Method of repairing a defective photomask
Assignee: AT&T Inc
•
Filing: 1985-04-29
•
Granted: 1987-01-13
•
Expires: 2005-04-29
Abstract
Abstract A process of laser-induced metal deposition for repairing transparent defects (18) in patterned metal films (14) of photomasks (10). The process comprises the steps of (a) coating the surface (16) of the substrate (12) having the film (14) thereon with a layer of metal-organic compound (50); (b) exposing the portions of the layer of metal-organic compound (50) overlying the defects (18) to a beam (24) of electromagnetic radiation from a laser (22); (c) ramping the power level of the radiation beam (24) delivered by the laser (22) until a metal patch (52) is reflective and adherent is formed; and (d) removing the unexposed portions of metal-organic compound (50) remaining on the substrate surface (16).
Inventors
- 👤 Georgia J. Fisanick
- 👤 Michal E. Gross
- 👤 Gary L. Wolk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:16
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/68; G03F1/72; C; C03; C03C; C03C17/00; C03C17/06; C23; C23C; C23C14/00; C23C14/22; C23C14/24; C23C14/28; C23C16/00; C23C16/04; C23C16/047; C23C16/56; C23C4/00; C23C4/18; C03C2217/00; C03C2217/20; C03C2217/25; C03C2217/251; C03C2217/254; C03C2217/255; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112; C03C2218/114; C03C2218/119; C03C2218/30; C03C2218/32; C03C2218/34; H; H05; H05K; H05K3/00; H05K3/10; H05K3/105; H05K3/22; H05K3/225; Y; Y10; Y10S; Y10S148/00; Y10S148/14; Y10S430/00; Y10S430/146
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
62 words
A method of depositing metal on a substrate, comprising the steps of (a) applying a metal-organic compound to a substrate; (b) exposing the metal-organic compound to light radiation; and (c) ramping the power level of the light radiation delivered to the metal-organic compound to cause said compound to decompose to volatile components and a metal film which is adherent to the substrate.
Claim 2
Independent Claim
62 words
A method of depositing metal on a substrate, comprising the steps of (a) applying a metal-organic compound to a substrate; (b) exposing the metal-organic compound to light radiation; and (c) ramping the power level of the light radiation delivered to the metal-organic compound to cause said compound to decompose to volatile components and a metal film which is adherent to the substrate.
Claim 3
Independent Claim
72 words
A method of repairing an opening in an opaque film on a substrate, comprising the steps of: (a) coating the opening with a layer of metal-organic compound; (b) exposing the portion of the layer of metal-organic compound overlying the opening to a beam of light radiation; and (c) ramping the power level of the light radiation delivered to said portion to cause the portion to become opaque and adherent to the substrate.
Claim 4
Independent Claim
72 words
A method of repairing an opening in an opaque film on a substrate, comprising the steps of: (a) coating the opening with a layer of metal-organic compound; (b) exposing the portion of the layer of metal-organic compound overlying the opening to a beam of light radiation; and (c) ramping the power level of the light radiation delivered to said portion to cause the portion to become opaque and adherent to the substrate.
Claim 5
Dependent Claim
47 words
The method as set forth in claim 2 wherein the step of ramping comprises gradually increasing the power level of the radiation delivered to the portion to cause metal from the metal-organic compound to be deposited within the opening until the metal is completely opaque and adherent.
Claim 6
Dependent Claim
20 words
The method as set forth in claim 2 wherein the metal-organic compound decomposes with an exothermic overall heat of reaction.
Claim 7
Dependent Claim
49 words
The method as set forth in claim 2 wherein the step of ramping is characterized by ramping the power level to 50 square microns of the compound from 0 milliwatts to 15 milliwatts over a time period of 5 seconds when the substrate is a crown or borosilicate glass.
Claim 8
Dependent Claim
50 words
The method as set forth in claim 2 wherein the step of ramping is characterized by increasing the power level to 50 square microns of the compound from 0 milliwatts to 25 milliwatts over a time period of 5 seconds when the substrate is a fused quartz or fused silica.
Claim 9
Dependent Claim
18 words
The method as disclosed in claim 2 wherein the wavelength of the light radiation is 5145 Angstrom units.
Claim 10
Independent Claim
117 words
A method of repairing a transparent defect in a thin film photomask pattern comprising: (a) coating the surface of the photomask having the film thereon with a layer of metal-organic compound which decomposes with an exothermic overall heat of reaction; (b) exposing the portion of the layer of metal-organic compound overlying the defect to a beam of electromagnetic radiation from a laser for initiating the decomposition of the metal-organic compound; (c) ramping the power level of the radiation delivered by the laser so as to completely decompose the metal-organic compound whereby the organic portion is vaporized and the metal portion is deposited into the defect; and (d) removing the unexposed metal-organic compound remaining on the photomask surface.
Claim 11
Independent Claim
117 words
A method of repairing a transparent defect in a thin film photomask pattern comprising: (a) coating the surface of the photomask having the film thereon with a layer of metal-organic compound which decomposes with an exothermic overall heat of reaction; (b) exposing the portion of the layer of metal-organic compound overlying the defect to a beam of electromagnetic radiation from a laser for initiating the decomposition of the metal-organic compound; (c) ramping the power level of the radiation delivered by the laser so as to completely decompose the metal-organic compound whereby the organic portion is vaporized and the metal portion is deposited into the defect; and (d) removing the unexposed metal-organic compound remaining on the photomask surface.
Claim 12
Dependent Claim
48 words
The method as set forth in claim 8 wherein the step of ramping is characterized by ramping the power level to 50 square microns portion from 0 milliwatts to approximately 15 milliwatts over a time period of 5 seconds when the substrate is a crown or borosilicate glass.
Claim 13
Dependent Claim
50 words
The method as set forth in claim 8 wherein the step of ramping is characterized by ramping the power level to a 50 square micron portion from 0 milliwatts to approximately 25 milliwatts over a time period of 5 seconds when the substrate is a fused quartz or fused silica.
Claim 14
Dependent Claim
21 words
The method as disclosed in claim 8 wherein the wavelength of the electromagnetic radiation from the laser is 5145 Angstrom units.
Claim 15
Dependent Claim
17 words
The method as set forth in claim 8 wherein the metal-organic compound comprises a gold terpene mercaptide.
Claim 16
Dependent Claim
18 words
The method as set forth in claim 12 wherein the metal-organic compound is combined with a titanium resinate.
Claim 17
Dependent Claim
30 words
The method as set forth in claim 8, wherein the laser power delivered to a 50 square micron portion is at least 3.0 milliwatts per micron for a quartz substrate.
Claim 18
Dependent Claim
30 words
The method as set forth in claim 8, wherein the laser power delivered to a 50 square micron portion is at least 2.0 milliwatts per micron for a glass substrate.
References Cited (Backward Citations)
US2490399A
Cited
US2984575A
Cited
US4190759A
Cited
US4256778A
Cited
US4220510A
Cited
US4340617A
Cited
US4340654A
Cited
US4444801A
Cited
US4463073A
Cited
US4510222A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-12 | 1990-07-14 | 1991-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-12 | 1994-07-14 | 1995-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-12 | 1998-07-14 | 1999-01-13 | $7700.00 | Window Closed / Lapsed |