Laminar electrical component with magnesium orthoborate
Assignee: MRA Laboratories Inc
•
Filing: 1985-08-07
•
Granted: 1986-12-30
•
Expires: 2005-08-07
Abstract
Abstract A laminar electrical component has at least one ceramic dielectric layer of from 85 to 100 mole percent magnesium orthoborate (Mg3B2O6) which has a low dielectric constant and a high Q. A monolithic ceramic capacitor may have a predominantly magnesium orthoborate body with lithium oxide as a flux so that sintering may be as low as 850 DEG C. and in a reducing atmosphere accommodating buried copper electrodes. A predominantly Mg3B2O6 multi-level printed wiring substrate of low dielectric constant can include tightly adhered layers of a high dielectric constant ceramic for making buried high capacity filter capacitors, and can also include cofired base metal conductors.
Inventors
- 👤 Galeb H. Maher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:19
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; C; C04; C04B; C04B35/00; C04B35/01; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/30; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W72/00; H10W72/071; H10W72/072; H10W72/07251; H10W72/20
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
102 words
A method for making a laminar electrical component comprising: (a) preparing a start ceramic powder comprised of from 85 to 100 mole % magnesium orthoborate; (b) combining said start powder with a liquid vehicle to form a first slurry; (c) forming at least a first layer of said first slurry and drying said slurry; (d) depositing one film of an electroding ink on a portion of said first layer; (e) sintering and transforming said dried layer into a dense ceramic layer and (f) firing and sintering said film of electroding ink to form a conductive film adhered to said first ceramic layer.
Claim 2
Independent Claim
102 words
A method for making a laminar electrical component comprising: (a) preparing a start ceramic powder comprised of from 85 to 100 mole % magnesium orthoborate; (b) combining said start powder with a liquid vehicle to form a first slurry; (c) forming at least a first layer of said first slurry and drying said slurry; (d) depositing one film of an electroding ink on a portion of said first layer; (e) sintering and transforming said dried layer into a dense ceramic layer and (f) firing and sintering said film of electroding ink to form a conductive film adhered to said first ceramic layer.
Claim 3
Dependent Claim
61 words
The method of claim 1 additionally comprising forming over said first layer and said one electroding film, a second layer of a slurry comprised of a mixture of a powdered dielectric material and a liquid carrier, and drying said second layer, wherein said sintering and firing are accomplished simultaneously to form a unitary dense ceramic body having an electrode buried therein.
Claim 4
Dependent Claim
51 words
The method of claim 2 wherein said powdered dielectric material has a composition essentially the same as that of said start powder and the composition of said carrier is essentially the same as that of said vehicle so that the compositions of said layers are essentially the same as each other.
Claim 5
Dependent Claim
40 words
The method of claim 2 additionally comprising prior to said sintering depositing another film of an electroding ink on an outer portion of said second layer to have a capacitive relationship through said second layer with said one electroding film.
Claim 6
Dependent Claim
45 words
The method of claim 4 wherein said depositing accomplishes positioning of said one and another electroding films to extend to and be exposed at opposite ends, respectively, of the assembly of said two layers, so that a monolithic ceramic capacitor is formed after said firing.
Claim 7
Dependent Claim
43 words
The method of claim 2 wherein said electroding ink consists essentially of a base metal in a carrying fluid, said firing being accomplished in a low partial oxygen atmosphere below the oxidation/reduction characteristic of said base metal to avoid oxidizing said base metal.
Claim 8
Dependent Claim
11 words
The method of claim 6 wherein said base metal is copper.
Claim 9
Dependent Claim
24 words
The method of claim 2 wherein, after said firing, said second layer has a substantially larger dielectric constant than that of said first layer.
Claim 10
Dependent Claim
23 words
The method of claim 1 wherein said combining includes mixing said start powder with another powder comprising the precursors of another ceramic compound.
Claim 11
Dependent Claim
22 words
The method of claim 9 wherein said another compound is a ceramic having a characteristic minimum sintering temperature greater than 1150° C.
Claim 12
Dependent Claim
42 words
The method of claim 9 wherein said start powder amounts to less than 10 weight percent of the sum of said start powder and said another powder and said sintering is accomplished at a temperature equal to or less than 1150° C.
Claim 13
Dependent Claim
67 words
The method of claim 1 wherein said depositing one film is to form a plurality of patches of said one film that become conductive patches after said firing; and additionally including attaching to said fired ceramic an integrated circuit chip having conductor bumps extending from one face thereof by registering said conductive bumps over said conductive film patches and energizing to form a permanent conductive connection therebetween.
Claim 14
Dependent Claim
34 words
A laminar electrical component having a first dense sintered ceramic layer comprised of from 85 to 100 mole % magnesium orthoborate; and at least one fired continuous conductive film adhered to said one layer.
Claim 15
Dependent Claim
34 words
A laminar electrical component having a first dense sintered ceramic layer comprised of from 85 to 100 mole % magnesium orthoborate; and at least one fired continuous conductive film adhered to said one layer.
Claim 16
Dependent Claim
33 words
The component of claim 13 additionally comprising another sintered ceramic layer overlying said one layer and burying said one conductive film, said ceramic layers having been cosintered to form a unitary ceramic body.
Claim 17
Dependent Claim
29 words
The component of claim 14 additionally comprising another conductive film overlying said second ceramic layer to form a capacitor wherein said second ceramic layer serves as the active dielectric.
Claim 18
Dependent Claim
23 words
The component of claim 15 wherein said one and another conductive films each extend only to opposite ends of said unitary ceramic body.
Claim 19
Dependent Claim
13 words
The component of claim 14 wherein said one buried conductive film is copper.
Claim 20
Dependent Claim
22 words
The component of claim 14 wherein said second ceramic layer has a substantially greater dielectric constant than that of said first layer.
Claim 21
Dependent Claim
23 words
The component of claim 13 wherein the composition of said second ceramic layer is the same as that of said first ceramic layer.
Claim 22
Dependent Claim
32 words
The component of claim 13 wherein said dense sintered ceramic layer consists of from 85 to 100 mole % magnesium orthoborate and from 0 to 15 mole % of a sintering aid.
Claim 23
Dependent Claim
11 words
The component of claim 20 wherein said sintering aid is BaO.
Claim 24
Dependent Claim
13 words
The component of claim 20 wherein said sintering aid is Li 2 O.
References Cited (Backward Citations)
US3770529A
Cited
US3885941A
Cited
US3962081A
Cited
US4027209A
Cited
US4101952A
Cited
US4127415A
Cited
US4221047A
Cited
US4266265A
Cited
US4308570A
Cited
US4464420A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |