Process for manufacturing clad aluminum-lithium alloys
Assignee: Kaiser Aluminum and Chemical Corp
•
Filing: 1985-01-24
•
Granted: 1987-01-13
•
Expires: 2005-01-24
Abstract
Abstract A metallurgical bond at the interface between an aluminum-lithium core alloy and a metallic liner is achieved by first forming a mechanical bond along the interface between the core and liner under moderated temperature and reduction conditions, and then heating the composite without simultaneous reduction to cause diffusion of the elements across the core-liner interface. The result is a metallurgical bond securing the layers together to form a composite which can be worked, shaped, and fabricated by normal reduction techniques into a full range of products without the discoloration and fouling problems otherwise typical of aluminum-lithium alloys.
Inventors
- 👤 William R. Mohondro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 03:11
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/01; B32B15/016; B23; B23K; B23K20/00; B23K20/04; B23K20/22; B23K2103/00; B23K2103/08; B23K2103/10; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/12069; Y10T428/12076; Y10T428/12493; Y10T428/12736
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
134 words
A method for effecting a substantially uniform adhesion of substantially all of the contacting surfaces of a lithium-containing core alloy with a metallic liner material, comprising the steps of: (a) preparing opposed surfaces of said core alloy and said liner material by removing therefrom substantially all oxide materials; (b) contacting said prepared surfaces to form a composite and tacking together the leading edges of each of said prepared surfaces; (c) roll bonding said composite from said leading edges to obtain substantially uniform adhesion along said contacting surfaces while causing at most a 2% reduction of said core alloy, at a temperature of up to about 450° F.; and (d) heating said roll bonded composite to form a metallurgical bond between said core alloy and said liner material along substantially all of said contacting surfaces.
Claim 2
Independent Claim
134 words
A method for effecting a substantially uniform adhesion of substantially all of the contacting surfaces of a lithium-containing core alloy with a metallic liner material, comprising the steps of: (a) preparing opposed surfaces of said core alloy and said liner material by removing therefrom substantially all oxide materials; (b) contacting said prepared surfaces to form a composite and tacking together the leading edges of each of said prepared surfaces; (c) roll bonding said composite from said leading edges to obtain substantially uniform adhesion along said contacting surfaces while causing at most a 2% reduction of said core alloy, at a temperature of up to about 450° F.; and (d) heating said roll bonded composite to form a metallurgical bond between said core alloy and said liner material along substantially all of said contacting surfaces.
Claim 3
Dependent Claim
23 words
A method in accordance with claim 1 in which the temperature in step (c) is from about 300° F. to about 450° F.
Claim 4
Dependent Claim
23 words
A method in accordance with claim 1 in which the temperature in step (c) is from about 325° F. to about 425° F.
Claim 5
Dependent Claim
51 words
A method in accordance with claim 1 in which step (c) is achieved by a plurality of successive rolling passes beginning with a sufficient number of passes at a total composite reduction of less than about 2% to secure at least a portion of said liner material to said core alloy.
Claim 6
Dependent Claim
23 words
A method in accordance with claim 1 in which the reduction of said core alloy in step (c) is at most about 1.5%.
Claim 7
Dependent Claim
36 words
A method in accordance with claim 1 in which step (d) is done at a temperature of from about 600° F. to about 1200° F. for at least about one hour per inch of composite thickness
Claim 8
Dependent Claim
36 words
A method in accordance with claim 1 in which step (d) is done at a temperature of from about 800° F. to about 1100° F. for at least about one hour per inch of composite thickness.
Claim 9
Dependent Claim
36 words
A method in accordance with claim 1 in which step (d) is done at a temperature of from about 800° F. to about 1100° F. for at least about three hours per inch of composite thickness.
Claim 10
Dependent Claim
28 words
A process according to claim 1 further comprising hot rolling said composite subsequent to step (d) at a temperature of from about 600° F. to about 1200° F.
