueous chromium-containing composition having a pH of no greater than about 4 and consisting essentially of the following dissolved ingredients: (A) ammonium, potassium or sodium dichromate in an amount equivalent to about 0.3 to about 3 g/l of Cr +6 ; (B) formaldehyde-reduced chromic acid in an amount equivalent to about 0.3 to about 3 g/l of chromium, with about 50 wt. % of the chromium being in reduced form; and (C) at least about 0.06 g of phosphoric acid for each gram of total chromium in said mix; and thereafter fusing the unfused coating.
Claim 3
Dependent Claim
134 words
A coating process according to claim 1 wherein the coating composition used to form said autodeposited coating has a pH of about 1.6 to about 4 and comprises (A) about 50 to about 100 g/l of resin solids selected from the class consisting of resin particles prepared by polymerizing (1) a conjugated diene, (ii) CH 2 ═CH--R wherein R is an aryl or cyano group, (iii) a vinyl halide, and (iv) a monoethylenically unsaturated monomer having a functional group selected from the class consisting of amide and carboxylic groups; and resin particles which are substantially chemically and physically homogeneous; (B) ferric fluoride in an amount such that it contains the equivalent of about 0.5 to about 3.5 g/l of ferric iron; (C) about 0.2 to about 5 g/l of HF; and (D) black pigment.
Claim 4
Dependent Claim
31 words
A process according to claim 2 wherein said conjugated diene is butadiene, said CH 2 ═CHR is styrene, said vinyl halide is vinylidene chloride and said unsaturated monomer is methacrylic acid.
Claim 5
Dependent Claim
14 words
A process according to claim 3 wherein said metallic surface is a ferriferous surface.
Claim 6
Dependent Claim
14 words
A process according to claim 4 wherein said ferriferous surface is hot rolled steel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-19 | 1990-07-21 | 1991-01-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-19 | 1994-07-21 | 1995-01-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-19 | 1998-07-21 | 1999-01-20 | $7700.00 | Window Closed / Lapsed |