Claim 11
Dependent Claim
28 words
A process according to claim 1 further comprising hot rolling said composite subsequent to step (d) at a temperature of from about 800° F. to about 1100° F.
Claim 12
Independent Claim
173 words
A method for cladding a lithium-containing aluminum core alloy with a metallic liner material at least about 0.02 inch thick to form a composite of which said liner material comprises from about 1.5% to about 15% per side of the thickness thereof, said method comprising: (a) preparing opposed surfaces of said core alloy and said liner material by removing therefrom substantially all oxide materials; (b) contacting said prepared surfaces to form a composite and tacking together the leading edges of each of said prepared surfaces; (c) roll bonding said composite from said leading edges to obtain substantially uniform adhesion along said contacting surfaces while causing at most a 15% reduction of said core alloy, at a temperature of up to about 425° F.; and (d) heating said roll bonded composite to a temperature of from about 800° F. to about 1100° F. for at least about three hours per inch of composite thickness to form a metallurgical bond between said core alloy and said liner material along substantially all of said contacting surfaces.
Claim 13
Independent Claim
173 words
A method for cladding a lithium-containing aluminum core alloy with a metallic liner material at least about 0.02 inch thick to form a composite of which said liner material comprises from about 1.5% to about 15% per side of the thickness thereof, said method comprising: (a) preparing opposed surfaces of said core alloy and said liner material by removing therefrom substantially all oxide materials; (b) contacting said prepared surfaces to form a composite and tacking together the leading edges of each of said prepared surfaces; (c) roll bonding said composite from said leading edges to obtain substantially uniform adhesion along said contacting surfaces while causing at most a 15% reduction of said core alloy, at a temperature of up to about 425° F.; and (d) heating said roll bonded composite to a temperature of from about 800° F. to about 1100° F. for at least about three hours per inch of composite thickness to form a metallurgical bond between said core alloy and said liner material along substantially all of said contacting surfaces.
Claim 14
Independent Claim
180 words
A method for cladding an aluminum core alloy containing from about 1.0% to about 5.0% lithium with a metallic liner material at least about 0.2 inch thick to form a composite of which said liner material comprises from about 2% to about 10% per side of the thickness thereof, said method comprising: (a) preparing opposed surfaces of said core alloy and said liner material by removing therefrom substantially all oxide materials; (b) contacting said prepared surfaces to form a composite and tacking together the leading edges of each of said prepared surfaces; (c) roll bonding said composite from said leading edges to obtain substantially uniform adhesion along said contacting surfaces while causing at most a 15% reduction of said core alloy, at a temperature of up to about 425° F.; and (d) heating said roll bonded composite to a temperature of from about 800° F. to about 1100° F. for at least about three hours per inch of composite thickness to form a metallurgical bond between said core alloy and said liner material along substantially all of said contacting surfaces.
Claim 15
Independent Claim
180 words
A method for cladding an aluminum core alloy containing from about 1.0% to about 5.0% lithium with a metallic liner material at least about 0.2 inch thick to form a composite of which said liner material comprises from about 2% to about 10% per side of the thickness thereof, said method comprising: (a) preparing opposed surfaces of said core alloy and said liner material by removing therefrom substantially all oxide materials; (b) contacting said prepared surfaces to form a composite and tacking together the leading edges of each of said prepared surfaces; (c) roll bonding said composite from said leading edges to obtain substantially uniform adhesion along said contacting surfaces while causing at most a 15% reduction of said core alloy, at a temperature of up to about 425° F.; and (d) heating said roll bonded composite to a temperature of from about 800° F. to about 1100° F. for at least about three hours per inch of composite thickness to form a metallurgical bond between said core alloy and said liner material along substantially all of said contacting surfaces.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-12 | 1990-07-14 | 1991-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-12 | 1994-07-14 | 1995-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-12 | 1998-07-14 | 1999-01-13 | $7700.00 | Window Closed / Lapsed |